NASA NTRS1976

Development of sputtered techniques for thrust chambers

Procedures for closing out coolant passages in regeneratively cooled thrust chambers by triode sputtering, using post and hollow Cu-0.15 percent Zr cathodes are described. The effects of aluminum composite filler materials, substrate preparation, sputter cleaning, substrate bias current density and system geometry on closeout layer bond strength and structure are evaluated. High strength closeout layers were sputtered over aluminum fillers. The tensile strength and microstructure of continuously sputtered Cu-0.15 percent Zr deposits were determined. These continuous sputtered deposits were as thick as 0.75 cm. Tensile strengths were consistently twice as great as the strength of the material in wrought form.

Mullaly, J. R.↗

NASA NTRS1975

Deposition rate and substrate temperature effects on the structure and properties of bulk-sputtered OFHC Cu and Cu-0.15Zr

Bulk-sputtered OFHC Cu and Cu-0.15 Zr used as inner walls of advanced regeneratively cooled thrust chambers are evaluated as to microstructure, surface topography, and fractography. It is found that under conditions of low substrate temperature, crystallite size and openness of the structure increase with increasing deposition rate for both materials. At elevated temperatures, an equiaxed ductile structure of OFHC Cu is produced only at low deposition rates; at higher deposition rate, open structures are observed with recrystallized equiaxed grains within large poorly bonded crystallites. The Cu-0.15 Zr alloy sputtered from the hollow cathode using a diode discharge shows open-type structures for all conditions evaluated. The use of a triode discharge in generating a dense non-voided structure of Cu-0.15 Zr is discussed.

Hecht, R. J.↗

NASA NTRS1975

Development of sputtered techniques for thrust chambers

Techniques and materials were developed and evaluated for the fabrication and coating of advanced, long life, regeneratively cooled thrust chambers. Materials were analyzed as fillers for sputter application of OFHC copper as a closeout layer to channeled inner structures; of the materials evaluated, aluminum was found to provide the highest bond strength and to be the most desirable for chamber fabrication. The structures and properties were investigated of thick sputtered OFHC copper, 0.15 Zr-Cu, Al2O3,-Cu, and SiC-Cu. Layered structures of OFHC copper and 0.15 Zr-Cu were investigated as means of improving chamber inner wall fatigue life. The evaluation of sputtered Ti-5Al-2.5Sn, NASA IIb-11, aluminum and Al2O3-Al alloys as high strength chamber outer jackets was performed. Techniques for refurbishing degraded thrust chambers with OFHC copper and coating thrust chambers with protective ZrO2 and graded ZrO2-copper thermal barrier coatings were developed.

Mullaly, J. R.↗

NASA NTRS1974

Development of sputtered techniques for thrust chambers, task 1

Filler materials proposed for use in the sputter fabrication regeneratively cooled thrust chambers were evaluated. Low melting castable alloys, CERROBEND. CERROCAST, and CERROTRU, slurry applied SERMETEL 481 and flame-sprayed aluminum were investigated as filler materials. Sputter deposition from a cylindrical cathode inverted magnestron was used to apply an OFHC copper closeout layer to filled OFHC copper ribbed-wall cylindrical substrates. The sputtered closeout layer structure was evaluated with respect to filler material contamination, predeposition machining and finishing operations, and deposition parameters. The application of aluminum by flame-spraying resulted in excessiver filler porosity. Though the outgassing from this porosity was found to be detrimental to the closeout layer structure, bond strengths in excess of 10,500 psi were achieved. Removal of the aluminum from the grooves was readily accomplished by leaching in a 7.0 molar solution of sodium hydroxide at 353 K. Of the other filler materials evaluated, CERROTRU was found to be the most suitable material with respect to completely filling the ribbed-wall cylinders and vacuum system compatibility. However, bond contamination resulted in low closeout layer bond strength with the CERROTRU filler. CERROBEND, CERROCAST, and SERMETEL 481 were found to be unacceptable as filler materials.

Mullaly, J. R.↗