Dispersion-strengthened nickel alloys are sanded on one side and chemically polished. This is followed by a single-step welding process wherein the polished surfaces are forced into intimate contact at 1,400 F for one hour in a vacuum. Diffusion, recrystallization, and grain growth across the original weld interface are obtained during postheating at 2,150 F for two hours in hydrogen.
Solid state welding a butt joint by fusion welding the peripheral surfaces to form a seal is described along with, autogenetically cleaning the faying or mating surfaces of the joint by heating the abutting surfaces to 1,200 C and heating to the diffusion welding temperature in air.
Using magnetic force upset welding to form T-joints between dissimilar thickness parts. This type of resistance welding is used to join compressor and turbine parts thereby reducing the weight and cost of a jet engine.
Surfaces of unrecrystallized alloys are sanded and polished. This is followed by a two-step welding process by which the strength of the parent metal is retained at the weld joint. The first step forces the surfaces into intimate contact at a temperature where the metal still has good ductility. The second step causes diffusion, recrystallization, and grain growth across the original weld interface.
Auto-vacuum cleaning technique was applied to titanium parts prior to welding. This provides oxide-free welding surfaces. Diffusion welding can be accomplished in as little as five minutes of hot pressing. Roll welding can be accomplished with only ten percent deformation.
An improved diffusion welding technique has been developed for TD-NiCr sheet. In the most preferred form, the improved technique consists of diffusion welding 320-grit sanded plus chemically polished surfaces of unrecrystallized TD-NiCr at 760 C under 140 MN/m2 pressure for 1hr followed by postheating at 1180 C for 2hr. Compared to previous work, this improved technique has the advantages of shorter welding time, lower welding temperature, lower welding pressure, and a simpler and more reproducible surface preparation procedure. Weldments were made that had parent-metal creep-rupture shear strength at 1100 C.
Hot press butt welds were made in 0.5 in. diameter bar, and roll lap welds were made in 0.060 in. thick sheet of Ti-6A1-4V. For hot press welds made after auto-vacuum cleaning at 1800 F for 2 hours, weld strength and ductility equaled the parent metal properties. Only 5 minutes of pressing time were needed at 1800 F and 200 psi to make the hot press welds. Roll welds were made in sheet at 1750 F with only 10 percent deformation. The welds in the bar and sheet were metallurgically indistinguishable from the parent material.
At the current state-of-technology there are many joining processes that can be used to make sound welds in TD-NiCr sheet. Some of these that are described in this report are electron beam welding (EBW), gas-tungsten arc welding (GTAW), diffusion welding (DFW), resistance spot welding (RSW), resistance seam welding (RSEW), and brazing. Roll welding (RW) and explosion welding (EXW) have not been developed to the point where they can be used to make sound welds in TD-NiCr. Joining work that has previously been done on TD-NiCr by various organizations, both privately supported and under Air Force and NASA contracts, is described in this summary. Current work is also described that is being done at General Dynamics/Convair (under NASA contract) and at NASA/Lewis to develop and evaluate DFW, RSW, RSEW, and brazing. Preliminary comparisons of joining processes are made for typical applications. A brief description of the manufacture of TD-NiCr sheet by a recently standardized process (under NASA contract) also is given.
Description of a simple and easily applied method of diffusion welding steel plate in air which does not require a vacuum furnace or hot press. The novel feature of the proposed welding method is that diffusion welds are made in air with deadweight loading. In addition, the use of an autogenous (self-generated) surface-cleaning principle (termed 'auto-vac cleaning') to reduce the effects of surface oxides that normally hinder diffusion welding is examined. A series of nine butt joints were diffusion welded in thick sections of AISI 1020 steel plate. Diffusion welds were attempted at three welding temperatures (1200, 1090, and 980 C) using a deadweight pressure of 34,500 N/sq m (5 psi) and a two-hour hold time at temperature. Auto-vac cleaning operations prior to welding were also studied for the same three temperatures. Results indicate that sound welds were produced at the two higher temperatures when the joints were previously fusion seal welded completely around the periphery. Also, auto-vac cleaning at 1200 C for 2-1/2 hours prior to diffusion welding was highly beneficial, particularly when subsequent welding was accomplished at 1090 C.
A method termed 'enhanced diffusion welding' has been developed to produce solid-state welds in TD-NiCr (Ni-20Cr-2ThO2) alloy sheet with weld strengths of 100% of the parent metal strength. Diffusion welded joints were made in specially processed TD-NiCr that equaled the tensile-shear and creep-rupture shear strengths of the parent material at 1090 deg C. The following observations have been made: specially processed TD-NiCr is preferred over commercial TD-NiCr for diffusion welding; the weld line can be eliminated when joining specially processed TD-NiCr by 600-grit sanding and electropolishing the faying surfaces prior to welding; and, a two-step weld cycle is preferred for diffusion welding of this alloy.
At the current state-of-technology there are many joining processes that can be used to make sound welds in TD-NiCr sheet. Some of these that are described in this report are electron beam welding, gas-tungsten arc welding, diffusion welding, resistance spot welding, resistance seam welding, and brazing. The strengths of the welds made by the various processes show considerable variation, especially at elevated temperatures. Most of the fusion welding processes tend to give weak welds at elevated temperatures (with the exception of fusion-type resistance spotwelds). However, solid-state welds have been made with parent metal properties. The process used for a specific application will be dictated by the specific joint requirements. In highly stressed joints at elevated temperatures, one of the solid-state processes, such as DFW, RSW (solid-state or fusion), and RSEW, offer the most promise.
Method is ideal for critical service requirements where parent metal properties are equaled in notch toughness, stress rupture and other characteristics. Welding technique variations may be used on a variety of materials, such as carbon steels, alloy steels, stainless steels, ceramics, and reactive and refractory materials.
Two-step solid state welding cycle applied to carefully prepared surfaces of an unrecrystallized alloy prevents loss of parent-metal strength at weld joint of dispersion-strengthened, nickel-chromium alloy.
Development of technique for diffusion welding of TD-NiCr metal sheets and analysis of mechanical properties
Development of method of diffusion welding steel butt joints in air without vacuum furnace or hot press
Solid state butt and lap joint welding of TD- nickel bar, evaluating performance by stress rupture and shear tests
Stainless steel sheet-to-plate tee joint resistance welded by Magnetic Force Upset Welding process, testing performance
Magnetic force upset welding of dissimilar thickness stainless steel T-joints