Interface stability of ultrasonic additively manufactured Zircaloy-4 during hydrothermal corrosion

Simulated pressurized water reactor conditions (330 °C, 15.6 MPa, ~20 ppb oxygen) without irradiation were used to investigate the hydrothermal corrosion behavior of ultrasonic additively manufactured Zircaloy-4 up to 1000 h. X-ray computed tomography allowed for visualization of defects from processing and their progression after corrosion experiments. The specimens were found to have clear variability in the mass change data, compared to typical wrought Zircaloy-4 specimens. The variation in the mass change after exposure was attributed to weld defects connected to the specimen surface which allowed ingress of oxidant into the samples. Defects visualized by computed tomography were found via metallography and characterized. In conclusion, ultrasonic additively manufactured Zircaloy-4 was found to have comparable corrosion behavior as wrought Zircaloy-4 for specimens which did not have clear surface defects along weld interfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Structure–property relations in graphitic pebbles for nuclear applications

This work presents an analytical approach for holistically characterizing graphitic matrix pebbles for nuclear applications whereby the macrostructure, microstructure, and thermophysical properties of pebbles are determined. A systematic sectioning method was applied to several pebbles to describe the regional properties of the samples. Intact matrix-only spheres and sections of spheres fabricated by Kairos Power were characterized via optical imaging, x-ray computed tomography, x-ray diffraction, and ellipsometry to determine 2D and 3D macrostructure and anisotropy. The thermophysical properties of these materials were determined via measurements of density, specific heat, thermal expansion, and thermal diffusivity. The results of this study indicate that the pebble fabrication methods and their resultant effect on microstructure have a nontrivial effect on thermophysical properties, confirming the importance of robust characterization of these components. A discussion of the characterization approach and its applicability to nuclear fuel development activities is also included.

42 ENGINEERING↗
DOE OSTI2023

Determination of Average Burnup in AGR-3/4 Compacts 1-4 and 7-4

The Advanced Gas Reactor (AGR) Fuel Development and Qualification Program third and fourth irradiation experiments (AGR-3/4), originally planned as separate tests, were combined in one test train for irradiation in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL). The irradiation test began on December 14, 2011, and ended on April 12, 2014 (Collin 2016). The originally planned AGR-3 and AGR-4 irradiation experiments were both focused on obtaining data on fission product transport to support the improvement of modeling. The AGR-3 experimental plan was focused on gaseous and metallic fission product release from the kernels and diffusion in the coatings during irradiation and post-irradiation safety testing. The AGR-4 experimental plan was focused on diffusivities and sorptivities in the compact matrix and reactor graphite. These two goals were combined in the AGR-3/4 irradiation, which consisted of 12 independently monitored capsules that each contained four AGR-3/4 compacts in a single stack surrounded by an inner ring of matrix or graphite and an outer ring of graphite. Two capsule types were used: a standard capsule and a so-called fuel body, in which the outer graphite ring included a floor and cap that fully enclosed the fuel. The fuel body design supported post-irradiation safety testing of the intact fuel and ring assembly to provide data on fission product transport and release from the matrix and graphite at accident temperatures.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

ORNL Analysis of Leach-Burn-Leach Round-Robin Test Samples

An international round-robin test to examine the consistency in leach-burn-leach (LBL) analysis of tristructural-isotropic- (TRISO-) coated particle fuel was conducted by three research organizations from the Generation IV International Forum member countries of the People’s Republic of China, the Republic of Korea, and the United States of America. Two sets of round-robin test samples were exchanged for analysis. One set of samples consisted of a series of nonuranium-bearing, TRISO-coated zirconium dioxide particles seeded with up to four depleted uranium-bearing, TRISO-coated uranium dioxide (UO 2 ) particles, which had intentionally damaged coating layers to simulate either particles with either exposed-kernel defects (i.e., particles with a cracked TRISO coating that should be detected during preburn leaching) or particles with silicon carbide (SiC) defects (i.e., particles with an intact pyrocarbon coating and a hole in the SiC layer that should be detected during postburn leaching). These simulated samples also contained added powder with known quantities of impurities from a coal standard. The other sample set consisted of representative sublots of UO 2 -TRISO particles fabricated in a production-scale coater, except they all contained depleted uranium instead of enriched uranium. In this report, the methodology used at Oak Ridge National Laboratory to conduct LBL analysis of the round-robin samples is presented, and the general results are summarized.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Accelerated fission rate irradiation design, pre-irradiation characterization, and adaptation of conventional PIE methods for U-10Mo and U-17Mo

Metallic U alloys have high U density and thermal conductivity and thus have been explored since the beginning of nuclear power research. Alloys of U with modest amounts of Mo, such as U-10 wt % Mo (U-10Mo), are of particular interest because the γ-U crystal structure in this alloying addition shows prolonged stability in reactor service. Historically, radiation data on U-10Mo fuels were collected in Na fast reactors or lower temperature research reactor conditions, but little is known about irradiation behavior, particularly swelling and creep, at irradiation temperatures between 250 and 500°C. This work discusses the methodology and pre-irradiation characterization results from a U-Mo irradiation campaign performed in the High Flux Isotope Reactor at Oak Ridge National Laboratory. U-10Mo and U-17Mo samples irradiations are being completed at temperatures ranging from 250 to 500°C to three targeted fission densities between 2 × 10 20 and 1.5 × 10 21 fissions per cubic centimeter. Swelling measurement of the specimen sizes studied here required development and assessment of new methods for volume determination before and after irradiation. Laser profilometry and X-ray computation tomography (XCT) were used to provide preirradiation characterization of samples to determine the error and applicability of each to determine swelling following irradiation. These outcomes are contextualized through use of BISON simulations performed to assess the predicted expansion of U-Mo fuels subjected to the irradiation conditions of this work. Use of existing BISON fuel performance models predicted a maximum of 7% swelling under the irradiation conditions of this study. Pre-irradiation characterization revealed the as-cast U-Mo fuel samples were uniformly large-grained fully cubic U crystals with small U-C/N bearing precipitates and pores distributed throughout. Samples were found to contain a bulk porosity between .4 and 3% because of the casting process. Local porosity in areas far from large, interconnected pores was found by Slice-and-View to be under .2%. Nanometer-sized precipitates rich in C and N were identified in all samples, likely because of impurities during the fabrication process. Dendritic bands were also observed throughout the samples. These bands were characterized by variable Mo content that deviated from the overall Mo content by 2–3 wt %. No other microstructural features were correlated to these bands. Mechanical properties were found to be slightly strengthened compared to literature reports of bulk U-Mo fuels due to the nano-scale precipitates throughout the sample.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Texture analysis of AGR program matrix materials

We report the fuel form for high-temperature gas-cooled reactors consists of tristructural isotropic (TRISO) particles embedded in a matrix of graphite flake and carbonized resin. The process of overcoating particles prior to compacting yields a circumferential orientation of the graphite flake surrounding the TRISO particles, which is modified to varied extents when overcoated particles are pressed into the final fuel form. As graphite is highly anisotropic, the texture may impact the properties and performance of the fuel. Ellipsometry was used to measure the texture of the matrix for fueled compacts and unfueled “matrix-only” samples. Results indicated local texture related to the spherical particles in compacts associated with overcoating versus a more linear layered structure in “matrix-only” samples.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗