Engineering Papers⌕ Search

Engineering topics

Jewell, R. A.

Publications and source records attributed to Jewell, R. A..

14 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1978

Solventless LARC-160 Polyimide Matrix Resin

The addition polyimide, LARC-160, which was originally synthesized from low cost liquid monomers as a laminating resin in ethanol, was prepared as a solventless, high viscosity, neat liquid resin. The resin was processed by hot-melt coating techniques into graphite prepreg with excellent tack and drape. Comparable data on graphite reinforced laminates made from solvent-coated and various hot-melt coated prepreg were generated. LARC-160, because of its liquid nature, can be easily autoclave processed to produce low void laminates. Liquid chromatographic fingerprints indicate good reaction control on resin scale ups. Minor changes in monomer ratios were also made to improve the thermal aging performance of graphite laminates.

Stclair, T. L.↗
NASA NTRS1977

A new polyimide laminatine resin

Addition polyimide for composite materials is based on liquid monomers and has significant advantages over most existing high-temperature resins. Essentially solventless prepreg has improved drape, tack.

Barrick, J. D. W.↗
NASA NTRS1976

LaRC-160 - A new 550 F polyimide laminating resin

A new addition polyimide, LaRC-160, based on liquid monomers has been prepared. The essentially solventless prepreg retains good drape and tack. Unidirectional HT-S composites were fabricated and tested before and after aging at temperatures between 505 K and 589 K (450 F and 600 F). Excellent retention of mechanical properties was realized after 2000 hours at 547 K (525 F). This material should be a candidate for solventless prepregging due to the liquid nature of the monomeric mixture.

St. Clair, T. L.↗