DOE OSTI2022

Deconvoluting sources of failure in lithium metal batteries containing NMC and PEO-based electrolytes

Solid-state lithium metal batteries (SSLMBs) containing polyethylene oxide (PEO)-derived polymer electrolytes and high-voltage (> 4 V vs. Li/Li + ) cathode materials suffer from three sources of failure: (1) instability between the polymer electrolyte and cathode at high voltage, (2) instability of the polymer electrolyte with Li metal, and (3) poorly-designed cathodes. In this study, these three sources of failure are deconvoluted by studying Ni-rich LiNi x Mn y Co 1-x-y O 2 (NMC, x ≥ 0.6) cathodes and a gel polymer electrolyte (GPE) derived from PEO. Initial cycling data reveals that rapid capacity fade occurs regardless of whether soft short circuits form due to Li dendrites. Cyclic voltammetry scans on cells featuring a Li metal electrode, GPE, and a NMC811 electrode free of additives suggest that there are no runaway reactions between the GPE and NMC811 up to 4.5 V vs. Li/Li + . Cathode/cathode symmetric cell cycling demonstrates that Li metal reactivity is a prime source of failure, though a poorly-designed cathode leads to subpar performance. A cathode with single-crystal NMC particles was demonstrated to achieve better initial capacity and longer cycle life, indicating room for improvement in SSLMB cathode design. Therefore, the sources of failure as enumerated may be ranked as follows from most to least concerning: 2 > 3 > 1.

25 ENERGY STORAGE↗

DOE OSTI2021

Role of silicon-graphite homogeneity as promoted by low molecular weight dispersants

This study explores low molecular weight polymers with the same chemical repeat structure as high molecular weight poly acrylic acid (PAA) and lithium poly acrylic acid (LiPAA) binders which act as a dispersant to improve the silicon-graphite electrode performance. The electrodes which utilize LiPAA as a dispersant perform, on average, the best with respect to the maximum capacity (compared to theoretical), rate performance, and capacity retention with time. These electrodes also have the poorest dispersion of binder, indicating that the poor binder dispersion is essential to electrode performance. In contrast, this study shows that electrodes formulated using PAA had good dispersion and performs the worst in cycling. Finally, this work demonstrates that the binder is not uniformly distributed in the electrode, but rather resides in local regions. Overall, the results indicate these regions accommodate volume expansion during cycling.

25 ENERGY STORAGE↗

DOE OSTI2021

Practical Considerations for Testing Polymer Electrolytes for High-Energy Solid-State Batteries

Polymer electrolytes are an important class of materials in enabling solid-state batteries, which have the potential to exceed 400 Wh/kg energy density. Despite significant advancements in their lithium-ion transport and mechanical properties over the last two decades, the integration and testing of these novel electrolyte materials into functioning cells with the electrode loadings and dimensions required to meet the cell-level energy density goals have been limited. Here, through multiple representative examples, we demonstrate the need of testing in close to practical cell conditions for a faster and more reliable evaluation of polymeric electrolytes. In particular, the need for testing with thin lithium anodes and practical cycling capacities is demonstrated for evaluation of their lithium-metal interfacial stability and dendritic resistance, respectively, and a testing protocol is suggested. The guidelines presented here will also apply to testing of other solid electrolytes for solid-state batteries.

25 ENERGY STORAGE↗