Linear Viscoelastic Properties of Putative Cyclic Polymers Synthesized by Reversible Radical Recombination Polymerization (R3P)
Linear viscoelastic properties in both melt and solution states are reported for a series of poly(3,6-dioxa-1,8-octanedithiol) (polyDODT) made by reversible radical recombination polymerization (R 3 P) under conditions designed to produce linear (LDODT), cyclic (RDODT) and linear-cyclic mixtures (LRDODT). PolyDODT is amorphous (T g < -50 °C) and highly flexible (entanglement molecular weight M e,lin ≈ 1850 g/mol for LDODT). PolyDODT’s low T g and low M e,lin enable characterization over a wide dynamic range and a wide range of dimensionless weight-average molecular weight Z w = M w /M e,lin . Measurements at temperatures from -57 °C to 100 °C provide up to 18 deades of reduced frequency, which is necessary to characterize RDODT melts with Z w from 23 to 300. The two highest molecular weight polymers in the present RDODT series have such high M w (406k and 556k g/mol) that mass spectrometry, NMR spectroscopy, and even chemical assays for chain ends are unable to rule out up to 2 mol% linear contaminant. By studying the samples in solution (using dilution to reduce Z w ) we could compare their dynamics with those of previously established high-purity polystyrene (PS) rings (limited to Z w ≤ 13.6). RDODT solutions with Z w < 15 (concentrations <5wt% for RDODT-406k and 556k) have dynamic moduli G^* that accord with LCCC-purified PS rings in terms of the frequency dependence (including the absence of a plateau), the progression of shapes of G* as a function of Z w , and the linear scaling of their zero-shear viscosity η0 with M w . The shape of G* as a function of Z w for solutions of RDODT-406k and -556k also accord with lower M w RDODT melts (which have ≤ 1.3mol% linear contaminant). Thus, measurement of the linear viscoelastic properties of appropriate concentrations of high M w (>200k g/mol) putative cyclic polymers, in which linear chains evade spectroscopic detection, may provide an alternative means (though not fully proven) of validation of sample purity. When Z w > 15 (including all seven RDODT melts and eight of their solutions), G* has a rubbery plateau. This suggests that the onset of entanglement-like behavior in rings requires 4-5-fold greater Z w than is required for linear chains. Further, the plateau moduli of RDODT samples are indistinguishable from G N o of the corresponding LDODT (melt or matched-concentration solutions). In entangled linear polymers, the observation that G N o is independent of Z w follows from limitations on lateral fluctuations due to neighboring chains becoming independent of position along a given chain. The present results for RDODT suggest that this holds for sufficiently long endless chains, too. While the RDODT have the same G N o as entangled LDODT, when Z w > 60 the terminal relaxation, if reached at all, of RDODT extends to orders of magnitude lower frequency than an entangled linear polymer of the same Z w . Consequently, the viscosity of RDODT with Z w > 60 increases with Z w much more strongly than the 3.4-power observed for entangled linear polymers. Lastly, these novel polymers, with disulfide-linked backbone and broad relaxation time distribution may prove important in relation to biodegradable elastomers and materials with exceptional low-frequency dissipation, extending at least 12 decades below the onset of the rubbery plateau.