DOE OSTI2024

Correlation of Fabrication Methods and Enhanced Wear Performance in Nanoporous Anodic Aluminum Oxide with Incorporated Molybdenum Disulfide (MoS 2 ) Nanomaterials

Wear performance is integral to component longevity, minimizing industrial waste and excess energy costs in a wide variety of applications. Anodized aluminum oxide (AAO) has many beneficial properties leading to its wide use across industries as a surface treatment for many aluminum components, but the wear properties of the coating could be improved significantly. Here, we used an electrochemical method to incorporate molybdenum disulfide (MoS 2 ), a nanomaterial used as a dry lubricant, to modify alloys of aluminum during AAO preparation. Using Raman spectroscopy and tribological scratch measurements, we thoroughly characterized the structure and wear behavior of the films. The MoS 2 deposition procedure was optimal on aluminum 5052 anodized in higher acid concentrations, with friction coefficients at around 0.05 (~10× better than unmodified AAO). Changing anodization conditions to produce harder films with smaller pores led to worsened wear properties, likely because of lower MoS 2 content. Studying a commercial MoS 2 /AAO film of a different Al alloy (7075) showed that a heat treatment step intended to fully convert all deposited MoS x species to MoS 2 can adversely affect wear in some alloys. While Al 6061 and 1100 produced films with worse wear performance compared to Al 5052 or 7075, our results show evidence that acid cleaning after initial anodization likely removes residual alloying elements, affecting MoS 2 incorporation. This study demonstrates a nanomaterial modified AAO film with superior wear characteristics to unmodified AAO and relates fabrication procedure, film structure, and practical performance.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Ultra-black coatings for space instruments: a comparison of traditional Ebonol C processes and a method for future repeatability

Ultra-black coatings have served various roles in space instrumentation and hardware. The Ebonol C coating has been used for various missions requiring low reflectivity on aluminum substrates that are electrically conducting. This coating is produced through the formation of a cupric oxide structure on an intermediate layer of copper applied to the aluminum. For many years, this commercial formulation has been used ubiquitously for space instruments. The coating relies upon details of the copper base layer that have been trade secret at various finishing companies, and the availability of the Ebonol C formulated chemistry from the chemical supplier. In recent years, this product has been discontinued at various times, leaving vendors to either rely on expired stock or to formulate their own equivalents. Here, we detail the processing methods, chemistries, and resultant coating structures that produce reflectance performance equivalent to baseline historical reflectance data. This process detail will ensure equivalent performance for such coatings for future missions and link the performance to past and currently deployed instruments.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Electrodeposition and analysis of thick bismuth films

Due to its unique physical and chemical properties, bismuth is an attractive candidate for a wide range of applications such as battery anodes, radiation shielding, and semiconductors, to name a few. This work presents the electrodeposition of mechanically stable and homogenous bismuth films at micron-scale thicknesses. A simple one-step electrodeposition process using either a pulse/reverse or direct current source yielded thick, homogenous, and mechanically stable bismuth films. Morphology, electrochemical behavior, adhesion, and mechanical stability of bismuth coatings plated with varying parameters were characterized via optical profilometry, cyclic voltammetry, electron microscopy, and tribology. Scratch testing on thick electroplated coatings (> 100 µm) revealed similar wear resistance properties between the pulse/reverse plated and direct current electroplated films. This study presents a versatile bismuth electroplating process with the possibility to replace lead in radiation shields with an inexpensive, non-toxic metal, or to make industrially relevant electrocatalytic devices.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Enhancing Surface Finish of Additively Manufactured 316L Stainless Steel with Pulse/Pulse Reverse Electropolishing

To improve the reliable integration of additively manufactured (AM) metal components, there is an urgent need for surface finishing methods capable of processing rough, “as-printed” surfaces. Here, we present a new and scalable electropolishing (EP) technique for use on AM 316L stainless steel (SS) that is capable of achieving a surface roughness equivalent to a machined finish, with arithmetic mean heights (S a ) as low as 1.0 µm. This technique utilizes the sequential application of a new, NaCl/H 2 O pulse/pulse reverse (P/PR) EP step along with a conventional DC (direct current) EP step, where P/PR expands the capability of EP by removing roughness features > 1 µm, which has been previously unattainable with DC EP alone without substantial material removal. This is achieved by independently varying pulse parameters, such as pulse width and height, allowing more control over electrodynamic processes at the part-electrolyte interface. Additionally, P/PR EP resulted in higher smoothing efficiency, where a higher degree of smoothing was achieved with less material removal when compared with conventional DC EP alone. This minimizes unwanted change in geometry from excessive metal dissolution.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Controlled compositional gradients of electroformed gold and silver

Motivated by an interest in high-pressure research, thick (>1 mm) compositionally graded gold/silver (Au/Ag) films were electroformed. Systematic studies were performed to understand the role of processing temperature on the nucleation and growth kinetics and associated microstructure. Furthermore, as the electrolyte composition is continuously changing during the experiment, systematic studies were performed to correlate electrochemical parameters with film morphology and composition. In this work, the results showed that the nucleation pathways and relative deposition rate of Au and Ag are heavily dependent on the processing temperature. A procedure to ramp the temperature while continuously pumping an Au electrolyte into an initial Ag electrolyte to produce the graded film is presented. The obtained film is comprised of a segment of pure Au followed by a complete compositional gradient and ending with a segment of pure Ag across 1.5 mm. The results presented here describe a general framework to fabricate gradients of other materials through electrodeposition.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Mechanical and tribological properties of anodic Al coatings as a function of anodizing conditions

Enhanced wear and corrosion resistance properties are vital for numerous functional and decorative applications. Anodizing is a process frequently used to generate stable oxide coatings on metal surfaces, including aluminium (Al). In this work, we present an evaluation of process variables for optimized anodized coating properties using existing methods and as a baseline for novel coating development. A representative relatively pure Al alloy was chosen as a model system with a goal of finding conditions to achieve high wear coatings with retained ductility. AA5052 alloy coupons were anodized in two different electrolytes (sulfuric and phosphoric acid) to study the effects of anodizing conditions on the mechanical and tribological properties of the anodic coatings. Porosity was evaluated with microscopy, coating hardness was determined via nanoindentation, and tribological properties were characterized using a pin-on-disk tribometer. These measurements were correlated and a loading evaluation was performed to assess the optimum nanoindentation parameters for the use of representative coupons without the need for special processing prior to anodizing. The porosity and coating thickness were found to depend on the anodizing time and the type of electrolyte. Thicker and harder anodic coatings were generated in sulfuric acid compared to phosphoric acid. Porosity studies of the anodic coatings generated in phosphoric acid revealed that coating porosity decreased as the anodizing time increased. Both electrolytes generated anodic coatings with improved tribological properties (friction coefficient and dimensional wear rate), and an optimum processing time was identified for best wear properties.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Modeling atomically mixed graded density impactors

Graded density impactors (GDIs) are multi-material composite impactors used in gas gun experiments to tailor the drive conditions imparted to a sample test material. Previous graded density impactors generally rely on thin, but discrete, layers of different materials. The thinner and the greater number of layers will result in smoother compression. Taken to the limit of very thin layers would be pure material 1 at one surface, such as the front surface of an impactor, smoothly transitioning at the atomic scale to pure material 2 on the back surface. Such an impactor can initially shock, then smoothly compresses a material during a dynamic experiment. This type of experiment can serve to explore a larger region of thermodynamic space than a single or even multi-shock experiments. An overview of how graded density impactors are made is reviewed and sample results are given. Additionally, a strategy for modeling these kinds of impactors is presented. The length scales of constituent mixing are given from the experimental build through electrochemical-deposition. Equation of state models for pure constituents and their subsequent mixtures are presented. It is demonstrated that the time scales for pressure and temperature equilibration, for atomically mixed GDIs, are short enough to be a justifiable closure for the resulting multiphase flow. Furthermore, we present simulation results of dynamic shock followed by a ramp compression, utilizing a silver/gold graded density impactor, onto a tantalum sample.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗