NASA NTRS1978

Thermal environment effects on strength and impact properties of boron-aluminum composites

A systematic study was conducted regarding the degradation of fracture strength and impact energy in commercial B-Al composites in both static and cyclic thermal environments. The composites used in the study contained approximately 50 vol % boron fibers, unidirectionally aligned in either a 6061 Al or 1100 Al matrix. The tensile strengths of the composites after 3000 thermal cycles as a function of upper cycle temperature are presented in graphs. The temperature at which the strengths of 6061 Al matrix, B-Al composites were significantly degraded after 3000 cycles was noticeably higher than that for the 1100 Al matrix composites. Static heating at 420 C resulted in no significant strength degradation for the 6061 Al matrix composites. In the case of 1100 matrix composites, some degradation was observed at 420 C but markedly less than in the composites cycled to 420 C.

Grimes, H. H.↗
NASA NTRS1977

Thermal degradation of the tensile strength of unidirectional boron/aluminum composites

The variation of ultimate tensile strength with thermal treatment of B-Al composite materials and of boron fibers chemically removed from these composites is studied systematically in an attempt to determine the mechanism of the resulting strength degradation. The results indicate that thermally cycling of B-Al represents a more severe condition than equivalent time at temperature. Degradation of composite tensile strength from about 1.3 GN/sq m to as low as 0.34 GN/sq m was observed after 3000 cycles to 420 C for 203-micron B-1100 Al composite. In general, the 1100 Al-matrix composites degraded somewhat more than the 6061 matrix material studied. Measurement of fiber strengths confirmed a composite strength loss due to the degradation of fiber strength. Microscopy indicated a highly flawed fiber surface. On the basis of various thermal-cycling studies and electron diffraction analysis, a mechanism is favored in which B reacts with Al, freshly exposed by cold working during cycling, to form AlB2. The nonuniform interface reaction leads to a highly flawed and weakened B fiber.

Grimes, H. H.↗
NASA NTRS1977

Thermal degradation of the tensile strength of unidirectional boron/aluminum composites

The variation of ultimate tensile strength with thermal treatment of B-Al composite materials and of boron fibers chemically removed from these composites in an attempt to determine the mechanism of the resulting strength degradation was studied. Findings indicate that thermally cycling B-Al represents a more severe condition than equivalent time at temperature. Degradation of composite tensile strength from about 1.3 GN/m squared to as low as 0.34 GN/m squared was observed after 3,000 cycles to 420 C for 203 micrometers B-1100 Al composite. In general, the 1100 Al matrix composites degraded somewhat more than the 6061 matrix material studied. Measurement of fiber strengths confirmed a composite strength loss due to the degradation of fiber strength. Microscopy indicated a highly flawed fiber surface.

Grimes, H. H.↗
NASA NTRS1977

Thermal environment effects on strength and impact properties of boron-aluminum composites

Thermal effects on fracture strength and impact energy were studied in 50 volume percent unidirectional composites of 143 and 203 micron boron fibers in 6061 and 1100 aluminum matrices. For 6061 matrix composites, strength was maintained to approximately 400 C in the cyclic tests and higher than 400 C in the static tests. For the 1100 matrix composites, strength degradation appeared near 260 C after cycling and higher than 260 C in static heating. This composite strength degradation is explained by a fiber degradation mechanism resulting from a boron-aluminum interface reaction. The impact energy absorption degraded significantly only above 400 C for both matrix alloys. Thus, while impact loss for the 6061 composite correlates with the fiber strength loss, other energy absorption processes appear to extend the impact resistance of the 1100 matrix composites to temperatures beyond where its strength is degraded. Interrupted impact tests on as-received and thermally cycled composites define the range of load over which the fibers break in the impact event.

Grimes, H. H.↗
NASA NTRS1975

EPR study of electron bombarded alkali- and alkaline-earth halide crystal surfaces

An EPR study of electron bombarded LiF, NaCl, KCl, CaF2 and BaF2 polycrystalline surfaces has shown that small metal particles are formed on the surfaces of the crystals. Identification was made from CESR signals. The symmetric line-shape of the signals, even at 77 K, indicated that the particles were less than 0.5 micron in diameter. Signals due to F centers were observed in LiF but not in the other halides. Implications to metal deposition are considered.

Fryburg, G. C.↗
NASA NTRS1972

Electron beam chemistry produces high purity metals

Application of radiation chemistry for deposition of metals by irradiation of aqueous solutions with high energy electrons is presented. Design of reaction vessel for irradiation of solution is illustrated. Features of radiochemical technique and procedures followed are described.

Philipp, W. H.↗
NASA NTRS1971

Use of radiation in preparative chemistry

A summary and updating of previous work on the use of radiation chemistry for the preparation of pure materials are presented. Work was chiefly concerned with the reduction of metal salts in solution to the free metal using 2 MeV electrons. Metals deposited from aqueous solution are copper, silver, zinc, cadmium, thallium, tin, lead, antimony, iron, nickel, cobalt, and palladium. Dry organic solvents were evaluated for the deposition of metals based on a study involving deposition of antimony from soltions of antimony (III) chloride. The use of organic liquids for the preparation of anhydrous metal halides is also presented. Reaction mechanisms for both organic liquids and aqueous system are discussed.

Philipp, W. H.↗
NASA NTRS1966

Surface physics and chemistry

Electron paramagnetic resonance techniques for studying surface chemistry and physics pertinent to catalysis

CATALYTIC ACTIVITY↗
NASA NTRS1960

Factors Affecting the Ductility and Strength of NaCl Single Crystals Tested in Flexure

An experimental investigation has revealed that the initial deformation of NaCl single crystals is anelastic rather than Hookean. This anelastic deformation is manifested by a low slope foot in the load‐deflection curve. The magnitude of the foot is dictated by the pretreatment given the specimen. Treatments which increase or decrease the fresh dislocation density respectively increase or decrease the length of the initial anelastic foot. The order of increasing ductility and strength with specimen pretreatment was found to be (1) heated at 135 C, (2) as cleaved, (3) coated with silver, (4) heated at 135 C and then water polished, (5) water polished and then coated with silver, (6) water polished, (7) water polished and then heated at 135 C, (8) annealed at 700 C, and (9) annealed at 700 C and then water polished. The experimental results have been discussed in terms of the role played in deformation and fracture by surface cracks, grown‐in dislocations, and fresh dislocations.