Imig, L. A.

Publications and source records attributed to Imig, L. A..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1982

Heating and cooling system

A heating and cooling apparatus capable of cyclic heating and cooling of a test specimen undergoing fatigue testing is discussed. Cryogenic fluid is passed through a block clamped to the speciment to cool the block and the specimen. Heating cartridges penetrate the block to heat the block and the specimen to very hot temperaures. Control apparatus is provided to alternatively activate the cooling and heating modes to effect cyclic heating and cooling between very hot and very cold temperatures. The block is constructed of minimal mass to facilitate the rapid temperature changes.

Imig, L. A.↗
NASA NTRS1981

Temperature controller adapts to fatigue tester

Identical blocks of aluminum, held against front and back of specimen, each contain electrical heaters, liquid nitrogen cavity with input and exhaust tubes, and thermocouple. Thermocouples are connected to control unit, which adjusts specimen temperature during fatigue tests over range of 850 degrees F.

Imig, L. A.↗
NASA NTRS1979

Fatigue failure load indicator

An indicator for recording the load at which a fatigue specimen breaks during the last cycle of a fatigue test is described. A load cell is attached to the specimen which is alternately subjected to tension and compression loads. The output of the load cell which is proportional to the load on the specimen is applied to the input of a peak detector. Each time the specimen is subjected to a compression load, means are provided for applying a positive voltage to the rest of the peak detector to reset it. During the last cycle of the tension load the peak detector measures the maximum load on the specimen. Means are provided for disconnecting the load cell from the peak detector when there is a failure in the specimen.

Imig, L. A.↗
NASA NTRS1976

Fatigue of titanium alloys in a supersonic-cruise airplane environment

The test programs conducted by several aerospace companies and NASA, summarized in this paper, studied several titanium materials previously identified as having high potential for application to supersonic cruise airplane structures. These studies demonstrate that the temperature (560 K) by itself produced no significant degradation of the materials. However, the fatigue resistance of titanium-alloy structures, in which thermal and loading effects are combined, has been studied insufficiently. The predominant topic for future study of fatigue problems in Mach 3 structures should be the influences of thermal stress particularly, the effects of thermal stress on failure location.

Imig, L. A.↗
NASA NTRS1976

Crack growth in Ti-8Al-1Mo-1V with real-time and accelerated flight-by-flight loading

Crack growth in Ti-8Al-1Mo-1V was measured and calculated for real-time and accelerated simulations of supersonic airplane loading and heating. Crack-growth rates calculated on the assumption that an entire flight could be represented by a single cycle predicted the experimental rates poorly. Calculated crack-growth rates were slower than the experimental rates for all tests with flight-by-flight loading. For room-temperature accelerated tests, the calculated rates agreed well with the experimental rates; but the calculations became progressively less accurate for progressively more complex test conditions (tests that included elevated temperature). Calculations of crack growth using the crack-closure concept can probably be improved through study of crack-opening stresses using finite-element models that account for variable-amplitude loading, residual stresses, and temperature effects. The calculations of crack growth could also be improved through detailed studies of material properties and interactions among stress, temperature, and time as appropriate for the real-time operating conditions of a supersonic transport airplane.

Imig, L. A.↗
NASA NTRS1975

Crack growth in Ti-8Al-1Mo-1V with real-time and accelerated flight by flight loading

Crack growth in Ti-8Al-lMo-lV was measured and calculated for real time and accelerated simulations of supersonic airplane loading and heating. Crack-growth rates calculated on the assumption that an entire flight could be represented by a single cycle predicted the experimental rates poorly. Calculated crack growth rates were slower than the experimental rates for all tests with flight-by-flight loading. For room temperature accelerated tests, the calculated rates agreed well with the experimental rates; but the calculations became progressively less accurate for progressively more complex test conditions (tests that included elevated temperature).

Imig, L. A.↗
NASA NTRS1974

Anti-buckling fatigue test assembly

An antibuckling fatigue test assembly is described for holding a metal specimen which is subjected to compression and to rapid cyclical heating and cooling while permitting visual observation. In an illustrative embodiment of this invention, the anti-buckling fatigue test apparatus includes first and second guide members between which the metal specimen is disposed and held, a heating assembly comprising a suitable heating source such as a quartz lamp and a reflecting assembly directing the heat onto the specimen, and a cooling assembly for directing a suitable cooling fluid such as air onto the specimen. The guide members each have a passage to permit the heat to be directed onto the specimen. An opening is provided in the reflecting assembly to permit visual inspection of that region of the specimen adjacent to the opening onto which the heat is directed.

Eichenbrenner, F. F.↗
NASA NTRS1973

Fatigue-test acceleration with flight-by-flight loading and heating to simulate supersonic-transport operation

Possibilities for reducing fatigue-test time for supersonic-transport materials and structures were studied in tests with simulated flight-by-flight loading. In order to determine whether short-time tests were feasible, the results of accelerated tests (2 sec per flight) were compared with the results of real-time tests (96 min per flight). The effects of design mean stress, the stress range for ground-air-ground cycles, simulated thermal stress, the number of stress cycles in each flight, and salt corrosion were studied. The flight-by-flight stress sequences were applied to notched sheet specimens of Ti-8Al-1Mo-1V and Ti-6Al-4V titanium alloys. A linear cumulative-damage analysis accounted for large changes in stress range of the simulated flights but did not account for the differences between real-time and accelerated tests. The fatigue lives from accelerated tests were generally within a factor of two of the lives from real-time tests; thus, within the scope of the investigation, accelerated testing seems feasible.

Imig, L. A.↗
NASA NTRS1973

Fatigue testing device

Anti-buckling assembly prevents buckling of sheet metal fatigue specimen when axial compressive load is applied. It provides for cyclic heating and cooling of specimen during testing. Assembly permits tests at two locations on specimen. Device has ports for visual, optical, or photographic monitoring of fatigue crack propagation in test specimen.

Eichenbrenner, F. E.↗
NASA NTRS1973

Fatigue of supersonic transport materials using simulated flight-by-flight loading

Methods to reduce the fatigue test time for structural materials which are candidates for supersonic transport airplanes were investigated by conducting real-time and accelerated fatigue tests. The tests employed sequences of stresses and temperatures to simulate the flights of a Mach 3 transport airplane. Some of the simulated flights were altered to determine the effect of the design mean stress and the number of stress cycles per flight on fatigue life. Salt solution was also applied in other tests. Notched Ti-8Al-1Mo-1V and Ti-6Al-4V were used in the investigation.

Imig, L. A.↗