Advanced Vacuum Plasma Spray (VPS) for a Robust, Longlife and Safe Space Shuttle Main Engine (SSME)

In 1984, the Vacuum Plasma Spray Lab was built at NASA/Marshall Space Flight Center for applying durable, protective coatings to turbine blades for the space shuttle main engine (SSME) high pressure fuel turbopump. Existing turbine blades were cracking and breaking off after five hot fire tests while VPS coated turbine blades showed no wear or cracking after 40 hot fire tests. Following that, a major manufacturing problem of copper coatings peeling off the SSME Titanium Main Fuel Valve Housing was corrected with a tenacious VPS copper coating. A patented VPS process utilizing Functional Gradient Material (FGM) application was developed to build ceramic lined metallic cartridges for space furnace experiments, safely containing gallium arsenide at 1260 degrees centigrade. The VPS/FGM process was then translated to build robust, long life, liquid rocket combustion chambers for the space shuttle main engine. A 5K (5,000 Lb. thrust) thruster with the VPS/FGM protective coating experienced 220 hot firing tests in pristine condition with no wear compared to the SSME which showed blanching (surface pulverization) and cooling channel cracks in less than 30 of the same hot firing tests. After 35 of the hot firing tests, the injector face plates disintegrated. The VPS/FGM process was then applied to spraying protective thermal barrier coatings on the face plates which showed 50% cooler operating temperature, with no wear after 50 hot fire tests. Cooling channels were closed out in two weeks, compared to one year for the SSME. Working up the TRL (Technology Readiness Level) to establish the VPS/FGM process as viable technology, a 40K thruster was built and is currently being tested. Proposed is to build a J-2X size liquid rocket engine as the final step in establishing the VPS/FGM process TRL for space flight.

Holmes, Richard R.↗
NASA NTRS2008

Quench Crucibles Reinforced with Metal

Improved crucibles consisting mainly of metal-reinforced ceramic ampules have been developed for use in experiments in which material specimens are heated in the crucibles to various high temperatures, then quenched by, for example, plunging the crucibles into water at room temperature. In a traditional quench crucible, the gap between the ampule and the metal cartridge impedes the transfer of heat to such a degree that the quench rate (the rate of cooling of the specimen) can be too low to produce the desired effect in the specimen. One can increase the quench rate by eliminating the metal cartridge to enable direct quenching of the ampule, but then the thermal shock of direct quenching causes cracking of the ampule. In a quench crucible of the present improved type, there is no gap and no metal cartridge in the traditional sense. Instead, there is an overlay of metal in direct contact with the ampule, as shown on the right side of the figure. Because there is no gap between the metal overlay and the ampule, the heat-transfer rate can be much greater than it is in a traditional quench crucible. The metal overlay also reinforces the ampule against cracking.

Holmes, Richard R.↗
NASA NTRS2006

Enhanced-Contrast Viewing of White-Hot Objects in Furnaces

An apparatus denoted a laser image contrast enhancement system (LICES) increases the contrast with which one can view a target glowing with blackbody radiation (a white-hot object) against a background of blackbody radiation in a furnace at a temperature as high as approximately 1,500 C. The apparatus utilizes a combination of narrowband illumination, along with band-pass filtering and polarization filtering to pass illumination reflected by the target while suppressing blackbody light from both the object and its background.

Witherow, William K.↗
NASA NTRS2004

Progress in Fabrication of Rocket Combustion Chambers by VPS

Several documents in a collection describe aspects of the development of advanced materials and fabrication processes intended to enable the manufacture of advanced rocket combustion chambers and nozzles at relatively low cost. One concept discussed in most of the documents is the fabrication of combustion-chamber liners by vacuum plasma spraying (VPS) of an alloy of 88Cu/8Cr/4Nb (numbers indicate atomic percentages) -- a concept that was reported in "Improved Alloy for Fabrication of Combustion Chambers by VPS" (MFS-26546). Another concept is the deposition of graded-composition wall and liner structures by VPS in order to make liners integral parts of wall structures and to make oxidation- and thermal-protection layers integral parts of liners: The VPS process is started at 100 percent of a first alloy, then the proportion of a second alloy is increased gradually from zero as deposition continues, ending at 100 percent of the second alloy. Yet another concept discussed in one of the documents is the VPS of oxidation-protection coats in the forms of nickel-and-chromium-containing refractory alloys on VPS-deposited 88Cu/8Cr/4Nb liners.

Holmes, Richard R.↗
NASA NTRS2003

Better VPS Fabrication of Crucibles and Furnace Cartridges

An experimental investigation has shown that by (1) vacuum plasma spraying (VPS) of suitable refractory metal alloys on graphite mandrels, and then (2) heat-treating the VPS alloy deposits under suitable conditions, it is possible to fabricate improved crucibles and furnace cartridges that could be used at maximum temperatures between 1,400 and 1,600 C and that could withstand chemical attack by the materials to be heated in the crucibles and cartridges. Taken by itself, the basic concept of fabricating furnace cartridges by VPS of refractory materials onto graphite mandrels is not new; taken by itself, the basic concept of heat treatment of VPS deposits for use as other than furnace cartridges is also not new; however, prior to this investigation, experimental crucibles and furnace cartridges fabricated by VPS had not been heat treated and had been found to be relatively weak and brittle. Accordingly, the investigation was directed toward determining whether certain combinations of (1) refractory alloy compositions, (2) VPS parameters, and (3) heat-treatment parameters could result in VPS-fabricated components with increased ductility.

Holmes, Richard R.↗
NASA NTRS1995

Removable Mandrels For Vacuum-Plasma-Spray Forming

Improved mandrels developed for use in vacuum-plasma-spray (VPS) forming of refractory metal and ceramic furnace cartridge tubes. Designed so after tubes formed on them by VPS, mandrels shrink away from tubes upon cooling back to room temperature and simply slip out of tube.

Krotz, Phillip D.↗
NASA NTRS1993

Vacuum Plasma Spraying Of Copper Onto Titanium

Vacuum plasma spraying successful in depositing tenacious copper coat on flanges and other selected areas of titanium valve housing. Oxidation and concomitant brittleness eliminated.

Power, Chris↗
NASA NTRS1993

Method of fabricating a rocket engine combustion chamber

A process for making a combustion chamber for a rocket engine wherein a copper alloy in particle form is injected into a stream of heated carrier gas in plasma form which is then projected onto the inner surface of a hollow metal jacket having the configuration of a rocket engine combustion chamber is described. The particles are in the plasma stream for a sufficient length of time to heat the particles to a temperature such that the particles will flatten and adhere to previously deposited particles but will not spatter or vaporize. After a layer is formed, cooling channels are cut in the layer, then the channels are filled with a temporary filler and another layer of particles is deposited.

Holmes, Richard R.↗
NASA NTRS1992

Vacuum Plasma Spraying Replaces Electrodeposition

Vacuum plasma spraying used to fabricate large parts with complicated contours and inner structures, without uninspectable welds. Reduces time, and expense of fabrication. Wall of combustion chamber built up inside of outer nickel-alloy jacket by plasma spraying. Particles of metal sprayed partially melted in plasma gun and thrown at supersonic speed toward deposition surface. Vacuum plasma-spray produces stronger bond between the grooves and covering layer completing channels and wall of combustion chamber. In tests, bond withstood pressure of 20 kpsi, three times allowable limit by old method.

Holmes, Richard R.↗
NASA NTRS1991

Salt Filler For Making Covered Channels

In simple fabrication technique, metal salts used to create such subsurface channels as those for coolant in metallic heat exchanger. Layer of metal deposited on structure by vacuum plasma spraying, sealing channels. Metal salt or salt mixture has melting temperature higher than those of waxes and aluminum and withstands high temperature of plasma spraying. After plasma spraying, salt filler dissolved quickly and easily and flushed away with water or other appropriate solvent, leaving behind covered channels.

Mckechnie, Timothy N.↗
NASA NTRS1991

Multipiece Mandrel For Spray-Forming Complex Parts

With help of multipiece mandrel, parts of complicated shapes fabricated by spray forming. Spray-forming process faster and less costly than machining. Consists of etch-resistant end cones and etchable washer between them. Etchable layer applied over mandrel and under spray-formed part helps to ensure easy removal of mandrel. Shape, size, and number of segments in mandrel readily adapted to spray forming of other complicated parts. Process eliminates need for difficult internal and external machining. Segmented mandrel reusable.

Mckechnie, Timothy N.↗
NASA NTRS1989

Vacuum plasma spray coating

Currently, protective plasma spray coatings are applied to space shuttle main engine turbine blades of high-performance nickel alloys by an air plasma spray process. Originally, a ceramic coating of yttria-stabilized zirconia (ZrO2.12Y2O3) was applied for thermal protection, but was removed because of severe spalling. In vacuum plasma spray coating, plasma coatings of nickel-chromium-aluminum-yttrium (NiCrAlY) are applied in a reduced atmosphere of argon/helium. These enhanced coatings showed no spalling after 40 MSFC burner rig thermal shock cycles between 927 C (1700 F) and -253 C (-423 F), while current coatings spalled during 5 to 25 test cycles. Subsequently, a process was developed for applying a durable thermal barrier coating of ZrO2.8Y2O3 to the turbine blades of first-stage high-pressure fuel turbopumps utilizing the enhanced NiCrAlY bond-coating process. NiCrAlY bond coating is applied first, with ZrO2.8Y2O3 added sequentially in increasing amounts until a thermal barrier coating is obtained. The enchanced thermal barrier coating has successfully passed 40 burner rig thermal shock cycles.

Holmes, Richard R.↗