Khadkikar, P. S.

Publications and source records attributed to Khadkikar, P. S..

6 records

NASA NTRS1993

Transformation to Ni5Al3 in a 63.0 at. pct Ni-Al alloy

Microstructures of 63 at. pct P/M Ni-Al alloys with a composition close to the stoichiometry of the Ni5Al3 phase were investigated using homogenized and quenched specimens aged at low temperatures for various times. Results of analyses of XRD data and electron microscopy observations were used for quantitative phase analysis, performed to calculate the (NiAl + Ni5Al3)/Ni5Al3 phase boundary locations. The measured lattice parameters of Ni5Al3 phase formed at 823, 873, and 923 K indicated an increase in tetragonality of the phase with increasing nickel content.

Khadkikar, P. S.↗

NASA NTRS1990

Preferred orientations in extruded nickel and iron aluminides

A plotting of inverse pole figures is used to characterize the preferred orientations in both powder-extruded and cast-and-extruded NiAl, FeAl, and Ni3Al; the preferred 111 orientation has been noted along the extrusion direction in both powder-extruded and cast-and-extruded NiAl. While powder-extruded FeAl also had a 111 preferred orientation in the as-extruded condition, 110 was observed upon casting and extrusion; this was in turn replaced by a 211 orientation preference upon annealing, although annealing did not change the preferred orientation in either NiAl or in powder-extruded FeAl.

Khadkikar, P. S.↗

NASA NTRS1989

Notch effects on room temperature tensile and bend properties of Ni3Al and Ni3Al+B

The notched mechanical properties of Ni3Al and Ni3Al+B prepared by powder metallurgy techniques have been determined in both tension and bending at room temperature. Tensile tests performed using double-notched specimens containing relatively blunt notches produced intergranular fracture in both Ni3Al and Ni3Al+B, with evidence of fracture initiating in an intergranular manner ahead of the blunt notch in both cases. Estimates of notched fracture toughness from bend tests and of local grain boundary fracture stress from the notched tensile tests suggest an increase in these values with boron addition.

Khadkikar, P. S.↗

NASA NTRS1989

Strength and toughness of composite materials based on nickel aluminide matrices

Several nickel aluminide matrix composites were prepared using vacuum hot pressing techniques. The matrix compositions, based on Ni3Al, Ni3Al+B, and NiAl, were reinforced with 10 vol pct TiB2 particles. Both smooth- and notched-bend tests were conducted at room temperature on the monolithic as well as the reinforced materials in order to determine the effects of TiB2 reinforcement on both the smooth-bend and notched-bend properties. TiB2 additions were shown to improve the smooth-bend strengths regardless of the matrix composition, while notched-bend tests, conducted to provide estimates of fracture toughness, revealed somewhat lower values for the composites in comparison to the monolithic materials. Fractographic analyses and in situ fracture observations of the composites revealed that preferential fracture in regions of clustered TiB2 particles may significantly affect the measured toughnesses.

Rigney, J. D.↗

NASA NTRS1987

The role of boron in ductilizing Ni3Al

Ductilization of Ni3Al at room temperature by microalloying with boron has been primarily attributed to the increased grain boundary cohesion in the presence of boron. However, another aspect of the role played by boron in ductilizing Ni3Al is revealed when the Hall-Petch relationships for Ni3Al and B-doped Ni3Al are compared. A shallower slope for the B-doped Ni3Al compared to that for Ni3Al indicates a reduced resistance to slip propagation across grain boundaries, and therefore reduced stress concentration at boundaries, in the presence of boron. This comparison of Hall-Petch relationships was carried out by generating data for powder processed B-doped Ni3Al at various grain sizes and by compiling data for Ni3Al from the literature. In addition, the room temperature fracture of B-doped Ni3Al has been shown to initiate along certain grain boundaries. The fracture eventually occurs by transgranular ductile tearing.

Vedula, K.↗

NASA NTRS1987

Two-phase nickel aluminides

The as-extruded microstructures of two alloys in the two phase field consisting of Ni3Al and NiAl in the Ni-Al phase diagram exhibit fibrous morphology and consist of Ll(2) Ni3Al and B2 NiAl. These as-extruded microstructures can be modified dramatically by suitable heat treatments. Martensite plus NiAl or martensite plus Ni3Al microstructures are obtained upon quenching from 1523 K. Aging of martensite at 873 K results in the recently identified phase Ni5Al, whereas aging at 1123 K reverts the microstructures to Ni3Al plus NiAl. The microstructures with predominantly martensite of Ni5Al3 phases are brittle in tension at room temperature. The latter microstructure does not deform plastically even in compression at room temperature. However, some promise of room temperature tensile ductility is indicated by the Ni3Al plus NiAl phase mixtures.

Khadkikar, P. S.↗