Jun, Jiheon

Publications and source records attributed to Jun, Jiheon.

12 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

Corrosion evaluation of Al-Cu-Mn-Zr cast alloys in 3.5% NaCl solution

Corrosion behavior of cast Al-Cu-Mn-Zr (ACMZ) and RR350 alloys was compared to a cast 319 alloy in 3.5 wt.% NaCl. After 168 h immersion, ACMZ and RR350 alloys suffered from preferential attack adjacent to intermetallic particles decorated at grain boundaries while the attack in 319 occurred in eutectic Al-Si dendritic boundaries. Electrochemical data allowed semiquantitative comparison of alloy resistance to corrosion initiation, and ACMZ type alloys, including RR350 and three alloys with higher Cu, were considered more resistant than 319 due to the absence of deleterious Si particles. In case of 319, such Si particles presumably drove higher micro-galvanic influence to initiate and sustain Al corrosion. With lower susceptibility to corrosion initiation, ACMZ alloys should exhibit higher or at minimum similar resistance compared to cast 319.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Investigation of Chemical Species in the Corrosion Barrier Layer on Thermal CO 2 Treated AZ91D Magnesium Alloy with Lithium Nitrate

A unique corrosion barrier layer, formed by thermal CO 2 treatment with LiNO 3 on AZ91D, was characterized to reveal the chemical species and their spatial distribution using the combination of scanning transmission electron microscopy (STEM), energy dispersive spectroscopy (EDS), and electron energy loss spectroscopy (EELS) techniques. Two distinct and spatially segregated phases were identified as Li compound(s) with MgCO 3 and MgO in the surface barrier layer. Finally, based on the characterization results, it is presumed that the reaction of Mg oxide/hydroxide with LiNO 3 and CO 2 occurred preferentially in some local areas where Li compound(s) with MgCO 3 were present, but the unreacted areas contained MgO in the surface barrier layer.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Electrochemically Assisted Single Crystal Growth of Reduced Preyssler Polyoxometalates Decorated with M 2+ ( M = Co, Ni) and Cubane–Like Ni 4 O 4 Units

Polyoxometalates (POMs) are of great interest to the scientific community, and their reduction and nucleation have been well–established by multi–step techniques. The present study develops an electrochemical approach for simultaneous reduction and nucleation of polyoxometalate–containing solids. Herein we report crystal growth of reduced Preyssler polyoxotungstate–based (anionic formula [NaP 5 W 30 O 110 ] 14– ) new crystalline solids made of Preyssler anions interlinked by Co 2+ and Ni 2+ ions. Crystal nucleation and in situ reduction were achieved at room temperature using a two silver wire electrode setup in various aqueous solutions under constant applied potentials. The POM material was deposited on the cathode, and its structure was characterized by X–ray diffraction techniques. The primary structure type observed involves POMs decorated by disordered Co 2+ /Ni 2+ octahedra and fused into 1–D pillars by additional Co 2+ /Ni 2+ octahedra. Additionally, a secondary phase was observed in the Ni–based reactions, where reduced Preyssler anions are decorated by Ni 4 O 4 cubane–like units. To understand the electrochemical process, polarization curves of the electrolyte solutions are presented, suggesting an applied potential best suited for crystal growth. The work highlights the effectiveness of an electrochemical pathway where nucleation and simultaneous reduction of POMs can make novel reduced POM solids.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

Evaluation of liquid metal embrittlement of F82H and 4340 steels in liquid lithium

Here, to evaluate the liquid metal embrittlement (LME) susceptibility of F82H, a reduced activation ferritic-martensitic (RAFM) steel, a testing procedure using hollow cylindrical tensile specimens was used. Tensile tests are compared between specimens filled with argon and lithium at 200 °C. To validate the procedure, initial testing was performed on type 4340 steel, which is well-known to exhibit LME. Compared to 4340 steel, F82H only showed minor effects of Li exposure, including pre-testing exposures with Li at 400 °C for 1 h and 500 °C for 500 h. Furthermore, changing the strain rate or tensile test temperature also did not show significant embrittlement.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗
DOE OSTI2024

Performance Restoration of Iron Electrodes by Polarity Reversal after Long-Term Surface Fouling in Wastewater Electrocoagulation

Iron electrocoagulation (Fe-EC) performance often declines with time, producing lower contaminant removal efficiencies and higher energy requirements due to formation of a fouling layer on the electrodes. Here, we investigate the formation of the fouling layer and the effectiveness of polarity reversal to restore the Fe-EC performance. A thin, porous iron oxide layer initially forms on the anode, thickening into a dense, over 150-μm thick crystalline layer after extended operation. This fouling layer restricts dissolution and diffusion of Fe ions into the bulk solution, thus increasing the anode potential required to maintain a desired electrical current and decreasing Faradaic efficiency. Polarity reversal applied when performance decline is observed effectively removes the fouling layer, thereby restoring Faradaic and contaminant removal efficiencies and decreasing energy consumption. Our findings suggest that gas generation at the cathode surface after polarity reversal causes removal of the fouling layer. This study enhances the current understanding of fouling-layer formation in Fe-EC and offers a practical approach, involving polarity reversal, to maintain electrode reactivity and optimal Fe-EC performance.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

Advanced neutron absorber Ni-Cr-Mo-Gd alloys seawater corrosion mechanism and susceptibility study

Previous studies demonstrated the corrosion susceptibility of advanced neutron absorber (ANA) Ni-Cr-Mo-Gd in a seawater environment but remained inconclusive. In this paper, scanning electron microscopy was employed to identify the corrosion phase in Ni-Cr-Mo-Gd, and computational thermodynamic simulation was used to study phase corrosion potentials. Results showed that the Ni 5 Gd second phase, distributed along FCC grain boundaries in Ni-Cr-Mo-Gd, has lower corrosion potential than the substrate. Furthermore, heat treatment and alloy chemistry adjustment would not ameliorate the ANA corrosion susceptibility. Finally, isolating the Ni 5 Gd from the corrosion medium through advanced manufacturing is a viable way to improve the ANA corrosion resistance.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Open-air plasma-assisted deposition of organosilicon coating for corrosion protection of AZ91D Mg alloy

As a corrosion barrier layer, open-air plasma-assisted organosilicon coating was applied on AZ91D Mg alloy. Organosilicon-coated AZ91D samples, prepared from two different plasma coating processes, were used for corrosion evaluation based on multistep electrochemical and H 2 collection measurements in 3.5 wt% sodium chloride (NaCl) solution. Some coated AZ91D samples were characterized with and without corrosion exposure in NaCl solution using electron microscopies and X-ray chemical analysis techniques. Further, the results indicate that the organosilicon coatings from open-air plasma processes are effective to delay the initiation of corrosion attack and also reduce the corrosion rate for AZ91D substrate. The corrosion attack was considered to develop after permeation of NaCl solution through the coating layer.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Novel Approaches and Technologies for Aging Management

As part of the application process for license renewal and subsequent license renewal, nuclear utilities must perform an evaluation to confirm that they have appropriately considered aging effects on plant structures, systems, components within the scope of the license renewal. This effort within the Light Water Reactor Sustainability program’s Risk-informed System Analysis pathway is focused on risk-informed and performance-based approaches for aging management of buried piping, specifically managing selective leaching degradation phenomena. Selective leaching is a commonly occurring aging and degradation mechanism in buried pipes at nuclear power plants. To better understand the extent of selective leaching and its effect on the health of buried components, the licensees currently rely on visual inspections and destructive examinations which require extraction of multiple buried components. This research explores technological solutions that may replace or supplement existing inefficient, costly, and labor-intensive methods used in aging management.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Characterization and Electrochemical Analysis of Acidic Condensate-Induced Corrosion on Aluminized Coating on Steel in Residential Heaters

Condensing furnace residential heaters are starting to replace outdated and less efficient non-condensing units in homes across the US. However, the burning of natural gas in these new units produces acidic gases, which can form acid droplets (H 2 SO 4 , HNO 3 , H 2 CO 3 , etc.) that are corrosive to low-grade heat exchanger metallic materials. Type-1 aluminized steel has been used in industrial applications, such as marine, heating, and automobile parts, due to its resistance to oxidation at elevated temperature. Many components of the condensing furnaces, including heat exchangers, are made from type-1 aluminized steel. We investigated the interaction of type-1 aluminized steel substrates with two acidic condensate liquids by 500 h corrosion exposures as well as short-term electrochemical impedance measurements. SEM plan and cross-sectional view images revealed damage to the Al-Si rich layer and exposure of the steel substrate. The non-uniform damage in the Al-Si rich layer was likely attributed to a pitting corrosion mechanism and induced by high acidity of the condensate liquid. Electrochemical impedance measurements in an acidic condensate revealed lower corrosion resistance of the aluminized steel surface with a weld line, identifying welded sections as preferential corrosion initiation sites.

36 MATERIALS SCIENCE↗
DOE OSTI2023

An effective air–liquid contactor for CO 2 direct air capture using aqueous solvents

Here, the development of a cost-effective, corrosion resistant, high-flux direct air capture (HiDAC) contactor for a solvent-based direct air capture (DAC) process is reported. Literature technoeconomic analyses suggest that the air–liquid contactor can cost over 20 % of the overall DAC plant’s annualized capital costs. To bring down the overall cost of DAC, it is imperative that an effective contactor is developed. A hybrid contactor consisting of a commercial polyvinylchloride structured packing enhanced with stainless-steel 410 random packing has been developed to provide a high surface area for air–liquid contact. The contactor geometry, wettability, corrosion resistance, pressure drop, along with its CO 2 uptake efficiency, CO 2 uptake rates, and extended loading potential using potassium sarcosinate solutions are investigated. Results show that the HiDAC contactor has a relatively high specific surface area (885 m 2 /m 3 ), which allows for CO 2 uptake efficiencies of up to 75 % and capture rates of up to 550 g of CO 2 per day for a 0.3 × 0.25 × 0.3 m contactor. The contactor also exhibits high levels of wettability and corrosion resistance with amino acid-based DAC solvents. A CO 2 uptake model was developed, and modeling results are compared to experimental data to simulate and predict the performance of the contactor in a DAC process using potassium sarcosinate solvent. The system’s overall mass transfer coefficient and theoretical pressure drop were also calculated, and these results were compared to DAC data found in literature. The results presented indicate that the HiDAC contactor is well suited for DAC due to its high specific surface area, resistance to corrosion, and high degree of wettability.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Atmospheric Pressure Plasma Treatment of Magnesium Alloy for Enhanced Coating Adhesion and Corrosion Resistance

Atmospheric pressure plasma (AP) treatment, using an open-air jet of ionized CO 2 , N 2 , or air, was applied to AZ91D Mg alloy surfaces to investigate its effects on primer coating adhesion and corrosion resistance. The CO 2 and air AP treatments formed an O- and C-rich surface layer (Mg-O-C) consisting of agglomerated nanoparticles and pits with a depth of a few microns and increasing the surface roughness by 6–8 times compared with the reference 600 grit-finished surface. Then, three commercial primers, zinc phosphate (ZnP), chromate-containing epoxy, and MIL23377, were applied on the treated surfaces to evaluate the corrosion resistance associated with the coating adhesion. Microscopic analysis demonstrated stronger interlocking between the primer layer and the nano-/microrough Mg-O-C surface compared to the untreated (600 grit-finished) surfaces, indicating improved coating adhesion and corrosion resistance. Crosscut tests of the MIL23377 primer on the CO 2 and air AP-treated surfaces showed the highest level of adhesion, ASTM class 5B. Salt spray corrosion tests showed that after 8 days of exposure, the primer coatings on air AP-treated surfaces had corrosion areas that were more than four times smaller than that of the 600 grit-finished surface. The N 2 AP treatment showed similar adhesion enhancement. The preliminary operation expenses for AP treatment using CO 2 , N 2 , and air were estimated at USD 30.62, USD 35.45, and USD 29.75 (from an air cylinder)/USD 0.66 (from an air compressor) per m 2 , respectively.

36 MATERIALS SCIENCE↗