NASA NTRS1990

Matrix density effects on the mechanical properties of SiC/RBSN composites

The room temperature mechanical properties were measured for SiC fiber reinforced reaction-bonded silicon nitride composites (SiC/RBSN) of different densities. The composites consisted of approx. 30 vol percent uniaxially aligned 142 micron diameter SiC fibers (Textron SCS-6) in a reaction-bonded Si3N4 matrix. The composite density was varied by changing the consolidation pressure during RBSN processing and by hot isostatically pressing the SiC/RBSN composites. Results indicate that as the consolidation pressure was increased from 27 to 138 MPa, the average pore size of the nitrided composites decreased from 0.04 to 0.02 microns and the composite density increased from 2.07 to 2.45 gm/cc. Nonetheless, these improvements resulted in only small increases in the first matrix cracking stress, primary elastic modulus, and ultimate tensile strength values of the composites. In contrast, HIP consolidation of SiC/RBSN resulted in a fully dense material whose first matrix cracking stress and elastic modulus were approx. 15 and 50 percent higher, respectively, and ultimate tensile strength values were approx. 40 percent lower than those for unHIPed SiC/RBSN composites. The modulus behavior for all specimens can be explained by simple rule-of-mixture theory. Also, the loss in ultimate strength for the HIPed composites appears to be related to a degradation in fiber strength at the HIP temperature. However, the density effect on matrix fracture strength was much less than would be expected based on typical monolithic Si3N4 behavior, suggesting that composite theory is indeed operating. Possible practical implications of these observations are discussed.

Bhatt, Ramakrishna T.↗

NASA NTRS1989

Slurry-pressing consolidation of silicon nitride

A baseline slurry-pressing method for a silicon nitride material is developed. The Si3N4 composition contained 5.8 wt percent SiO2 and 6.4 wt percent Y2O3. Slurry-pressing variables included volume percent solids, application of ultrasonic energy, and pH. Twenty vol percent slurry-pressed material was approximately 11 percent stronger than both 30 vol percent slurry-pressed and dry-pressed materials. The Student's t-test showed the difference to be significant at the 99 percent confidence level. Twenty volume percent (300 h) slurry-pressed test bars exhibited strengths as high as 980 MPa. Large, columnar beta-Si3N4 grains caused failure in the highest strength specimens. The improved strength correlated with better structural uniformity as determined by radiography, optical microscopy, and image analysis.

Sanders, William A.↗

NASA NTRS1989

Grinding Si3N4 Powder In Si3N4 Equipment

Three methods of grinding compared. Report based on study of grinding silicon nitride powder in preparation for sintering into solid ceramic material. Attrition, vibratory, and ball mills lined with reaction-bonded silicon nitride tested. Rates of reduction of particle sizes and changes in chemical compositions of powders measured so grinding efficiences and increases in impurity contents from wear of mills and media evaluated for each technique.

Herbell, Thomas P.↗

NASA NTRS1989

High-frequency ultrasonic characterization of sintered silicon carbide

High-frequency 60- to 160-MHz ultrasonic nondestructive evaluation was used to characterize variations in density and microstructural constituents of sintered SiC bars. Ultrasonic characterization methods included longitudinal velocity, reflection coefficient, and precise attenuation measurements. The SiC bars were tailored to provide bulk densities ranging from 90 to 98 percent of theoretical, average grain sizes ranging from 3.0 to 12.0 microns, and average pore sizes ranging from 1.5 to 4.0 microns. Velocity correlated with specimen bulk density irrespective of specimen average grain size, average pore size, and average pore orientation. The attenuation coefficient was found to be sensitive to both density and average pore size variations, but was not affected by large differences in average grain size.

Baaklini, George Y.↗

NASA NTRS1988

Slurry-pressing consolidation of silicon nitride

Sanders, William A.↗

NASA NTRS1988

Materials technology assessment for a 1050 K Stirling space engine design

An assessment of materials technology and proposed materials selection was made for the 1050 K (superalloy) Stirling Space Engine design. The objectives of this assessment were to evaluate previously proposed materials selections, evaluate the current state-of-the-art materials, propose potential alternate materials selections and identify research and development efforts needed to provide materials that can meet the stringent system requirements. This assessment generally reaffirmed the choices made by the contractor. However, in many cases alternative choices were described and suggestions for needed materials and fabrication research and development were made.

Scheuermann, Coulson M.↗

NASA NTRS1988

Improved "Green" Forming Of Silicon Nitride

Advanced processing techniques reduce incidence of critical flaws. Critical flaws reduced by processing of powders to avoid organic and metallic contamination and combination of colloidal techniques with innovative slurry-pressing technique avoiding agglomeration. Silicon nitride considered for many applications ranging from components of turbine engines to industrial heat exchangers.

Freedman, Marc R.↗

NASA NTRS1988

Reliability Of Inspection By SLAM

Scanning laser acoustic microscopy finds flaws in ceramic specimens. Laser light used to detect distortions, on angstrom scale, produced on surface of specimen by ultrasonic waves transmitted through specimen. From distortion, SLAM creates picture on video monitor of such defects as voids, inclusions, and cracks.

Roth, Don J.↗

NASA NTRS1988

A sintering model for SiC(sub)w/Si3N4 composites

Presented is a model which suggests that it should be possible to pressureless sinter a SiC(sub w)/ Si3N4 composite to theoretical density. Prior failure to achieve complete densification by sintering is attributed to the use of compositions which result in a glass deficit. There is one basic premise for this model. The ratio of glass amount to surface area of nonglass constituents must be the same for both composite and sinterable monolithic Si3N4. This model suggests that whisker and grain sizes and whisker loading influence the glass amount necessary for successful sintering of composites. According to the model, a large glass amount will be necessary for successful sintering of these composites. However, grain boundary thicknesses in the composite will be less than those in the analogous monolithic materials. This suggests that good high temperature strength may still be attained. A recent report supports the predictions of the model.

Freedman, Marc R.↗

NASA NTRS1987

Ceramics for engines

Structural ceramics were under nearly continuous development for various heat engine applications since the early 1970s. These efforts were sustained by the properties that ceramics offer in the areas of high-temperature strength, environmental resistance, and low density and the large benefits in system efficiency and performance that can result. The promise of ceramics was not realized because their brittle nature results in high sensitivity to microscopic flaws and catastrophic fracture behavior. This translated into low reliability for ceramic components and thus limited their application in engines. For structural ceramics to successfully make inroads into the terrestrial heat engine market requires further advances in low cost, net shape fabrication of high reliability components, and improvements in properties such as toughness, and strength. These advances will lead to very limited use of ceramics in noncritical applications in aerospace engines. For critical aerospace applications, an additional requirement is that the components display markedly improved toughness and noncatastrophic or graceful fracture. Thus the major emphasis is on fiber-reinforced ceramics.

Kiser, James D.↗

NASA NTRS1987

Statistical Tests of Reliability of NDE

Capabilities of advanced material-testing techniques analyzed. Collection of four reports illustrates statistical method for characterizing flaw-detecting capabilities of sophisticated nondestructive evaluation (NDE). Method used to determine reliability of several state-of-the-art NDE techniques for detecting failure-causing flaws in advanced ceramic materials considered for use in automobiles, airplanes, and space vehicles.

Baaklini, George Y.↗

NASA NTRS1987

High frequency ultrasonic characterization of sintered SiC

High frequency (60 to 160 MHz) ultrasonic nondestructive evaluation was used to characterize variations in density and microstructural constituents of sintered SiC bars. Ultrasonic characterization methods included longitudinal velocity, reflection coefficient, and precise attenuation measurements. The SiC bars were tailored to provide bulk densities ranging from 90 to 98 percent of theoretical, average grain sizes ranging from 3.0 to 12.0 microns, and average pore sizes ranging from 1.5 to 4.0 microns. Velocity correlated with specimen bulk density irrespective of specimen average grain size, average pore size, and average pore orientation. Attenuation coefficient was found to be sensitive to both density and average pore size variations, but was not affected by large differences in average grain size.

Baaklini, George Y.↗