The impact of interfacial Si contamination on GaN-on-GaN regrowth for high power vertical devices
The development of gallium nitride (GaN) power devices requires a reliable selective-area doping process, which is difficult to achieve because of ongoing challenges associated with the required etch-then-regrow process. The presence of silicon (Si) impurities of unclear physical origin at the GaN regrowth interface has proven to be a major bottleneck. Furthermore, this paper investigates the origin of Si contamination at the epitaxial GaN-on-GaN interface and demonstrates an approach that markedly reduces its impact on device performance. An optimized dry-etching approach combined with UV-ozone and chemical etching is shown to greatly reduce the Si concentration levels at the regrowth interface, and a significant improvement in a reverse leakage current in vertical GaN-based p–n diodes is achieved.
AlGaN/GaN metal–insulator–semiconductor high electron mobility transistors (MISHEMTs) using plasma deposited BN as gate dielectric
AlGaN/GaN metal–insulator–semiconductor high electron mobility transistors (MISHEMTs) were fabricated on Si substrates with a 10 nm boron nitride (BN) layer as a gate dielectric deposited by electron cyclotron resonance microwave plasma chemical vapor deposition. The material characterization of the BN/GaN interface was investigated by X-ray photoelectric spectroscopy (XPS) and UV photoelectron spectroscopy. The BN bandgap from the B1s XPS energy loss is ~5 eV consistent with sp2 bonding. The MISHEMTs exhibit a low off-state current of 1 × 10 –8 mA/mm, a high on/off current ratio of 10 9 , a threshold voltage of –2.76 V, a maximum transconductance of 32 mS/mm at a gate voltage of –2.1 V and a drain voltage of 1 V, a subthreshold swing of 69.1 mV/dec, and an on-resistance of 12.75 Ω·mm. The interface state density (D it ) is estimated to be less than 8.49 × 10 11 cm –2 eV –1 . Gate leakage current mechanisms were investigated by temperature-dependent current–voltage measurements from 300 K to 500 K. The maximum breakdown electric field is no less than 8.4 MV/cm. Poole–Frenkel emission and Fowler–Nordheim tunneling are indicated as the dominant mechanisms of the gate leakage through the BN gate dielectric at low and high electric fields, respectively.