DOE OSTI2021

Examining CO 2 as an Additive for Solid Electrolyte Interphase Formation on Silicon Anodes

In this study, we demonstrate that the addition of CO 2 to a standard 1.0 M LiPF 6 3:7 wt% ethylene carbonate:ethyl methyl carbonate electrolyte results in the formation of a thinner insoluble solid electrolyte interphase (SEI) that is dominated by the presence of LiF. In contrast, cells without CO 2 result in a thicker insoluble SEI layer containing more organic constituents. The CO 2 is incorporated in the dimethyl carbonate soluble part of the SEI composed primarily of polymeric poly(ethylene oxide) (PEO) on the surface of a thin inorganic layer. This combination of properties from CO 2 addition provides an improved cycling performance through the reduction of irreversible side reactions, leading to higher coulombic efficiency. The results indicate that CO 2 incorporates into the SEI and plays a role similar to additives like fluorinated ethylene carbonate and vinylene carbonate with respect to polymeric components.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Growth and characterization of homoepitaxial β-Ga 2 O 3 layers

ß-Ga 2 O 3 is a next-generation ultra-wide bandgap semiconductor (E g = 4.8 eV to 4.9 eV) that can be homoepitaxially grown on commercial substrates, enabling next-generation power electronic devices among other important applications. Analyzing the quality of deposited homoepitaxial layers used in such devices is challenging, in part due to the large probing depth in traditional x-ray diffraction (XRD) and also due to the surface-sensitive nature of atomic force microscopy (AFM). Here, a combination of evanescent grazing-incidence skew asymmetric XRD and AFM are investigated as an approach to effectively characterize the quality of homoepitaxial ß-Ga 2 O 3 layers grown by molecular beam epitaxy at a variety of Ga/O flux ratios. Accounting for both structure and morphology, optimal films are achieved at a Ga/O ratio of ~1.15, a conclusion that would not be possible to achieve by either XRD or AFM methods alone. Finally, fabricated Schottky barrier diodes with thicker homoepitaxial layers are characterized by J-V and C-V measurements, revealing an unintentional doping density of 4.3×10 16 cm -3 - 2×10 17 cm -3 in the epilayer. These results demonstrate the importance of complementary measurement methods for improving the quality of the ß-Ga 2 O 3 homoepitaxial layers used in power electronic and other devices.

36 MATERIALS SCIENCE↗

DOE OSTI2020

High Current Cycling in a Superconcentrated Ionic Liquid Electrolyte to Promote Uniform Li Morphology and a Uniform LiF-Rich Solid Electrolyte Interphase

High-energy-density systems with fast charging rates and suppressed dendrite growth are critical for the implementation of efficient and safe next-generation advanced battery technologies such as those based on Li metal. However, there are few studies that investigate reliable cycling of Li metal electrodes under high-rate conditions. in this work, by employing a superconcentrated ionic liquid (IL) electrolyte, we highlight the effect of Li salt concentration and applied current density on the resulting Li deposit morphology and solid electrolyte interphase (SEI) characteristics, demonstrating exceptional deposition/dissolution rates and efficiency in these systems. Operation at higher current densities enhanced the cycling efficiency, e.g., from 64 ± 3% at 1 mA cm –2 up to 96 ± 1% at 20 mA cm –2 (overpotential <±0.2 V), while resulting in lower electrode resistance and dendrite-free Li morphology. A maximum current density of 50 mA cm –2 resulted in 88 ± 3% cycling efficiency, displaying tolerance for high overpotentials at the Ni working electrode (0.5 V). X-ray photoelectron microscopy (XPS), time-of-flight secondary-ion mass spectroscopy (ToF-SIMS), and scanning electron microscopy (SEM) surface measurements revealed that the formation of a stable SEI, rich in LiF and deficient in organic carbon species, coupled with nondendritic and compact Li morphologies enabled enhanced cycling efficiency at higher currents. Reduced dendrite formation at high current is further highlighted by the use of a highly porous separator in coin cell cycling (1 mAh cm –2 at 50 °C), sustaining 500 cycles at 10 mA cm –2 .

25 ENERGY STORAGE↗