Engineering topics
Publications and source records attributed to Jensen, Kenneth A..
The present invention is directed to a method and apparatus for producing a highly -textured surface on a copper substrate -with only extremely small amounts of texture-inducing seeding or masking material. The texture-inducing seeding material is delivered to the copper substrate electrically switching the seeding material in and out of a circuit loop.
The present invention is directed to a method and apparatus for producing a highly-textured surface on a copper substrate with only extremely small amounts of texture-inducing seeding of masking material. The texture-inducing seeding material is delivered to the copper substrate electrically switching the seeding material in and out of a circuit loop.
Circuit reliably switches power at supply potential of minus 1,500 V, with controlled frequency and duty cycle. Used in argon-plasma ion-bombardment equipment for texturing copper electrodes, as described in "Texturing Copper To Reduce Secondary Emission of Electrons" (LEW-15898), also adapted to use in powering gaseous flash lamps and stroboscopes.
Ion-beam process produces clean, deeply textured surfaces on copper substrates with reduced secondary electron emission. In process, molybdenum ring target positioned above and around copper substrate. Target potential repeatedly switched on and off. Switching module described in "High-Voltage MOSFET Switching Circuit" (LEW-15986). Useful for making collector electrodes for traveling-wave-tube and klystron microwave amplifiers, in which secondary emission of electrons undesirable because of reducing efficiency.
The present invention is directed to a method and apparatus for producing a highly-textured surface on a copper substrate with only extremely small amounts of texture-inducing seeding or masking material. The texture-inducing seeding material is delivered to the copper substrate electrically switching the seeding material in and out of a circuit loop.
Untreated oxygen-free, high-conductivity (OFHC) copper, commonly used for MDC electrodes, exhibits relatively high secondary electron emission characteristics. This paper describes a specialized ion-bombardment procedure for texturing copper surfaces which sharply reduces the emission properties relative to untreated copper. The resulting surface is a particle-free, robust, uniformly highly-textured all-metal structure. The use of this process requires no modifications to copper machining, brazing, or other MDC normal fabrication procedures. The flight TWT for a planned NASA deep space probe, the Cassini Mission, will incorporate copper MDC electrodes treated with the method described here.
A method for producing a uniform, highly textured surface on oxygen-free, high conductivity (OFHC) copper by ion bombardment using sputtered molybdenum as a texture-inducing masking film was developed and used to provide samples for study. The purpose was to develop a basically OFHC copper surface having very low secondary electron emission characteristics. Surfaces having low secondary electron emission are a requirement for the electrodes of very high efficiency multistage depressed collectors (MDC's). Such MDC's are used in microwave amplifier traveling wave tubes for space communications and other applications. OFHC copper is the material most commonly used for MDC electrodes because it has high thermal conductivity, it is easy to machine, and its fabrication and brazing procedures are well established. However, its untreated surface displays relatively very high levels of secondary electron emissions. Textured OFHC copper samples were tested for true secondary electron emission and relative reflected primary electron yield at primary electron beam energy levels from 200 to 2000 eV and at direct (0 deg) to oblique (60 deg) beam impingement angles. The test results for three of the samples, each of which was processed in a slightly different way, are compared with each other and with test results for a machined OFHC copper sample. Although the textured samples are not represented here as having been processed optimally, their measured secondary electron emission characteristics are significantly lower than those of the untreated OFHC copper sample over the range of conditions studied. Importantly, the relative reflected primary electron yield of one of the textured samples is conspicuously lower than that of the others. Clearly, with further development, the molybdenum-masked ion-textured OFHC copper surface will be a promising material for high-efficiency MDC electrodes.
Experimentally determined values of true secondary electron emission and relative values of reflected primary electron yield are presented for untreated (simply machined) and ion-textured, high-purity titanium over ranges of primary electron beam energies and beam impingement angles. The purpose of the investigation was to explore the feasibility of using titanium as electrode material in the multistage depressed collectors (MDC's) used in microwave amplifier traveling wave tubes (TWT's) for space communications and aircraft applications. Because of its relatively low density and thermal expansion characteristics and relatively high strength, thermal emissivity, and melting temperature, titanium presents itself as a possible candidate for the MDC electrode application. A detailed description of the method of ion texturing the titanium is included. Although the ion-treated surface considered in this study is not presented as being optimum from the standpoint of secondary electron emission suppression, it nevertheless serves to demonstrate that the surface can be modified by this procedure to significantly reduce these emission characteristics relative to those of the untreated surface. Further studies can reasonably be expected to produce surfaces with even lower secondary emission characteristics. The titanium surface were tested at primary electron beam energies of 200 to 2000 eV and at direct (0 deg) to near-grazing (85 deg) beam impingement angles. True secondary electron emission and relative reflected primary electron yield characteristics of the surfaces were compared with each other and with textured titanium surface exhibited secondary electron emission characteristics sharply lower than those exhibited by untreated titanium or copper. Clearly, then, in consideration of the secondary electron emission suppression of ion-textured titanium along with its other favorable physical properties, it must be included as a potential candidate for use as MDC electrode material in some applications.