Hu, Hongjie | Engineering Papers

DOE OSTI2022

Perovskite superlattices with efficient carrier dynamics

Compared with their three-dimensional (3D) counterparts, low-dimensional metal halide perovskites (2D and quasi-2D; B 2 A n-1 M n X 3n+1 , such as B = R-NH 3 + , A = HC(NH 2 ) 2 + , Cs + ; M = Pb 2+ , Sn 2+ ; X = Cl - , Br - , I - ) with periodic inorganic-organic structures have shown promising stability and hysteresis-free electrical performance. However, their unique multiple-quantum-well structure limits the device efficiencies because of the grain boundaries and randomly oriented quantum wells in polycrystals. In single crystals, the carrier transport through the thickness direction is hindered by the layered insulating organic spacers. Furthermore, the strong quantum confinement from the organic spacers limits the generation and transport of free carriers. Also, lead-free metal halide perovskites have been developed but their device performance is limited by their low crystallinity and structural instability 11 . Here, in this paper, we report a low-dimensional metal halide perovskite BA 2 MA n-1 Sn n I 3n+1 (BA, butylammonium; MA, methylammonium; n = 1, 3, 5) superlattice by chemical epitaxy. The inorganic slabs are aligned vertical to the substrate and interconnected in a criss-cross 2D network parallel to the substrate, leading to efficient carrier transport in three dimensions. A lattice-mismatched substrate compresses the organic spacers, which weakens the quantum confinement. The performance of a superlattice solar cell has been certified under the quasi-steady state, showing a stable 12.36% photoelectric conversion efficiency. Moreover, an intraband exciton relaxation process may have yielded an unusually high open-circuit voltage (V OC ).

36 MATERIALS SCIENCE↗

DOE OSTI2022

Impact of specimen preparation method on photovoltaic backsheet degradation during accelerated aging test

In this study, we highlight some important factors in the specimen preparation methods for evaluating photovoltaic backsheet properties after accelerated aging. Two different sequences are considered: Method (I) cut-then-age: cut into 1-cm wide strips and then expose to stress, and Method (II) age-then-cut: expose a larger sheet to stress and then cut into 1-cm widths for mechanical property measurements. We also compare the effect of three cutting methods, (a) tensile specimen punch, (b) paper cutter, and (c) fresh razor blade. Several commercial backsheets were evaluated, with stress exposures including (a) pressure cooker test (PCT), (b) dry ultraviolet (UV) radiation exposure, and (c) UV combined damp heat tests. Fourier transform infrared spectrometer (FTIR) and intrinsic viscosity (IV) were used to analyze the materials on unstressed materials and samples exposed to PCT. The results show that both the cutting method and the time of cutting have an impact on the backsheet mechanical properties. Additionally, under UV exposure, Method II, age-then-cut, generally resulted in a higher average value, with more variation than Method I; however, if the side strips from Method II were excluded, the variation dropped to the same level. This is because the specimens at the sides of the sheet get additional damage from UV light from the exposed sides of the sample. In contrast to UV exposure, PCT specimens prepared by Method II result in lower average values and higher variability. This is attributed to embrittlement through the bulk of the sample where the cutting of embrittled specimens appears to result in more edge defects which can then initiate a break at smaller strains. The data suggest that for UV exposures, the specimens should be cut after aging and the exposed side specimens discarded, and that for PCT exposures, the specimens should be cut before the exposure.

14 SOLAR ENERGY↗