Kiser, Doug

Publications and source records attributed to Kiser, Doug.

7 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS2017

Effect of Mechanical and Thermal Loading Histories on Residual Properties of SiCf/SiC Ceramic Matrix Composites

Silicon Carbide based Ceramic Matrix Composites (CMCs) are attractive materials for use in high-temperature structural applications in the aerospace and nuclear industries. Under high stresses and temperatures, creep degradation is the dominant damage mechanism in CMCs. Consequently, chemical vapor infiltration (CVI) SiCf/SiC ceramic matrix composites (CMC) incorporating SylramicTM-iBN SiC fibers coated with boron nitride (BN) interphase and CVI-SiC matrix were tested to examine creep behavior in air at a range of elevated temperatures of (2200 - 2700 F). Samples that survived creep tests were evaluated via RT fast fracture tensile tests to determine residual properties, with the use of acoustic emission (AE) to assess stress dependent damage initiation and progression. Microscopy of regions within the gage section of the tested specimens was performed. Observed material degradation mechanisms are discussed.

creep↗
NASA NTRS2017

Crack Opening Displacement Behavior in Ceramic Matrix Composites

Ceramic Matrix Composites (CMC) modeling and life prediction strongly depend on oxidation, and therefore require a thorough understanding of when matrix cracks occur, the extent of cracking for given conditions (time-temperature-environment-stress), and the interactions of matrix cracks with fibers and interfaces. In this work, the evolution of matrix cracks in a melt-infiltrated Silicon Carbide/Silicon Carbide (SiC/SiC) CMC under uniaxial tension was examined using scanning electron microscopy (SEM) combined with digital image correlation (DIC) and manual crack opening displacement (COD) measurements. Strain relaxation due to matrix cracking, the relationship between COD's and applied stress, and damage evolution at stresses below the proportional limit were assessed. Direct experimental observation of strain relaxation adjacent to regions of matrix cracking is presented and discussed. Additionally, crack openings were found to increase linearly with increasing applied stress, and no crack was found to pass fully through the gage cross-section. This observation is discussed in the context of the assumption of through-cracks for all loading conditions and fiber architectures in oxidation modeling. Finally, the combination of SEM with DIC is demonstrated throughout to be a powerful means for damage identification and quantification in CMC's at stresses well below the proportional limit.

acoustic emission↗
NASA NTRS2016

Advanced Environmental Barrier Coating Development for SiC-SiC Ceramic Matrix Composite Components

This presentation reviews the NASA advanced environmental barrier coating (EBC) system development for SiCSiC Ceramic Matrix Composite (CMC) components for next generation turbine engines. The emphasis has been placed on the current design challenges of the 2700F environmental barrier coatings; coating processing and integration with SiCSiC CMCs and component systems; and performance evaluation and demonstration of EBC-CMC systems. This presentation also highlights the EBC-CMC system temperature capability and durability improvements through advanced compositions and architecture designs, as shown in recent simulated engine high heat flux, combustion environment, in conjunction with mechanical creep and fatigue loading testing conditions.

Simulated Engine Test↗
NASA NTRS2016

Characterization of SiCSiC Composites in Support of Environmental Degradation Modeling

SiCSiC (silicon carbide fiber reinforced silicon carbide) composites are candidate materials for various turbine engine applications because of their high specific strength and good creep and oxidation resistance at elevated temperatures. This study was performed to characterize the microstructure of a melt infiltrated (MI) SiCSiC, and to examine environmental degradation mechanisms occurring in precracked MI SiCSiC CMC specimens under tensile stresses of 30 ksi or less at 815C in dry air or argon. In addition, the oxidation of the BN interface was characterized at815C, and crack opening displacement as a function of stress measurements were made. This material characterization is being performed to obtain data to support NASA GRC modeling of SiCSiC environmental degradation. The comparison of experimentally-observed phenomena with model predictions can lead to improved understanding of material degradation mechanisms.

SiC/SiC composites↗
NASA NTRS2016

InSitu SEM Investigation of Microstructural Damage Evolution and Strain Relaxation in a Melt Infiltrated SiC/SiC Composite

With CMC components poised to complete flight certification in turbine engines on commercial aircraft within the near future, there are many efforts within the aerospace community to model the mechanical and environmental degradation of CMCs. Direct observations of damage evolution are needed to support these modeling efforts and provide quantitative measures of damage parameters used in the various models. This study was performed to characterize the damage evolution during tensile loading of a melt infiltrated (MI) silicon carbide reinforced silicon carbide (SiC/SiC) composite. A SiC/SiC tensile coupon was loaded to a maximum global stress of 30 ksi in a tensile fixture within an SEM while observations were made at 5 ksi increments. Both traditional image analysis and DIC (digital image correlation) were used to quantify damage evolution. With the DIC analysis, microscale damage was observed at the fiber-matrix interfaces at stresses as low as 5 ksi. First matrix cracking took place between 20 and 25 ksi, accompanied by an observable relaxation in strain near matrix cracks. Matrix crack opening measurements at the maximum load ranged from 200 nm to 1.5 m. Crack opening along the fiber-matrix interface was also characterized as a function of load and angular position relative to the loading axis. This characterization was funded by NASA GRC and was performed to support NASA GRC modeling of SiC/SiC environmental degradation

testing↗
NASA NTRS2000

Ceramic Matrix Composite Turbine Disk for Rocket Engines

NASA has recently completed testing of a ceramic matrix composite (CMC), integrally bladed disk (blisk) for rocket engine turbopumps. The turbopump's main function is to bring propellants from the tank to the combustion chamber at optimal pressures, temperatures, and flow rates. Advantages realized by using CMC blisks are increases in safety by increasing temperature margins and decreasing costs by increasing turbopump performance. A multidisciplinary team, involving materials, design, structural analysis, nondestructive inspection government, academia, and industry experts, was formed to accomplish the 4.5 year effort. This article will review some of the background and accomplishments of the CMC Blisk Program relative to the benefits of this technology.

Effinger, Mike↗