Characterization of Cycle-Aged Commercial NMC and NCA Lithium-ion Cells: I. Temperature-Dependent Degradation

Lithium-ion batteries are widely used in applications from consumer electronic devices to stationary energy storage. Appropriate management of batteries is challenging due to limited data on their performance and materials degradation. Previous studies have focused on characterization of single cells under specific operating conditions. In the present work, commercial 18650 lithium-ion cells with LiNi x Mn y Co 1-x-y O 2 (NMC) and LiNi x Co y Al 1-x-y O 2 (NCA) positive electrodes were characterized by a wide range of electrochemical and materials techniques after cycling at 15, 25, or 35 °C to ∼80% capacity. The NCA cells exhibit weak temperature dependence in their cycle aging and materials degradation. The NMC cells exhibited increased capacity fade and materials degradation as ambient temperature decreased. All cells exhibited loss of lithium inventory as their primary degradation mode. However, the NCA cells only showed evidence of solid electrolyte interphase (SEI) growth whereas the NMC cells showed signs of Li plating at 15 °C, transitioning to SEI growth at 35 °C. The NMC cells displayed signs of loss of active material at the positive electrode at lower temperatures, suggesting that Li plating is correlated to additional processes that increase the rate of degradation. These results highlight the importance of avoiding broad generalizations about Li-ion battery temperature dependence.

25 ENERGY STORAGE↗

DOE OSTI2021

Lessons Learned—Lithium Silicide Hydration Fire

Alkali metals, such as lithium, sodium, potassium, etc., are highly reactive elements. While researchers generally handle these metals with caution, less caution is taken when these elements have been “reacted”. In this work, a recent incident is examined in which a pair of researchers ignited a lithium silicide alloy sample that was assumed to be fully hydrated to lithium hydroxide and, thereby, no longer water-reactive. However, variations in the original chemical composition of the lithium compounds examined resulted in select mixtures failing to hydrate and react completely to lithium hydroxide in the time frame allowed. This gave rise to residual unreacted, water-sensitive lithium silicide which resulted in a violent exothermic reaction with water and autoignition of the produced hydrogen gas. This Article describes this incident and improvements that can be implemented to prevent similar incidents from occurring.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Lessons Learned—Fluoride Exposure and Response

Laboratory research can expose workers to a wide variety of chemical hazards. Researchers must not only take personal responsibility for their safety but also inevitably rely on coworkers to also work safely. The foundations for protocols, requirements, and behaviors come from our history and lessons learned from others. For that reason, here, a recent incident is examined in which a researcher suffered hydrofluoric acid (HF) burns while working with an inorganic digestion mixture of aqueous HF (8%) and nitric acid (HNO 3 , 58%). HF education is critical for workers because delays in treatment, improper treatment, and delay of symptoms are all factors in unfavorable outcomes in case reports. Furthermore, while the potential severity of the incident was elevated due to bypassed engineered controls and lack of proper personal protective equipment, only minor injuries were sustained. We discuss the results of a causal analysis of the incident that revealed areas of improvement in protocols, personal protective equipment, and emergency response that could help prevent similar accidents from occurring. We also present simple improvements that anyone can implement to reduce the potential consequences of an accident, based upon our lessons learned.