Robust Dissimilar Metal Friction Welded Spool for Enhanced Capability for Steam Power Components (Final Program Report)
This project successfully demonstrated the feasibility and advantages of producing durable, friction-welded dissimilar-metal spools, both with and without transition pieces, as well as the use of advanced oxidation-protective coatings for steam power applications. The work encompassed the optimization and full-scale production of NFA tubing, overcoming manufacturing and processing challenges to achieve enhanced strength, creep, and fatigue properties validated by extensive microstructural characterization. Optimized welding techniques were developed and refined for joining dissimilar materials, resulting in defect-free welds optimized for both low- and high-pressure boiler circuits. Systematic evaluation of welding parameters, coupled with heat treatments, ensured reliable performance and minimized weld defects such as banding and cracking. Comprehensive mechanical and non-destructive testing, including tensile, bend, fatigue, and CT scanning, confirmed the superior integrity and durability of the friction-welded joints under representative service conditions. To address oxidation-related degradation, a range of protective alloy coatings—such as IN625, APMT, Duplex 2507, and FeCrAlY—were selected and evaluated for their ability to counteract oxide notch formation at dissimilar metal interfaces. These coatings demonstrated improved oxidation resistance and long-term stability under thermal cycling, thereby extending weld service life. Thermal cyclic testing and long-term studies captured the phase stability and diffusion behavior of coated and uncoated configurations. Validated models for low-cycle fatigue (LCF), creep, and thermal mechanical fatigue (TMF) were developed to predict component life and failure modes. These models confirmed that friction-welded configurations exhibited significantly enhanced performance compared to conventional gas-tungsten arc welding (GTAW), with up to 7× improvement in creep resistance and at least 2× enhancement in fatigue properties. The introduction of a tailored transition piece further reduced thermally induced strains, enhancing fatigue life. The results demonstrate a robust pathway for retrofitting existing steam fleet components and upgrading future equipment to deliver substantially improved cold-start cycling behavior and reduction of unplanned outages due to premature weld failures.