NASA NTRS2024

Effects of Specimen Geometry on Flatwise Tensile Strength

The through-thickness or flatwise strength of a uniaxial polymer matrix composite was investigated with several test specimen geometries and starting plate thicknesses. The use of thinner plates is desirable to save material and lower costs during materials development programs. The various configurations gave similar results with the exception of thin, straight-sided specimens. Thin specimens tended to provide invalid results per ASTM International D7291; however, the addition of a large, shallow radius improved the results. The Weibull distribution provided a good fit to the combined data.

Polymer matrix composite↗

NASA NTRS2024

Residual Strength of Hypervelocity Impacted Silica

Windows in the International Space Station (ISS) are subject to ongoing micrometeoroid and orbital debris (MMOD) damage. The reliability of the windows is ensured by monitoring of damage, life prediction, and measurement of the residual strength of man-made and natural hypervelocity impacted window materials. Information on the residual strength of man-made craters and MMOD craters harvested from space shuttle windows was used to estimate strength as a function of damage dimensions and thereby derive design allowables for U.S. and Russian fused silicas used in the ISS. An effect of impact angle is apparent, with 0° impacts exhibiting the lowest strength for Russian quartz-derived silica. The crater morphology for fused silica consists of a central pit, crush zone, shallow rings, and radial cracks dividing shallow, petal-like lateral cracks (petaloids). The morphology of alkaline glass differs from that of fused silica, with a more distinct pit and pulverized region, and bell-shaped and tail-like features below the pit.

International space station,↗

NASA NTRS2024

Investigation of Carbon-Reinforced Acrylonitrile Butadiene Styrene 3D-Printed Honeycomb Composites

The expansive utility of polymeric 3D printing technologies and demand for high-performance lightweight structures has prompted the emergence of various carbon-reinforced polymer composite filaments. However, detailed characterization of the processing-microstructure-property relationships of these materials is still required to realize their full potential. In this study, acrylonitrile butadiene styrene (ABS) and carbon reinforced ABS variants, both carbon nanotubes (CNT) and 5 wt.% chopped carbon fiber (CF), are fabricated in a honeycomb geometry and investigated across a range of layer thicknesses and hex sizes. Microscopy of material cross-sections is conducted to evaluate the relationship between print parameters and porosity. Additionally, mechanical properties are evaluated through compression testing, demonstrating the potential of honeycomb ABS, ABS-CNT, and ABS-5wt.% CF polymer composites for novel 3D printed structures.

ABS (Acrylonitrile Butadiene Styrene)↗

NASA NTRS2024

Thermal Conductivity and Mechanical Properties of Epoxy Composites With Hybridized PAN- and Pitch-Based Fiber Architecture

A series of hybrid polyacrylonitrile- (PAN-) and pitch-based carbon fiber/epoxy composites were fabricated and tested to evaluate the influence of hybrid fiber configurations on composite strength, modulus, and through-thickness thermal conductivity. Two grades of pitch-based fiber were selected based on their thermal conductivity: YSH-60A and YSH-80A from Nippon Graphite. These pitch-based fibers were received in tow form and as plain weave to allow flexibility in the architecture of the multifiber laminate. Two hybridization approaches were followed: (1) interleave of pitch-based fiber weave within braided PAN/epoxy prepreg and (2) incorporation of pitch-based fiber tows within a three-dimensional braided preform. These showed considerable impact on overall composite mechanical properties and through-thickness thermal conductivity.

Polymer Composite↗

NASA NTRS2023

The Effect of Oxidation in Environmental Barrier Coatings Subject to Foreign Object Damage

Oxidation and foreign object damage (FOD) are two key failure modes for environmental barrier coatings (EBCs). For EBCs with a silicon (Si) bond coat, a thermally grown oxide (TGO) layer forms at the EBC –bond coat interface. The TGO layer is considered the weak interface, and directly influences the life of the EBC. Moreover, FOD has been shown to cause significant subsurface damage resulting in delamination or spallation of the EBC which can occur at the EBC -bond coat interface or the bond coat -substrate interface. The purpose of this work is to investigate the synergistic effects of oxidation and FOD in a ytterbium disilicate (𝑌𝑏2𝑆𝑖2𝑂7) EBC. FOD testing is conducted on as-deposited and steam oxidized samples at room temperature using a 1.59-mm hardened steel ball projectile. The resulting damage is characterized by optical profilometry and scanning electron microscopy (SEM). Additionally, a quasi-static, mechanical assessment of the EBC bond strength in the presence of a growing TGO is presented.

environmental barrier coatings (EBCs)↗

NASA NTRS2022

Fracture Mechanics Properties of Fused Silicas Used for International Space Station Windowpanes

The fracture toughness and slow crack growth (SCG) parameters of a quartz-based silica and a high-purity fused silica were measured as part of a program to review the reliability of the International Space Station windows. The materials exhibit the same fracture toughness (.75 MPa m^(1/2) in N2) and very similar SCG parameters. The literature on fused silica indicates excellent agreement of fracture toughness, but a very wide range of SCG parameters, even from the same institution, with strength-based methods usually yielding a lower power law exponent than direct crack velocity measurements. Use of the exponential function is shown to provide better agreement between test methods, with velocity curves derived from strength tests of bare fiber and polished or ground test specimens paralleling those from wide-range, direct crack velocity observations, implying that constant stress rate tests can predict long lifetime via the exponential function. However, much variation still exists. SCG parameters for soda–lime silicate are much less sensitive to the test method than fused silica. Static load tests and stress intensity measurements resulted in a fatigue threshold of .3 MPa m^(1/2) for fused silica.

Silica, toughness, impact, crack growth, windows, ↗

NASA NTRS2021

Interpretation of Zerodur® Strength Data

Recent, detailed fractographic analysis of Zerodur® strength test specimens prepared by linear grinding and etching with a proprietary process indicated low frequency damage to be the strength limiting defects Recent, detailed fractographic analysis of Zerodur® strength test specimens prepared by linear grinding and etching with a proprietary process indicated low frequency damage to be the strength limiting defects [1]. The 2-parameter Weibull distribution is usually assumed when working with ceramic and glasses such as Zerodur®, although 3-parameter behavior is occasionally considered [2]. Detailed statistical modeling of the Zerodur® strength data with the was initial perspective of a 3-parameter Weibull distribution gave unsatisfying results [3]. The subsequent fractographic investigation indicated [1] that the usual assumption of many small, random, noninteracting flaws [4] was not represented, but instead, less frequent, aligned flaws along etching ridges parallel to the grinding direction were present, Figure 1. It was thus concluded that the strength of Zerodur® as prepared was not Weibull distributed. The flaws represent a sparse flaw population relative to typical grinding damage, but an extensive occurrence (high frequency) of handling damage. We examine the type of distribution present and explain the appearance of a 3-parameter distribution.

Glass, ceramic, strength, Weibull, distribution, m↗

NASA NTRS1988

Fracture resistance of a TiB2 particle/SiC matrix composite at elevated temperature

The fracture resistance of a commercial TiB 2 particle/SiC matrix composite was evaluated at temperatures ranging from 20 to 1400 °C. A laser interferometric strain gauge (LISG) was used to continuously monitor the crack mouth opening displacement (CMOD) of the chevron-notched and straight-notched, three-point bend specimens used. Crack growth resistance curves (R-curves) were determined from the load versus displacement curves and displacement calibrations. Fracture toughness, work-of-fracture, and R-curve levels were found to decrease with increasing temperature. Microstructure, fracture surface, and oxidation coat were examined to explain the fracture behavior.

Fracture↗