Studies of Lubricating Materials in Vacuum

Lubricating materials for use in a vacuum environment have been the subject of a series of experimental investigations. Evaporation properties were evaluated for solid polymeric compositions. Friction and wear studies explored the behavior during sliding contact for series of polymeric compositions, binary alloys containing soft film-forming phases, complex alloys with film-forming materials, and a burnished MoS2 film. Friction and wear experiments were conducted at 10(exp-9)mm Hg with a 3/16-inch-radius-hemisphere rider specimen sliding on the flat surface of a rotating 2-1/2-inch-diameter disk specimen with materials that had low rates of evaporation. The influence of fillers in polytetrafluoroethylene (PTFE) on decomposition during vacuum friction studies was determined with a mass spectrometer. A real advantage in reducing decomposition and improving friction wear properties is gained by adding fillers (e.g., copper) that improve thermal conductivity through the composite materials. A polyimide and an epoxy-MoS2 composition material were found to have better friction and wear properties than PTFE compositions. A series of alloys (cast binary as well as more complex alloys) that contained microinclusions of potential film-forming material was studied. These materials replaced the normal surface oxides as they were worn away on sliding contact. Iron sulfide, nickel oxide, and tin are typical film-forming materials employed and were demonstrated to be effective in inhibiting surface welding and reducing friction. A burnished MoS2 film applied to type 440-C stainless steel in argon with a rotating soft wire brush had good endurance properties but somewhat higher friction than commercially available bonded films. An oil film applied to the burnished MoS2 markedly reduced its endurance life.

WEAR↗
NASA NTRS1960

A Solid Film Lubricant Composition for Use at High Sliding Velocities in Liquid Nitrogen

Solid-lubricant-containing compositions can be of value as films and solid bodies for bearing and seal surfaces in low-temperature liquefied gases. An experimental composition including polytetrafluoroethylene (PTFE), an epoxy resin, and lithium-alumina-silicate was studied in friction, wear, and endurance experiments in liquid nitrogen (−320 F). This composition was formulated to approximate the thermal expansion of metals used in cryogenic systems. Hemisphere (3/6-in. radius) rider specimens were used and in most experiments the load was 1000 g. Films (0.005-in. thick) on disk specimens gave good endurance life, low rider wear, and desirable friction (f = 0.02 to 0.07). They functioned at a higher sliding velocity (no failure at 16, 000 ft/min) with copper rider specimens than with stainless steel riders (failure at 9000 ft/min). Solid rider material of the experimental composition had good friction and wear properties at sliding velocities above 4000 ft/min. It is important to use the experimental composition with mating materials having good thermal conductivity.

Wisander, D. W.↗