Constraint-dependent CTOA determination for stable ductile crack growth

The crack tip opening angle (CTOA) has been used as a reliable fracture toughness to characterize stable crack growth for thin-wall structures in low-constraint conditions. Recently, it is found that CTOA can also be utilized as a robust fracture parameter to describe the arrest fracture toughness for gas transmission pipelines in ductile steels. For better understanding the concept of CTOA, this paper presents a brief review on the CTOA definitions and its test methods. And then, four CTOA models are developed for determining the CTOA toughness using conventional single edge notched bend (SENB) specimens, including the load–displacement linear fit model, the logarithmic load–displacement linear fit model, the stable tearing energy model, and the J-differentiation model. Here fracture test data from SENB specimens in A285 carbon steel are employed to evaluate the proposed CTOA models. The results show that these CTOA models can determine either identical or comparable critical CTOA values for stable ductile crack growth using the SENB specimens. A constraint-corrected CTOA resistance curve and a constraint-corrected critical CTOA equation are also obtained for A285 carbon steel.

42 ENGINEERING↗

DOE OSTI2022

Nondestructive Evaluation of Stress Corrosion Cracking in a Welded Steel Plate Using Guided Ultrasonic Waves

Stress corrosion cracking (SCC) had occurred in early-generation high-level nuclear waste tanks constructed by welding carbon steel. This paper describes an ultrasonic inspection system and its fundamental ability to detect and quantify the length of SCC on thick welded steel plates. The finite element method (FEM) was applied to simulate the welding process to estimate the welding residual stress field. Growth of stress corrosion cracks is driven by crack stress intensities exceeding the subcritical cracking threshold intensity. The subject plate was experimentally inspected with ultrasonic nondestructive evaluation (NDE) techniques to characterize the extent of SCC. The NDE system uses a piezoelectric transducer to generate guided waves in the thick steel plate, and a scanning laser Doppler vibrometer (SLDV) to measure multidimensional time–space wavefield data over a user-defined scanning area in the plate surface. The measured wavefield data can show wave interactions in a localized area in the plate due to the presence of the discontinuities of the SCC. To generate an inspection image that can precisely show the crack’s location and/or the dimension, the wavefield data are further processed to generate inspection image that maps the entire sample plate so the crack can be clearly identified in the plate while its length can be readily estimated. In conclusion, the ultrasonic test results for crack length agree well with the visually estimated length and are close to that predicted by the FEM for cracks in the weld residual stress field.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Crack Stability in Breached Fuel

This report describes the fracture mechanics formalism to evaluate the stability of cracks in a fuel cladding. Recognized consensus-body linear elastic fracture mechanics (LEFM) was applied to identify the crack instability length, or the length at which unstable mechanical crack extension would occur, as a function of pellet swelling loading (radial strain and fraction conversion from UO 2 to U 3 O 8 ) at the local cracked cladding region for two postulated fracture toughness (K IC ) values of the cladding. The crack opening displacement (COD) and the crack opening area (COA) were also identified. This analysis informs evaluations for crack extension and the potential for pellet debris loss from the fuel rod for cases of pellet oxidation in dry storage canisters where inadvertent residual water may undergo radiolysis causing oxidizing conditions to pellets exposed to the canister environment through breached cladding.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Crack Stability in Breached Fuel

This report describes the fracture mechanics formalism to evaluate the stability of cracks in a fuel cladding. Recognized consensus-body linear elastic fracture mechanics (LEFM) was applied to identify the crack instability length, or the length at which unstable mechanical crack extension would occur, as a function of pellet swelling loading (radial strain and fraction conversion from UO 2 to U 3 O 8 ) at the local cracked cladding region for two postulated fracture toughness (K IC ) values of the cladding. The crack opening displacement (COD) and the crack opening area (COA) were also identified. This analysis informs evaluations for crack extension and the potential for pellet debris loss from the fuel rod for cases of pellet oxidation in dry storage canisters where inadvertent residual water may undergo radiolysis causing oxidizing conditions to pellets exposed to the canister environment through breached cladding.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2020

Large Plate Experiment of Chloride-induced Stress Corrosion Cracking in Spent Nuclear Fuel Storage Canisters

This report provides a description of the testing (in progress at the Savannah River National Laboratory) to evaluate the corrosion behavior of a large section of welded plate material harvested from the Sandia National Laboratories’ full-size mockup of a spent nuclear fuel (SNF) dry storage canister. The details of the establishment of this plate test, the interim corrosion results (from visual examination), and the general plan for examination of the plate in CY21 to evaluate crack growth behavior (if any) are provided. This work is intended to inform aging management programs for SNF canisters under conditions of extended dry storage. A “large plate” (approximately 51 x 46 cm with thickness 16 mm and weight about 30 kg) and containing a circumferential weldment from the mockup is the test specimen. The knowledge of the salt, temperature, humidity conditions for chloride-induced stress corrosion cracking (CISCC) including the threshold stress intensity factor, K iscc , were used to setup the large plate test in which a set of part-through-wall and through-wall electrical discharge machined (EDM) defects were positioned in the weld residual stress field of the welded plate material from the mockup canister. A marine salt solution was applied to this plate specimen with an air-brush spray, then dried, and then exposed to a sustained 71-73% RH condition at an ambient room temperature of 22 °C. The salt loading and environmental condition is expected to be aggressive to cause CISCC