Chloride Reduction of Mn 3+ in Mild Hydrothermal Synthesis of a Charge Ordered Defect Pyrochlore, CsMn 2+ Mn 3+ F 6 , a Canted Antiferromagnet with a Hard Ferromagnetic Component

Geometrically frustrated systems play an important role in studying new physical phenomena and unconventional thermodynamics. Charge ordered defect pyrochlores AM 2+ M 3+ F 6 offer a convenient platform for probing the interplay between electron distribution over M 2+ and M 3+ sites and structural distortions; however, they are limited to compounds with M 2+/3+ = V, Fe, Ni, and Cu due to difficulties in the simultaneous stabilization of other 3d elements in the +2 and +3 oxidation states. Herein, we employ Cl– anions under hydrothermal conditions for the mild reduction of Mn 2 O 3 in concentrated HF to obtain the CsMn 2+ Mn 3+ F 6 composition as a phase pure sample and study its properties. The magnetism of CsMn 2 F 6 was characterized by measuring the magnetic susceptibility and isothermal magnetization data, and a magnetic transition to a canted antiferromagnet state was found at 24.1 K. We determined the magnetic structure of CsMn 2 F 6 using powder neutron diffraction, which revealed successive long-range ordering of the Mn 2+ and Mn 3+ sites that is accompanied by a second transition. As a result, the role and strength of magnetic exchange interactions were characterized using DFT calculations.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Phase evolution during lithium–indium halide superionic conductor dehydration

Select rare-earth alkali halides have demonstrated high lithium ion conductivity. The conductivity appears to be related to the stability of the crystal phase, ordering of the lithium sublattice and the amount of residual H 2 O. Li 3 InCl 6 can be synthesized from concentrated aqueous solution through controlled dehydration. In this work, we track Li 3 InCl 6 dehydration using a multimodal approach that combines thermogravimetric, spectroscopic, X-ray diffraction, and neutron scattering techniques. In situ X-ray diffraction suggests a single phase transition caused by dehydration, in disagreement with spectroscopic and thermodynamic measurements. Neutron scattering, being sensitive toward the H 2 O and Li sublattices, reveals multiple phase transitions. We show that the loss of the final trace H 2 O leads to strain and grain boundary formation. Thus, controlled dehydration may be a viable strategy for high-throughput processing for roll-to-roll manufacturing of REAH solid electrolytes.

36 MATERIALS SCIENCE↗