NASA NTRSDate not supplied

Progressive Damage Failure Analysis of a Multi-Stringer Post-Buckled Panel

Validation of a progressive damage finite element analysis model using the CompDam material model was performed on a large multi-stringer panel subjected to compressive loading. The panel had a Teflon insert embedded between the skin panel and stiffener to cause an ultimate failure mode of stiffener separation. The compressive loading of the panel caused the skin between the stiffeners to locally buckle before any damage began to occur. The post-buckled behavior of the panel was the driving mechanism to the onset of damage and the damage growth that led to skin-stiffener separation. An integrated global-local modeling approach was used to validate several aspects the overall behavior of the panel from start to failure. The global region captured the pre-buckled stiffness of the test panel within 10% and the buckling load of the skin panel at the critical location within 2%. The skin’s five half-wave buckled mode shape was accurately predicted by the model. The integrated local model captured the load corresponding to the onset of damage within 5% of the average test data. Comparisons are made for key aspects of the damage morphology, such as a growth pattern that included a significant matrix split in the first ply of the skin and a migration of the delamination from the skin-stiffener interface to the skin’sply1-ply2 interface. The ultimate failure mode was shown to be an unstable growth of delamination damage under the stiffeners which led to a peak load of the analysis that was approximately 5% above the average peak load of the testing. The validated global-local modeling approach used on the multi-stringer post-buckled panel with a Teflon insert used a methodology and lessons learned using smaller specimens applied to a subcomponent that captured several aspects of a modern aircraft design.

Jason Action↗

NASA NTRSDate not supplied

Testing of a Multi-Stringer Post-Buckled Panel with Incremental Damage Detection

A multi-stringer panel was designed and tested to produce a failure mode of skin-stiffener delamination due to compression loading of a post-buckled skin to support the validation of high-fidelity progressive damage failure analysis modeling. The test procedure included multiple methods of data acquisition ranging from multiple strain gages, front and back digital image correlation, passive thermography, acoustic emission, and ultrasonic inspection to capture key events and damage progression prior to catastrophic failure. Detailed data showing the initial stiffness, onset of skin buckling, buckled mode shape, damage initiation load, damage propagation morphology, and peak load was captured. Two panel configurations were tested. The first had a Teflon insert placed in the interface between the skin and the stiffener flanges adjacent to the center skin bay. The second was subjected to impact damage to the skin-stiffener flange. In each case, continuously-loaded-to-failure tests were conducted first with passive thermography being used exclusively to determine key damage events. Then, incrementally loaded tests were completed where ultrasonic inspections were conducted between each increment. The amount of load applied between each increment was determined based on the in-situ damage detection provided by the passive thermography system. The results of the testing showed a complex delamination growth pattern which migrated between ply interfaces through matrix splits in the upper skin ply of the panel. The result of the testing produced very detailed data which will prove to be useful for validation of delamination growth and migration predictions from progressive damage failure analysis methods.

Jason Action↗

NASA NTRSDate not supplied

Progressive Damage Failure Analysis of Post-Buckled Composite Single-Stringer Panel with Teflon Inserts

The high strength-to-weight and stiffness-to-weight ratio materials, such as laminated composites, are advantageous for modern aircraft. Laminated composites with initial flaws are susceptible to delamination under buckling loads. PDA tools help enhance the industry’s understanding of the mechanisms for damage initiation and growth in composite structures while assisting in the design, analysis, and sustainment methods of these composite structures. The global-local modeling approach for the single-stringer post-buckled panel was evaluated through this effort, using Teflon inserts to simulate the defect of damage during manufacturing. This understanding is essential for designing the post-buckled structure, reducing weight while predicting damage initiation location, and addressing a potential design review for future aircraft repairs. In this work, the initial damage was captured with Teflon inserts as the starting configuration; and any reference to the damage initiation refers to any damage beyond the “initial unbonded region.” The effort aims to develop, evaluate, and enhance methods to predict damage initiation and progression and the failure of post-buckled hat-stiffened panels using multiple Abaqus FEA Virtual Crack Closure Technique (VCCT) definitions. Validation of the PDA using the VCCT material model was performed on a large single-stringer panel subjected to compressive loading. The compressive loading of the panel caused the skin to buckle before any damage began to occur locally. In addition, comparisons are made for critical aspects of the damage morphology, such as a growth pattern that included delamination from the skin-stiffener interface to the skin and ply interfaces. When compared against the experimental data produced through the NASA Advanced Composites Project (ACP), the present model captured damage migration from one surface to another, and model validations were within 4% of the experimental data.

PDA↗