X-Ray Characterization of Atomistic Defects Causing Irradiation Creep of SiC
Explore the source record for details and available documents.
Engineering topics
Publications and source records attributed to Koyanagi, Takaaki.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
Additive manufacturing (AM) is a rapidly evolving technology being considered for nuclear applications. A special focus on AM to fabricate nuclear-grade silicon carbide (SiC) is explored in this paper. First, we present currently available AM processing options for SiC. AM methods commonly used for other ceramics, in which the feedstocks are forms of polymers, powders, and/or reactive chemical vapors, are also applicable to SiC. SiC phases are formed by pyrolysis of pre-ceramic polymer, direct reaction of powder precursors, sintering of SiC powders, or chemical vapor deposition/infiltration. Second, we discuss how the different microstructures of SiC materials fabricated by various processing methods affect their behavior in nuclear environments. Third, we discuss state-of-the-art AM technologies for the fabrication of relatively pure SiC, which show great potential to retain its strength under neutron irradiation: (1) binder jet printing followed by chemical vapor infiltration, (2) laser chemical vapor deposition, and (3) selective laser sintering of SiC powders.
The irradiation temperature of silicon carbide (SiC) was determined post-irradiation by examination of the recovery of the electrical resistivity due to thermal annealing in a rapid heating/cooling optical furnace. High-purity, high-resistivity grade SiC is routinely used as a passive temperature monitor in neutron irradiation studies at the High Flux Isotope Reactor (HFIR), and this paper presents an alternative automated technique for determination of the irradiation temperature the SiC experienced. Neutron collisions with the atoms results in displaced lattice atoms (interstitials) that act as electron donors yielding a significant decrease in electrical resistivity. The irradiation defects become thermodynamically unstable and start to recombine, when annealed above the irradiation temperature, resulting in a recovery of the electrical resistivity. The resistivity is measured at a fixed elevated temperature above ambient, which is below the target irradiation temperature. When the resistivity is plotted as a function of annealing temperatures, a clear increase is observed due to the recovery of irradiation defects. We have demonstrated that this electrical resistivity measurement of SiC is effective to determine irradiation temperature of SiC. In conclusion, energy levels of various defects in SiC were calculated from Arrhenius plots of electrical conductivity versus inverse temperature.
Silicon carbide (SiC) ceramic-based composites continue to be attractive material options for fusion in-vessel components and fission reactor core structures because of their exceptional high-temperature capability and favorable neutronic properties. As performance data accumulates, the limitations of the current generation of nuclear-grade SiC composites are becoming more apparent. These limitations mainly involve strength degradation during high-dose neutron irradiation. In this paper, we discuss several options for improving the performance of the next generation of SiC composites to enhance the radiation resistance, along with new experimental results on neutron irradiation resistance. The main emphasis is on the selection of the fibers and the design and development of alternative interphase layers for advanced composites.
Conventional direct joining technologies are difficult to use with silicon carbide (SiC) materials, especially for fiber composite forms of SiC, because of the harsh conditions required. Therefore, to reduce the temperature and/or process time required for the direct joining process, an electric current–assisted joining (ECAJ) method was studied. Joining of low–resistivity grade, nitrogen doped β-SiC was demonstrated at a relatively low nominal temperature of 1750 °C with a 10 min hold by enhancing the passage of current through the material. The joining mechanism is discussed in terms of localized overheating and accelerated self-diffusion at the interface. In the case of joining at 2160 °C for 1 min, rapid crystal growth of textured SiC was found at the interface. This study indicates that rapid ECAJ-based direct joining is a practical and appropriate method for joining SiC-based materials.
In the Transformational Challenge Reactor (TCR), the fuel blocks consist of an additively-manufactured silicon carbide (SiC) matrix and uranium nitride tristructural isotropic (UN TRISO) fuel particles, which are stacked to form fuel columns. The SiC matrix is manufactured using binderjet 3D printing followed by loading the TRISO fuel particles and the chemical vapor infiltration (CVI) process. Because the fuel matrix is a primary component of the TCR core and its response to mechanical and thermal loads during operation is one of the most influential factors on the integrity of TCR core, testing and evaluation have focused on producing mechanical and thermophysical properties data for the binderjet/CVI SiC. Mechanical and thermophysical properties were measured from various types of specimens printed for two or three orientations, which included equibiaxial flexural failure strength, elastic constants, thermal diffusivity and conductivity, density, and the coefficient of thermal expansion. Flexural failure strength datasets showed similar Weibull distributions regardless of sample variants including different orientations. The mean failure strengths of the 3D-printed SiC variants were in the range of 286–306 MPa, which are 22–27% lower than that of the CVD SiC. Thermophysical test results showed that specific heat and thermal expansion are not sensitive to the build directions of SiC samples, while thermal diffusivity is highly dependent on the build direction and can be correlated to the anisotropic character of the 3D-printed SiC. This report also includes discussions on the uniaxial tensile properties of the as-printed SiC before CVI and on ongoing efforts for irradiation effects studies.
In this work, high purity SiC and SiC/SiC composites coated with commercial TiN, Cr, CrN, or CrN/Cr multilayer coatings were irradiated in Ar or flowing PWR water in the Massachusetts Institute of Technology Nuclear Reactor Laboratory (MITR). Irradiation in Ar was performed in the core. In the water environment, identical samples were placed in one of three different locations: in-core, providing exposure to neutron damage and radiolysis-affected water; above-core, where samples were exposed to radiolysis-affected water but not neutron damage, or outside of the core, where samples were exposed to the coolant water without the effects of radiation. Radiation in Ar revealed significant cracking of all but the TiN coatings, attributed to differential swelling between the coating and substrate. Lattice swelling was not observed in any of the coatings, but 0.2% void swelling was observed in the Cr coating. All of the coatings failed during water exposures in the core. Likewise, CrN/Cr spalled in each condition. Cr was protective, except under radiation damage as a result of cracking, and TiN severely degraded in the core with no coating was found following exposure. A SiC/coating ATF cladding system is anticipated to perform adequately following improvements in coating ductility and purity.