NASA NTRS1986

Damage-induced property changes in composites subjected to cyclic thermal loading

Damage in the form of transverse cracks resulting from thermal loading is studied as it relates to the dimensional stability of flat laminates and stiffness changes in cylindrical tubes. Graphite-epoxy specimens were subjected to cyclic thermal loading in the temperature range -250 to + 250 F. It is shown that transverse cracking is the dominant damage mechanism in both types of structural elements. Fiber splitting is also quite common at the low test temperatures. Experimental results indicate that damage significantly reduces the inplane coefficients of thermal expansion of flat laminates and the torsional stiffness of the tubes. Theoretical predictions for coefficients of thermal expansion as a function of crack spacing in flat laminates followed the same trend as experimental results.

Herakovich, Carl T.↗
NASA NTRS1985

Effects of load proportioning on the capacity of multiple-hole composite joints

This study addresses the issue of adjusting the proportion of load transmitted by each hole in a multiple-hole joint so that the joint capacity is a maximum. Specifically two-hole-in-series joints are examined. The results indicate that when each hole reacts 50% of the total load, the joint capacity is not a maximum. One hole generally is understressed at joint failure. The algorithm developed to determine the load proportion at each hole which results in maximum capacity is discussed. The algorithm includes two-dimensional finite-element stress analysis and failure criteria. The algorithm is used to study the effects of joint width, hole spacing, and hole to joint-end distance on load proportioning and capacity. To study hole size effects, two hole diameters are considered. Three laminates are considered: a quasi-isotropic laminate; a cross-ply laminate; and a 45 degree angle-ply laminate. By proportioning the load, capacity can be increased generally from 5 to 10%. In some cases a greater increase is possible.

Hyer, M. W.↗
NASA NTRS1985

Stresses and deformations in cross-ply composite tubes subjected to a uniform temperature change: Elasticity and Approximate Solutions

The effects of a uniform temperature change on the stresses and deformations of composite tubes are investigated. The accuracy of an approximate solution based on the principle of complementary virtual work is determined. Interest centers on tube response away from the ends and so a planar elasticity approach is used. For the approximate solution a piecewise linear variation of stresses with the radial coordinate is assumed. The results from the approximate solution are compared with the elasticity solution. The stress predictions agree well, particularly peak interlaminar stresses. Surprisingly, the axial deformations also agree well. This, despite the fact that the deformations predicted by the approximate solution do not satisfy the interface displacement continuity conditions required by the elasticity solution. The study shows that the axial thermal expansion coefficient of tubes with a specific number of axial and circumferential layers depends on the stacking sequence. This is in contrast to classical lamination theory which predicts the expansion to be independent of the stacking arrangement. As expected, the sign and magnitude of the peak interlaminar stresses depends on stacking sequence.

Hyer, M. W.↗
NASA NTRS1985

The stress distribution in pin-loaded orthotropic plates

The performance of mechanically fastened composite joints was studied. Specially, a single-bolt connector was modeled as a pin-loaded, infinite plate. The model that was developed used two dimensional, complex variable, elasticity techniques combined with a boundary collocation procedure to produce solutions for the problem. Through iteration, the boundary conditions were satisfied and the stresses in the plate were calculated. Several graphite epoxy laminates were studied. In addition, parameters such as the pin modulus, coefficient of friction, and pin-plate clearance were varied. Conclusions drawn from this study indicate: (1) the material properties (i.e., laminate configuration) of the plate alter the stress state and, for highly orthotropic materials, the contact stress deviates greatly from the cosinusoidal distribution often assumed; (2) friction plays a major role in the distribution of stresses in the plate; (3) reversing the load direction also greatly effects the stress distribution in the plate; (4) clearance (or interference) fits change the contact angle and thus the location of the peak hoop stress; and (5) a rigid pin appears to be a good assumption for typical material systems.

Klang, E. C.↗
NASA NTRS1985

Thermally induced stresses and deformations in layered composite tubes

The thermally induced stresses and deformations in layered, orthotropic tubes are studied. The motivation for studying tubes is their likely application for use in space structures. Tubes are a strong candidate for this application because of their high structural efficiency, as measured by stiffness per unit weight, and their relative ease of fabrication. Also, tubes have no free edges to deteriorate or delaminate. An anticipated thermal condition for tubes in space is a circumferential temperature gradient. This type of gradient will introduce dimensional changes into the structure and may cause stresses large enough to cause damage to the material. There are potentially large differences in temperatures at different circumferential locations on the tube. Because of this, the effects of temperature dependent material properties on the stresses and deformations may be important. The study is composed of three parts: experiments to determine the functional form of the circumferential gradient and to measure tube deflections; an elasticity solution to compute the stresses and deformations; and an approximate approach to determine the effects of temperature dependent material properties.

Cooper, D. E.↗
NASA NTRS1985

The dynamic response of composite beams to axial impact

Large deformation response of simple composite structural elements to intense dynamic loadings is studied by focusing on the response of beams. Overall goals are to: design a simple test fixture to introduce crash related bending loads in beams; determine any difference between large deformation static and large deformation dynamic response; determine the influence of laminate stacking arrangements on the dynamic response, failure mode, and energy absorbed; and predict the dynamic response. Twelve different laminate orientations were investigated. Modeling of the response was done with an existing finite element program. The program computed nonlinear transient response analysis of a structure objected to a time varying load.

Derian, E. J.↗
NASA NTRS1985

Damage initiation at curved free edges - Application to uniaxially loaded plates containing holes and notches

The concept which imputes initial free edge interlaminar damage to the differences in material properties among adjacent laminae, formerly applied to straight free edges, is presently extended to the case of curved free edges through interpretation in terms of differences in the shear and elongation strains among adjacent laminae. Attention is given to both material property differences and laminate strain spatial distributions at the hole edge. Since a large strain level and a small difference in material properties are found to be as damaging as a small strain and large difference, interlaminar damage will probably begin at a circumferential location other than the net section. These findings are further explored in view of a second extension, using the edges replication technique to record damage at a curved free edge. The damage recorded for uniaxially loaded plates with central circular holes and semicircular edge notches are compared with difference theory predictions.

Klang, E. C.↗
NASA NTRS1985

Contact stresses in pin-loaded orthotropic plates

The effects of pin elasticity, friction, and clearance on the stresses near the hole in a pin-loaded orthotropic plate are described. The problem is modeled as a contact elasticity problem using complex variable theory, the pin and the plate being two elastic bodies interacting through contact. This modeling is in contrast to previous works which assumed that the pin is rigid or that it exerts a known cosinusoidal radial traction on the hole boundary. Neither of these approaches explicitly involves a pin. A collocation procedure and iteration were used to obtain numerical results for a variety of plate and pin elastic properties and various levels of friction and clearance. Collocation was used to enforce the boundary and iteration was used to find the contact and no-slip regions on the boundary. Details of the numerical scheme are discussed.

Hyer, M. W.↗
NASA NTRS1984

Stresses in pin-loaded orthotropic plates using photoelasticity

The stresses in transparent glass-epoxy plates loaded by a steel pin through a hole were determined by photoelasticity. The stresses around the hole edge, across the net section, along the shear out line, and on the centerline below the hole for quasiisotropic, unidirectional, and angle ply plates are outlined. Stresses in an isotropic comparison specimen are also presented. Stress concentration factors for several locations around the plates are tabulated. The experimental apparatus and the experimental technique are discussed. The isochromatic and isoclinic fringe patterns for the four plates are shown. A description of the necessary photoelastic theory is appended.

Hyer, M. W.↗
NASA NTRS1984

Contact stresses in pin-loaded orthotropic plates

The effects of pin elasticity, friction, and clearance on the stresses near the hole in a pin-loaded orthotropic plate are described. The problem is modeled as a contact elasticity problem using complex variable theory, the pin and the plate being two elastic bodies interacting through contact. This modeling is in contrast to previous works which assumed that the pin is rigid or that it exerts a known cosinusoidal radial traction on the hole boundary. Neither of these approaches explicitly involves a pin. A collocation procedure and iteration were used to obtain numerical results for a variety of plate and pin elastic properties and various levels of friction and clearance. Collocation was used to enforce the boundary and iteration was used to find the contact and no-slip regions on the boundary. Details of the numerical scheme are discussed.

Hyer, M. W.↗
NASA NTRS1984

Residual stresses in cross-ply composite tubes

The residual thermal stresses in 4-layer cross-ply tubes are studied. The tubes considered has a small radius to wall-thickness ratios and so elasticity solutions were used. The residual thermal stress problem was considered to be axisymmetric and three elasticity solutions were derived and the results compared with the results using classical lamination theory. The comparison illustrates the limitations of classical lamination theory. The three elasticity solutions derived were: plane stress, plane strain, and generalized plane strain, the latter being the most realistic. Residual stresses in both the hoop and axial direction is significant. Stacking arrangement effects the residual stress to some extent, as do the material properties of the individual lamina. The benefits of hybrid construction are briefly discussed.

Cohen, D.↗
NASA NTRS1984

An assessment of the accuracy of orthotropic photoelasticity

The accuracy of orthotropic photoelasticity was studied. The study consisted of both theoretical and experimental phases. In the theoretical phase a stress-optic law was developed. The stress-optic law included the effects of residual birefringence in the relation between applied stress and the material's optical response. The experimental phase had several portions. First, it was shown that four-point bending tests and the concept of an optical neutral axis could be conveniently used to calibrate the stress-optic behavior of the material. Second, the actual optical response of an orthotropic disk in diametral compression was compared with theoretical predictions. Third, the stresses in the disk were determined from the observed optical response, the stress-optic law, and a finite-difference form of the plane stress equilibrium equations. It was concluded that orthotropic photoelasticity is not as accurate as isotropic photoelasticity. This is believed to be due to the lack of good fringe resolution and the low sensitivity of most orthotropic photoelastic materials.

Hyer, M. W.↗
NASA NTRS1984

Stresses in a quasi-isotropic pin-loaded connector using photoelasticity

Birefringent glass-epoxy and a numerical stress separation scheme are used to compute the stresses in the vicinity of a pin-loaded hole. The radial and circumferential stresses at the hole edge, and the net section and shear-out stresses are computed. The numerical and experimental results are compared with the computed stresses. The fixture used to load the connector is discussed and typical isochromatic and isoclinic fringe patterns are presented. The stress-separation scheme is briefly discussed. Previously announced in STAR as N83-33220

Hyer, M. W.↗
NASA NTRS1984

Stresses around holes in pin-loaded orthotropic plates

The effects of pin elasticity, pin/hole friction, and pin/hole clearance on the stresses around a hole in a pin-loaded orthotropic plate were studied. The problem was modeled as a planar problem, the pin and plate being two elastic bodies interacting through contact. Complex variable elasticity, a collocation scheme to enforce the pin/hole boundary conditions, and an iteration procedure to find the contact, slip, and no-slip regions were used to obtain numerical results. The results indicate that pin elasticity is not as important a variable as friction and clearance are. A rigid pin assumption, as opposed to the popular cosinusoidal radial traction, can be used without much error but clearance and friction should not be ignored.

Hyer, M. W.↗
NASA NTRS1984

Response of long shallow cylindrical panels to radial line loads

The large displacement static response of shallow orthotropic panels subjected to lateral loading is examined both theoretically and experimentally. The panels are circular cylindrical open shells which are also thin and long. The straight edges are simply supported at a fixed distance apart, and the curved edges are free. The lateral load is a spatially uniform line load acting along the generator direction of the cylinder, and is directed radially inward toward the center of curvature. The load induces a circumferential thrust, and the panel can, and does, snap-through to an inverted configuration at the buckling load. The effect of load position on the response is also examined. The test panels discussed in the paper are /(90/0)3/S graphite-epoxy laminates. Nominal dimensions are a radius of 60 in., a thickness of 0.060 in., and an arc length of 12 in. Very good agreement between theory and experiment is achieved.

Johnson, E. R.↗
NASA NTRS1984

An assessment of the accuracy of orthotropic photoelasticity - Abbreviated report

A brief overview is presented of a comprehensive study whose aim was to assess the accuracy of orthotropic photoelasticity. Particular attention is given to calibration of the material, forward testing for global and local behavior, and backward testing for stress determination. The experimentally determined stresses were found to agree with the elasticity solution. It is concluded that orthotropic photoelasticity does not appear to have the resolution of its isotropic counterpart, this being a consequence of the inherent inhomogeneity of the material.

Hyer, M. W.↗
NASA NTRS1984

The effects of thermal cycling on matrix cracking and stiffness changes in composite tubes

The study investigated the accumulation of transverse matrix cracks and the resultant loss of torsional, extensional, and bending stiffnesses in 8 layer 0.5 in. diameter crossply tubes subjected to thermal cycling. The tubes were graphite-epoxy and the temperature range during cycling was -250 to 200 F. The effect of fiber and matrix properties was investigated through the use of T300 and P75S fibers and 934 and CE339 resins. The study considered 0, 10, 50, 100, 300, and 500 thermal cycles. Photomicrographs, X-rays, and edge replication were used to evaluate cracking. Special loading fixtures were used to measure stiffness changes. An important finding was that for the tubes studied, even with extensive cracking, the bending and extensional stiffnesses were not affected. The torsional stiffness, however, was strongly affected.

Cohen, D.↗