Phase Field Modeling of Corrosion for Design of Next-Generation Magnesium-Aluminum Vehicle Joints
In this study, WPI and its partners sought to understand galvanic corrosion in Mg-Al friction stir weld (FSW) joints. Unlike fusion welds, FSW is done in the solid state. This limits (but does not eliminate) the formation of brittle Al-Mg intermetallics, resulting in better joint strength and corrosion resistance. This study aimed to understand corrosion behavior of Mg-Al FSW joints by using a Cahn-Hilliard phase field electrochemistry model based on the work of Pongsaksawad et al. Its context challenge problem was an ultra-light door designed by Magna with 6061-Al sheet outer and ZEK100-Mg sheet inner panels, joined by an adhesive and FSW. Unlike most FSW joints, which weld through the softer material into the harder one, the Al sheet’s hem joint around Mg required the FSW tool to through the harder Al into the softer Mg, which was itself a challenge. Despite this challenge, PNNL succeeded in consistently making very strong FSW lap joints, by using a triflute tool and power control. Characterization showed mostly separate Al and Mg regions in the weld, usually with a hook protruding from Al into Mg, which likely contributed to high joint strength. Nanohardness mapping showed higher hardness in thin Mg swirls into the Al nugget, likely due to the intermetallics. The study used the industry standard SAE J2334 Cyclic Corrosion Test (CCT) to simulate corrosion conditions over the life of a vehicle, as well as linear polarization testing and ASTM G71 pitting corrosion testing. Corrosion reactions were: H 2 O + ½O 2 + 2e - → 2OH - at the Al cathode, and either Mg → Mg 2+ + 2e - or Mg + 2OH - → Mg(OH) 2 + 2e - at the Mg anode, with electron transfer through the joint. Mass loss increased with Al section length, supporting the hypothesis that galvanic corrosion in Al-Mg joints is limited by the cathodic reaction. Both pitting corrosion (first anode reaction) and hydroxide film formation (second reaction) were observed. The J2334 CCT test method was slightly modified, adding a chromium solution cleaning step after each week of corrosion testing, in order to remove Mg oxides and hydroxides and accurately measure mass loss over time. That said, FSW joints treated in this way did not did not exhibit significant reduction in lap shear strength of the joints vs. newly welded samples which had not undergone corrosion. Corrosion appeared to consist mainly of pitting in Mg in a way which did not directly affect the bond between the materials where the joints failed. A Cahn-Hilliard phase field model coupled with electrical potential described the electronically mediated galvanic corrosion electrochemical reactions described above in the four-component Al-Mg-H 2 O-(H 2 O+½O 2 ) system. This 2-D model successfully predicted Mg(OH)₂ formation at the anode in some circumstances, and Mg pitting corrosion in others, and showed the correct electric field directions in both cases. The model predicted Mg pit corrosion depth within a factor of two of measured pits.
Material flow behavior and microstructural refinement of AA6061 alloy during friction extrusion
In this work we used friction extrusion (FE), a solid phase processing technique, to produce dense, fully consolidated 5?mm rods of aluminum alloy 6061 (AA6061). The combination of large shear stresses and high temperatures at the tool-billet interface during extrusion produced equiaxed, dynamically recrystallized grains and finely distributed precipitates. Texture and microstructure evolution during extrusion was investigated in detail using scanning electron microscopy, electron backscatter diffraction, and transmission electron microscopy. Smoothed particle hydrodynamics simulation was performed to study complex material flow during extrusion. Simulation results suggest spiral material flow during extrusion which corroborated experimental results. Advantages of friction extruded microstructure over conventionally extruded counterparts are also explored using flash annealing for solution treatment followed by artificial aging. Mechanical properties of the as-friction extruded, and the artificially aged specimens were evaluated using tensile testing and compared with conventional extruded material properties.
Manufacture aluminum alloy tube from powder with a single-step extrusion via ShAPE
Mechanical performance of aluminum in terms of strength, wear and corrosion resistance, especially high-temperature strength has been shown to improve with the addition of transition metal (TM) elements of Fe, Cr, and Ti. However, these feedstock materials occur as powders. As such, the traditional fabrication process is complex and expensive because it requires multiple procedures and consumes considerable energy. This study developed Shear Assisted Processing and Extrusion (ShAPE) as a single-step process that manufactures tubes directly from Al-TM powders obtained via gas atomization. Meter-long Al-TM alloy tubes are extruded from powders with different processing conditions. The ShAPE tubes have very low porosity and the average density is 2.94 kg/cm 3 , which is equal to or higher than parts fabricated by hot extrusion and sintering. The powder-to-tube fabrication process was revealed and discussed by examining the microstructural evolution. The Vickers hardness of ShAPE tubes ranges from 110 to 140 HV through wall thickness and at different extrusion speeds. The variation in hardness was correlated with the extent of refinement of intermetallics and attributed to the shear deformation per unit extrusion length. Energy cost analysis shows that ShAPE save ~60% energy compared to the conventional sintering and extrusion processes. Results indicate ShAPE is a low-cost, high-efficiency manufacturing process for producing tubes from metallic powders.
A Combined Experimental and Modeling Approach to Investigate the Performance of Joint Between AZ31 Magnesium and Uncoated DP590 Steel Using Friction Stir-Assisted Scribe Technique
In this study, friction stir assisted scribe technique is used to achieve a viable joint between AZ31 magnesium alloy and uncoated DP590 steel. Here, the mechanical properties and performance of the joint are investigated using finite element modeling and electron microscopy. The joint strength can be ascribed to two factors, the mechanical interlocking and the metallurgical bonding of two materials at their interface. The contribution of both factors is intended, and the metallurgical bonding is studied to understand the basic joining phenomenon.
Determining cohesive parameters for modeling interfacial fracture in dissimilar-metal friction stir welded joints
Not Available
Temperature controlled friction extrusion process
Processing temperature is decisive to the properties and performance of the product in friction extrusion. However, the constantly varying thermal boundary conditions result in an unstable processing temperature even fixed die rotational speed and feed rate were implemented, which extensively disturb the stability of the process and the quality of the product. It is key to maintain the process temperature to ensure the properties of the product is uniform. What's more, a controlled processing temperature enables the properties of the product to be manipulatable between parts and between different locations of one part