Summary of Alloy 617 and Alloy 709 Elevated Temperature Crack Growth Test Results from the Planned FY24 Crack Growth Test Activities

This report covers the results from crack growth rate testing performed at Idaho National Laboratory in the fiscal year 2024. It includes two creep crack growth rate tests and two creep-fatigue crack growth rate tests. Results are shown for each of these tests, included crack growth measured during the test using direct current potential drop, and measurements based off of the fracture surface. Load line displacement, as well as load, were also collected during the tests. Detailed analysis of the results will continue into the next fiscal year, however, a number of potential improvements to the equipment and testing procedures were identified that will increase testing reliability and throughput, as well as decrease complications with the analysis.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Results of FY 2023 Alloy 617 and Alloy 709 High-Temperature Crack-Growth Testing

This report summarizes the work performed at Idaho National Laboratory under the “Creep, fatigue and creep-fatigue crack growth tests” task of the “Long-Term VHTR Material Qualification – INL” work package. Work was performed this year to validate the crack growth monitoring setup used with the test frames against both continuous crack length monitoring using an optical camera, as well as post-mortem analysis of marker bands on the fracture surface. Delays prevented the use of a gauge to measure load-line displacement for early tests, and so the creep-fatigue crack growth setup was evaluated using the actuator displacement for a load-line displacement setup. While not ideal, this allowed examination of the shortcomings with the current software setup that was originally designed for performing stress corrosion crack growth rate studies. The method for data collection was modified to link the crack growth monitoring software with Instron’s Wave Matrix software. Once the load-line displacement gauge arrived, the crack growth equipment was successfully modified to permit continuous monitoring of both load-line displacement and crack length. This is critical for creep-fatigue and creep crack growth rate studies for ductile material, as it permits the C* and Ct analyses. Test results are shown for Alloy 617 fatigue and creep-fatigue (without the gauge for load-line displacement measurements), as well as creep-fatigue of Alloy 709, which was performed with the completed test setup, allowing for crack length and load-line displacement monitoring.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

In Cell Thermal Creep Frames for Demonstration Project Preparations

The thrust of advanced nuclear reactor demonstrations demands the accelerated qualification of in-core materials to enable licensing processes and developing the performance data. Due to the high-operating temperatures of such reactors, long-term mechanical behavior under constant load is essential to determine the geometrical and mechanical integrity of in-core components during operation and off-normal conditions. Therefore, the thermal creep behavior of neutron-irradiated advanced reactor materials must be determined. The feasibility of using subsize specimens for the irradiation campaigns and the limited available infrastructure challenge the assessment of thermal creep behavior of advanced reactor materials. Therefore, the U.S. Department of Energy Office of Nuclear Energy (DOE-NE) National Reactor Innovation Center (NRIC) prioritizes the development of a thermal creep testing infrastructure for multiple subsize specimens to accelerate the demonstration and deployment of advanced reactor concepts. This report describes the activities for the construction of a thermal creep testing capability at Idaho National Laboratory (INL). The overall project consists of conceptual design, out-of-cell demonstration, and in-cell demonstration phases. During fiscal year (FY)-2021, the team finished the conceptual design of a thermal creep test facility that can test multiple subsize specimens. This conceptual design consisted of the determination of technical and functional requirements, the determination of the design space, and the preparation of the technical drawings. Technical and functional requirements were categorized as required and desired capabilities and the conceptual design was performed to meet all the required capabilities with the flexibility to achieve the desired capabilities. The design space identified the operational capacity of the creep frame for different advanced reactor relevant materials with the consideration of the feasible operation in the hotcell at the Fuels and Applied Science Building (FASB) at INL. Based on the requirements and design space, the multiple specimen creep frame was designed. The official INL engineering drawing process was started and the procurement of materials for construction was initiated. For FY-2022, the out-of-cell demonstration and final installation of the multiple creep frame is planned.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Recent Progress in U-10Mo Mechanical and Thermophysical Property Characterization

Results are presented on the mechanical and thermophysical property characterization of U-10Mo as part of the MP-1 qualification campaign. The thermal diffusivity, specific heat and thermal conductivity of as fabricated U-10Mo fuel foils and plates were measured using the thermal conductivity microscope (TCM), differential scanning calorimeter (DSC) and laser flash analyzer (LFA) all of which located in a shielded glove box – thermal property cell (TPC). A novel inverse method based on finite element analysis was developed to evaluate the thermal diffusivity of composite/layered materials via the LFA technique such as the 5-lyered U-10Mo monolithic fuel mini-plates.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Recent Progress in U-10Mo Mechanical and Thermophysical Property Characterization -- Poster

Results are presented on the mechanical and thermophysical property characterization of U-10Mo as part of the MP-1 qualification campaign. The thermal diffusivity, specific heat and thermal conductivity of as fabricated U-10Mo fuel foils and plates were measured using the thermal conductivity microscope (TCM), differential scanning calorimeter (DSC) and laser flash analyzer (LFA) all of which located in a shielded glove box – thermal property cell (TPC). A novel inverse method based on finite element analysis was developed to evaluate the thermal diffusivity of composite/layered materials via the LFA technique such as the 5-lyered U-10Mo monolithic fuel mini-plates.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

In-Cell Thermal Creep Frame Capability: Out-of-Cell Construction and Subsized Sample Testing

This report describes the activities related to the construction of an in-cell thermal creep test facility for small-scale specimens in the irradiation-assisted stress-corrosion cracking (IASCC) hotcell located at the Fuels and Applied Science Building (FASB) at INL. The whole project includes three stages: (i) conceptual design; (ii) out-of-cell demonstration tests; and (iii) in-cell demonstration testing. During the current fiscal year (FY)-2022, materials and equipment required to construct the conceptual design outlined in a previous report were procured. Frames for conducting out-of-cell testing have been constructed, and testing plans have been developed to assess the operation of the newly constructed frames. Preliminary testing of flat subsized tensile specimens on ASTM creep frames has also been completed for two sample thicknesses: 0.75 mm and 1.0 mm.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Effect of Water Chemistry on Crack Growth Rate in Neutron Irradiated X-750 and XM-19

The Advanced Test Reactor (ATR) National Science User Facility (NSUF) was used to study the effect of neutron damage on crack growth rates (CGR) under simulated boiling water reactor (BWR) water chemistry conditions using a fast neutron spectrum to accelerate the damage process. Nickel based Alloy X-750 and XM-19 were irradiated in the ATR center flux trap (CFT), with this experiment marking the first civilian project to utilize this position within the reactor. 0.4T-CT specimens were used to study crack growth rates for two sample fluences (~1.9 x 1020 n/cm2 and ~9.5 x 1020 n/cm2, E > 1MeV)) in both normal water chemistry (NWC) at 2.5 ppm O2 and hydrogen water chemistry (HWC) at ~80 ppb H2. CGR testing was conducted at a temperature of 288 °C. A decrease in CGR was observed for both alloys with the average ratio (CGR in NWC/CGR in HWC) being a factor of 281 for the XM-19 samples and a factor of 27.8 for the X-750 samples. Observed CGRs in this study showed little difference compared to non-irradiated samples (the non-irradiated XM-19 was 20% cold worked), suggesting limited sensitivity of these susceptible alloys to irradiation effects. Detailed results of CGR response to varying environmental electrochemical potential (ECP) and water purity will be presented in the context of crack growth mitigation in different water chemistries and the change in material behavior relative to non-irradiated samples of the material.

36 MATERIALS SCIENCE↗
DOE OSTI2022

GCR: Alloy 617 Crack Growth Testing Status

Environment can have an appreciable effect on crack growth. This presentation provides updates on environmental crack growth testing of Alloy 617 at INL.