NASA NTRS1991

Improved compression molding technology for continuous fiber reinforced composite laminates. Part 2: AS-4/Polyimidesulfone prepreg system

AS-4/polyimidesulfone (PISO2) composite prepreg was utilized for the improved compression molding technology investigation. This improved technique employed molding stops which advantageously facilitate the escape of volatile by-products during the B-stage curing step, and effectively minimize the neutralization of the consolidating pressure by intimate interply fiber-fiber contact within the laminate in the subsequent molding cycle. Without the modifying the resin matrix properties, composite panels with both unidirectional and angled plies with outstanding C-scans and mechanical properties were successfully molded using moderate molding conditions, i.e., 660 F and 500 psi, using this technique. The size of the panels molded were up to 6.00 x 6.00 x 0.07 in. A consolidation theory was proposed for the understanding and advancement of the processing science. Processing parameters such as vacuum, pressure cycle design, prepreg quality, etc. were explored.

Baucom, Robert M.↗

NASA NTRS1991

An improved compression molding technology for continuous fiber reinforced composite laminate. Part 1: AS-4/LaRC-TPI 1500 (HFG) Prepreg system

Poor processability of fiber reinforced high performance polyimide thermoplastic resin composites is a well recognized issue which, in many cases, prohibits the fabrication of composite parts with satisfactorily consolidated quality. Without modifying the resin matrix chemistry, improved compression modeling procedures were proposed and investigated with the AS-4/LaRC-TPI 1500 High Flow Grade (HFG) prepreg system. Composite panels with excellent C-scans can be consistently molded by this method under 700 F and a consolidation pressure as low as 100 psi. A mechanism for the consolidation of the composite under this improved molding technique is discussed. This mechanism reveals that a certain degree of matrix shear and tow filament slippage and nesting between plies occur during consolidation, which leads to a reduction of the consolidating pressure necessary to offset the otherwise intimate inter fiber-fiber contact and consequently achieves a better consolidation quality. Outstanding short beam shear strength and flexural strength were obtained from the molded panels. A prolonged consolidation step under low pressure, i.e., 100 psi at 700 F for 75 minutes, was found to significantly enhance the composite mechanical properties.

Hou, Tan-Hung↗

NASA NTRS1990

Thermoplastic polyimide NEW-TPI (trademark)

Thermal and rheological properties of a commercial thermoplastic polyimide, NEW-TPI (trademark), were characterized. The as-received material possesses initially a transient crystallite form with a bimodal distribution in peak melting temperatures. After the melting of the initial crystallite structure, the sample can be recrystallized by various thermal treatments. A bimodal or single modal melting peak distribution is formed for annealing temperatures below or above 360 C, respectively. The recrystallized crystallinities are all transient in nature. The polymers are unable to be recrystallized after being subjected to elevated temperature annealing above 450 C. The recrystallization mechanism was postulated, and a simple kinetics model was found to describe the behavior rather satisfactory under the conditions of prolonged thermal annealing. Rheological measurements made in the linear viscoelastic range support the evidence observed in the thermal analysis. Furthermore, the measurements sustain the manufacturer's recommended processing window of 400 to 420 C for this material.

Hou, Tan-Hung↗

NASA NTRS1990

LaRC TPI 1500 series polymers

The crystallization behavior and the melt flow properties of two batches of 1500 series LaRC-TPI polymers from Mitsui Toatsu Chemicals (MTC) were investigated. The characterization methods include Differential Scanning Calorimetry, the x ray diffractography and the melt rheology. The as-received materials possess initial crystalline melting peak temperatures of 295 and 305 C, respectively. These materials are less readily recrystallizable at elevated temperatures when compared to other semicrystalline thermoplastics. For the samples annealed at temperatures below 330 C, a semicrystalline polymer can be obtained. On the other hand, a purely amorphous structure is realized in the samples annealed at temperatures above 330 C. Isothermal crystallization kinetics were studied by means of the simple Avrami equation. The viscoelastic properties at elevated temperatures below and above glass transition temperature of the polymers were measured. Information with regard to the molecule sizes and distributions in these polymers were also extracted from melt rheology.

Hou, Tan-Hung↗

NASA NTRS1989

On processing development for fabrication of fiber reinforced composite, part 2

Fiber-reinforced composite laminates are used in many aerospace and automobile applications. The magnitudes and durations of the cure temperature and the cure pressure applied during the curing process have significant consequences for the performance of the finished product. The objective of this study is to exploit the potential of applying the optimization technique to the cure cycle design. Using the compression molding of a filled polyester sheet molding compound (SMC) as an example, a unified Computer Aided Design (CAD) methodology, consisting of three uncoupled modules, (i.e., optimization, analysis and sensitivity calculations), is developed to systematically generate optimal cure cycle designs. Various optimization formulations for the cure cycle design are investigated. The uniformities in the distributions of the temperature and the degree with those resulting from conventional isothermal processing conditions with pre-warmed platens. Recommendations with regards to further research in the computerization of the cure cycle design are also addressed.

Hou, Tan-Hung↗

NASA NTRS1987

A DSC study on crystalline LaRC TPI powder - A new version with higher initial molecular weight

A new version of crystalline Langley Research Center Thermoplastic Polyimide (LaRC-TPI) imidized powder, which possesses a higher initial molecular weight (MW), has been prepared and characterized. The scheme used for cyclodehydration during the synthesis of this material is described. Evidence of a higher initial MW for the subject LaRC-TPI is supported by both measurements of the inherent viscosity and the DSC thermograms. An initial melting peak at 295 C is noted in the freshly-synthesized sample. The powder can be recrystallized at any elevated temperatures below 340 C, and a single crystalline endothemic peak is always observed after various thermal histories. The heat of fusion for the fresh sample, as represented by the area under the melting peak in the directional scanning calorimeter thermogram, is about 3.9 cal/gm. Comparisons of thermal properties for the subject material are made to those exhibited by the commercial LaRC-TPI powder.

Hou, Tan-Hung↗

NASA NTRS1986

Characterization of crystalline LARC-TPI powder

LARC-TPI, a linear aromatic polyimide, developed by NASA Langley Research Center in the late 1970's had thermoplastic character, but its melt-flow properties were much lower than those of conventional thermoplastics. An imidized version of the LARC-TPI molding powder was submitted to NASA-Langley for evaluation. The initial broad melt of this material occurs in the 270 C range and reorders to higher melting forms, depending on the physical and thermal treatments. Rheological characterization of this polymer shows it to have a very low melt viscosity, which increases as the melted specie transforms to other crystalline forms with higher melting temperatures.

Burks, Harold D.↗