The current study explores the role that dislocation climb has in mediating plasticity a Mg alloy at moderately elevated temperatures. Interrupted tensile tests were performed on samples of Mg alloy, AZ31B, sheet in the O temper condition over a range of strain rates (10 -5 to 10 -1 s -1 ) and temperatures (20–350°C) along the rolling and transverse directions. Experimental measurements of the resulting strain anisotropy and texture evolution were used as constraints during a parametric study employing a new crystal plasticity model (VPSC-CLIMB), which explicitly accounts for the kinematics of dislocation climb. The results reveal that the climb of basal (a) dislocations is not only important for dislocation recovery, but also demonstrate that climb accommodates a significant fraction of the strain in conditions where a power-law creep-type constitutive response prevails. This work does not discredit the notion that non-basal slip of (a) and (c+a) dislocations is important over a wide range of temperatures and strain rates. However, it demonstrates that the activation of dislocation climb as the mechanistic change within the power law regime provides an explanation for a wide range of observations, including the simultaneous reduction in strain anisotropy, slowed texture evolution, and rapid increase in strain rate sensitivity. Finally, it is hypothesized that these conclusions may even apply to cases in which grain boundary sliding and/or dynamic recrystallization are observed.
36 MATERIALS SCIENCE↗
Evaluating the grain-scale deformation behavior of a single-phase FCC high entropy alloy using synchrotron high energy diffraction microscopy
We report although the deformation behavior of high-entropy alloys (HEAs) has been extensively studied at the macroscale, many important properties have yet to be explored for these alloys at the microscale, thus hampering accurate prediction of damage and failure processes. Synchrotron high-energy diffraction microscopy (HEDM) and fast-Fourier transform-based crystal plasticity modeling was conducted to investigate the three-dimensional (3D) grain-resolved micromechanical response for approximately 1,900 constituent grains within a single-phase FCC HEA up to 1% applied strain. The evolution of grain-resolved elastic strains, lattice reorientations, and maximum resolved shear stresses (mRSS) were evaluated to quantify elastic, yield, and fully plastic behavior. Overall, the initial critical resolved shear stress (CRSS), determined via in situ HEDM and companion modeling, was found to be > 20% higher than estimated using the classical polycrystalline Taylor factor (M = 3.06). However, a descriptive parameter based on the average grain-resolved Taylor factor ($\overline{M}$) was found to show excellent agreement with plastic yielding behavior observed within HEDM datasets. Noticeable deviations in HEDM lattice reorientations compared to both EVP-FFT simulations and classical predictions for FCC polycrystals were discovered, highlighting the complexity in correlating local lattice reorientations, Taylor, and Schmid factors with plastic response for this material at the grain-scale. Therefore, it is anticipated that the overall trends and parameter identification of 3D grain-resolved properties in this study can serve as an important foundation for continued mesoscale investigation on both well-established and newly developed Cantor-like HEAs.