Engineering topics
Publications and source records attributed to Lager, J. R..
Manufacturing process precures components of composite panels prior to assembly. Process separately cures the graphite/epoxy skin, stiffener ribs, and stiffener grid. After curing, panels are assembled using special adhesive. With implementation of cost effective manufacturing techniques, uses of graphite-epoxy laminate panels may be found in other areas such as auto industry.
The structural concept considered for a spacecraft body structure is a grid stiffened skin with a skin laminate configuration and the stiffener grid geometry selected to best suit the design requirements. The orthogrid panel developed weighs 0.55 lb/sq ft and resisted an ultimate in-plane shear load of 545 lbf/in. The basic concept of a grid stiffener composite panel is that a relatively thin skin is reinforced with a gridwork of stiffeners so that the overall panel can resist design loads without becoming structurally unstable or being overstressed. The main feature of the orthogrid panel design is that it provides the potential for low cost structural panels when advanced to the production phase. The most innovative part of the fabrication method is the foam/fiberglass stiffener web grid billet fabrication and machining to size.
HOLBOAT computer program provides instability analysis of inhomogeneous, anisotropic, right-circular cylinder or segment under combined loading. Program is based on Kirchhoff-Love hypothesis, general anisotropic constitutive equations, and Flugge's differential equations of equilibrium.
Lightweight honeycomb sandwich construction using a wide variety of metal and fibrous composite faceskins was used in the design of a typical Space Tug skirt structure. Relatively low magnitude combined loading of axial compression and torsion resulted in designs using ultrathin faceskins, lightweight honeycomb cores, and thin faceskin/core adhesive bond layers. Two of the designs with metal faceskins (aluminum and titanium) and four with fibrous composite faceskins (using combinations of fiberglass, boron, and graphite) were evaluated through the fabrication and structural test of a series of small development panels. The two most promising concepts with aluminum and graphite/epoxy faceskins, were further evaluated through the fabrication and structural test of larger compression and shear panels. All panels tested exceeded design ultimate load levels, thereby, verifying the structural integrity of the selected designs. Projected skirt structural weights for the graphite/epoxy and aluminum concepts fall within original weight guidelines established for the Space Tug vehicle.
New forming and patching methods have been developed for high-quality graphite/epoxy laminates. Laminates range in thickness from 0.012 to 0.018 in. (0.31 to 0.46 mm).
A cylindrical shell structure 3.66 m (144 in.) high by 4.57 m (180 in.) diameter was designed using a wide variety of materials and structural concepts to withstand design ultimate combined loading 1225.8 N/cm (700 lb/in.) axial compression and 245.2 N/cm (140 lb/in.) torsion. The overall cylinder geometry and design loading are representative of that expected on a high performance space tug vehicle. The relatively low design load level results in designs that use thin gage metals and fibrous-composite laminates. Fabrication and structural tests of small panels and components representative of many of the candidate designs served to demonstrate proposed fabrication techniques and to verify design and analysis methods. Three of the designs evaluated, honeycomb sandwich with aluminum faceskins, honeycomb sandwich with graphite/epoxy faceskins, and aluminum truss with fiber-glass meteoroid protection layers, were selected for further evaluation.