Robust RF Photocathodes (Phase II Final Report)
This program addressed requirements for photocathodes with high quantum efficiency (QE) and long lifetimes. Currently, photocathodes with QEs above 1% exhibit lifetimes measured in a few hours. This is unacceptable for commercial devices using photocathodes as the electron source. This includes accelerators for industrial, medical, defense, and educational applications as well as emerging applications, such as time resolved electron microscopy. Calabazas Creek Research, Inc. (CCR) and the University of Maryland (UMD) attempted to develop reservoir photocathodes that dramatically increased lifetime and increased the ability to recover from contaminating events, such as loss of system vacuum. The Phase I program demonstrated the viability of the reservoir approach for higher QE cathodes. The Phase II program focused on design, fabrication, and delivery. This included increasing understanding of photocathode physics, investigating design options, addressing performance issues, and developing fabrication and packaging techniques leading to commercial products. The initial task identified specific photocathode materials that provide high QE and are compatible with the reservoir approach. The goal was that these photocathodes be manufacturable in a production environment, understanding that the “environment” is highly specialized. The photocathode geometry was modified to address several photogun performance issues related primarily to emittance. A goal was to reduce or eliminate thermal emittance issues arising from the reservoir heater. The program developed fabrication, handling, and transport techniques and facilities to allow commercial photocathode production for certain materials. Not only was complex chemistry involved, but practical issues of transporting and installing the cathodes into user systems were addressed. A critical goal was demonstration of reservoir photocathodes in operating RF guns, where performance could be directly measured. Success depended on clear demonstration that the cathodes could be produced, delivered, installed, and provide the required performance. The principal effort in this program was to develop reservoir cesium antimonide photocathodes. Cesium antimonide cathodes provide a work function in excess of the 1% goal, while the current generation exhibits lifetimes measured in hours. The reservoir in CCRs’ controlled porosity reservoir (CPR) cathodes provides a mechanism for replacing cesium evaporating from the surface by transporting replacement cesium from the reservoir. This is accomplished by gently heating the reservoir to induce cesium diffusion through micron-scale pores in the reservoir cap and photocathode emitter. Experiments at the UMD determined that cesium diffused from the reservoir would only react with antimony on the surface if the temperature exceeded 300C. At this temperature, however, the surface cesium evaporated faster than it could be replenished from the reservoir. Consequently, the QE decreased each time recessiation was attempted. This appears to be a fundamental problem with this approach. The sections below provide information on accomplishments for each task in the program. Once the issue with cesium antimonide cathodes was identified, CCR refocused the program to begin investigation of graphene coated photocathodes in collaboration with SLAC National Accelerator Laboratory (SLAC). The photocathode test chamber developed in the program was transferred to SLAC for use in the graphene research. This is described below in a task added to the program.