DOE OSTI2024

2D Polyhedral Template Matching for Atomic Resolution Microscopy

SAND2024-13879O The 2D Polyhedral Template Matching for Atomic Resolution Microscopy is a suite of functions for analyzing atomic resolution electron microscopy images using the 2D polyhedral template matching (2D-PTM) method. This software analyzes atomic resolution microscopy data from electron microscopic imaging or scanning probe microscopies. The primary application is for identifying different crystal phases, crystal orientations, and defect structures obtained in such atomic resolution images. Written in MATLAB and starting from an atomic resolution image, the code identifies the positions of atomic intensity peaks. It then matches predefined structural templates to the local atomic environments. Outputs include the local structural identification, the template scaling factor and rotation angle, root-mean-squared deviation (RMSD), and centrosymmetry parameter.

Medlin, Douglas↗
DOE OSTI2023

Taming the Pseudoelastic Response of Nitinol Using Ion Implantation

Implantation of Ni 50.5 Ti 49.5 wire with 30 MeV Ni 6+ ions at doses (< 0.1 DPA) typically smaller than employed in the literature is shown to systematically alter the pseudoelastic response, with extrema in Berkovich nanoindentation load (+50%), hysteresis (–60%), and recoverable displacement (–19%) occurring at ~ 3.6 μm below the implantation surface. These extraordinary values are attributed to ~ 10 to 20 nm amorphous clusters that constrain the stress-induced B2-B19' phase transformation. This is substantiated by phase field simulations of crystalline-amorphous composites and molecular dynamics simulations of crystalline-vacancy cluster composites showing the spatial refinement of martensite caused by nm-scale defects. Finally, the results suggest that ion implantation may potentially expand the processing and performance space for NiTi, by creating amorphous defects at smaller length scales than dislocation substructures produced by conventional deformation processing.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Modulating the Pseudoelastic Response of NiTi Using Ion Implantation

Ni-ion irradiated NiTi is nearly 50% harder, retains 85% recoverable deformation, and has reduced hysteresis. This work explores the feasibility of using ion beam modification to modulate the austenite to martensite phase transformation in NiTi, thereby achieving novel or localized properties in near-surface regions.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Modulating the Pseudoelastic Response of NiTi Using Ion Implantation

Ni-ion irradiated NiTi is nearly 50% harder, retains 85% recoverable deformation, and has reduced hysteresis. This work explores the feasibility of using ion beam modification to modulate the austenite to martensite phase transformation in NiTi, thereby achieving novel or localized properties in near-surface regions.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Modulating the Pseudoelastic Response of Nitinol Using Ion Implantation

This work explores whether ion beam modification can be used to modulate the austenite to martensite phase transformation in Nickel-Titanium (NiTi), thereby achieving novel or localized transformation properties in near-surface regions. We report this could provide alternatives to laser shot peening or other surface treatment methods and possibly expand applications in biomedical, aerospace, and other fields. Irradiation induces defects and internal stress that can serve as nucleation and/or pinning sites for the phase transformation. Thus, it can augment more convention- al approaches, including alloying, severe mechanical work, grain size reduction, and precipitation of coherent precipitates. A range of outcomes is possible in principle, including a shift of the critical stress or temperature for onset of the transformation, linearization, reduction of hysteresis, stabilization, and extent of transformation strain.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Effect of hatch spacing and laser power on microstructure, texture, and thermomechanical properties of laser powder bed fusion (L-PBF) additively manufactured NiTi

This study systematically evaluates the effects of laser powder bed fusion additive manufacturing (L-PBF-AM) parameters (hatch spacing and laser power) on the thermomechanical behavior and microstructure of Ni 50.8 Ti 49.2 shape memory alloy. The samples were fabricated with hatch spacings from 40 to 240 µm and laser powers of 50 and 100 W at a constant scanning speed of 125 mm/s, resulting in parts with volumetric energy density levels from 55 to 666 J/mm 3 and two sets of linear energy densities of 0.4 and 0.8 J/mm. The results showed a reduced melt pool size and discontinuity of scan tracks with decreased laser power. Additionally, the porosity level was increased with larger hatch spacing and lower laser power. More notably, the transformation temperatures increased, and the critical stress, recoverable strain, and functional stability of samples improved with lower hatch spacing, where the recovery ratio of up to 90% was observed, regardless of the employed laser power. This study also discussed the relationship between the fabrication process and texture formation in the L-PBF-AM process. In conclusion, the advantage of L-PBF-AM was revealed in tailoring the microstructure from highly textured samples in [1 1 1] or [0 0 1] direction when hatch spacing lower than laser beam focused was employed, to the appearance of equiaxed solidification front with island grains and random orientations.

36 MATERIALS SCIENCE↗