Dynamic and static corrosion of chromium-alumina refractory in simulated nuclear waste glass

Monofrax® K-3, a chromium–alumina refractory, is widely used in nuclear waste glass melters due to its high durability. However, aggressive vitrification conditions still lead to corrosion that limits melter lifespan. Here, this study investigates two key corrosion modes, subsurface and melt-line corrosion, under static and dynamic conditions, using a custom setup enabling precise control of melt velocity and temperature. Experimental results, interpreted using diffusion-limited dissolution models, show that (i) subsurface corrosion increases by approximately 10% per mm/s increase in melt velocity, while melt-line corrosion remains virtually unaffected, (ii) corrosion rate dependence on temperature is inversely proportional to melt viscosity, and (iii) glass composition affects both corrosion modes similarly, based on Cr 2 O 3 , Al 2 O 3 , and alkali contents. The experimental data also allowed the determination of diffusion coefficients of major dissolving species, which were found to be consistent between the melt-line and subsurface corrosion models, indicating their suitability for future CFD studies.

12 - MGMT OF RADIOACTIVE AND NON-RADIOACTIVE WASTE

Glass Property-Composition Models Update for use in Direct Feed High-Level Waste Flowsheet Development

A set of preliminary glass property models and constraints were developed and augmented by models from literature for use in design of direct-feed high-level waste (DFHLW) glasses for flowsheet evaluation, testing, and design of the Tank Waste Treatment and Immobilization Plant (WTP) high-level waste (HLW) Facility. These models and constraints are meant to be used as a place-holder while glass property-composition data gaps are filled and final plant operating models are developed. This report describes the motivation and intended use of the models, the compilation of data, model fitting and selection, methods to apply the models and constraints in glass design and offers example calculations demonstrating their intended use.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W

K-3 Refractory Corrosion Test Results, HAL24M2

This report summarizes the refractory corrosion data of the high-Al matrix of Direct Feed High-Level Waste (DFHLW) glasses generated to expand glass compositional ranges. Design of a 20 high-Al glass matrix, HAL24M2, was reported in Russell et al. (2025, in progress). The HAL24M2 glasses were tested for K-3 corrosion and the results are presented in this report. Corrosion of Monofrax K-3 refractory materials in the HAL24M2 glass melts was measured using a crucible-scale method. Two test conditions, 1150 °C/7days and 1200 °C/7days were applied. The melt-line neck corrosion depth of the test coupons was measured by micro-computed tomography (micro-CT). The measured K-3 neck corrosion values were compared to predicted values using the model in Vienna et al. (2024). The model slightly over-predicted the neck corrosion depth of these glasses.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W

Direct Feed High-Level Waste APPS Model Glass Testing (DFHLW APPS) Matrix, Phase 2

This report summarizes the data collected during the batching and melting of a second matrix of Direct Feed High-Level Waste (DFHLW) glasses generated using the preliminary enhanced waste glass models (EWG2.5) and the Britton and Anderson (2024) preliminary DFHLW feed vector. The purpose of these glasses is two-fold: 1. Validate EWG2.5 glass calculations being used in the Aspen Process Performance Simulation (APPS) model. 2. Evaluate and ultimately improve the glass property models and formulation methods used for design of DFHLW glasses as part of an iterative process of data collection and model refinement. Some of the 16 APPS2 glasses tested did not satisfy all target property constraints due to the limited data on DFHLW glass supporting the EWG2.5 models. • One glass, APPS2-10, formed nepheline on canister centerline cooling (CCC) heat-treatment and failed the product consistency test (PCT) response limits. This glass also had high B and Cr release rates for the toxicity characteristic leaching procedure (TCLP). All other glasses were found to satisfy the PCT and TCLP constraints for both quenched and CCC samples. • One glass, APPS2-08, had higher than acceptable viscosity due to magnetite crystallization. • One glass, APPS2-09, formed greater than 2 vol% crystals at 950 °C. As the glass design criterion was that the temperature at 2 vol% crystal (T 2% ) be less than 950 °C, only one glass failed the criteria. However, this criterion is being reevaluated. Four additional glasses formed crystal fractions between 1 and 2 vol% at 950 °C (APPS2-03, -08, -12, and -14). • Four glasses – APPS2-01, -02, -04, and -16 – failed the Monofrax K-3 refractory neck corrosion (k neck ) design limit of 0.04 in. at 1208 °C for 6 d. This is another criterion being reevaluated. Four additional glasses (APPS2-05, -06, -11, and -13) exhibited 0.025 = k neck = 0.04 in. • All 16 glasses passed the sulfur solubility and TCLP constraints. The measured property values were compared to predicted values using EWG2.5 and a selection of other existing models. A few models (e.g., electrical conductivity, TCLP) were found to be adequate for designing DFHLW glasses in the near future, while others require refits or offsets. It is recommended that new property models be developed for EWG3.0, as a large amount of DFHLW glass property data (> 14 × existing data) is expected to be collected in the compositional spaces where no data was previously available. To enable near-term calculations and formulations for designing DFHLW glasses and processing rate estimations, a formulation algorithm with minor modifications will be developed, EWG2.6.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W