9 records

DOE OSTI2023

Analyzing photovoltaic module mechanics using composite plate theories and finite element solutions

Deflection and stress calculated from an experimentally validated, high-fidelity finite element model (FEM) of a photovoltaic module experiencing mechanical load was compared to results from a simplified FEM treating the module laminate as a homogenized composite using a rule of mixtures approach, and further compared to analytical calculations treating the module as a Kirchoff-Love flat plate. The goal of this study was to determine the error incurred by analyzing module mechanics with varying levels of simplification, since resolving the aspect ratios of a module is computationally expensive. Homogenized FEMs were found to underpredict peak deflection under a 1.0 kPa load by between 13 and 19% for lower and upper bound application of the rule of mixtures. However, module shape was captured, implying that a useful replication of a resolved model could be achieved with a reduced, calibrated material stiffness. Homogenized stress results captured glass layer tensile stress components to within 46 to 52% at a sample location of interest, though agreement was poor through the remainder of the laminate due to the lack of material resolution. For plate theory, deflection was overpredicted by 45 to 67% for upper and lower bound homogenizations, and frame-adjacent module shapes were not adequately replicated. Stress results mirrored FEM trends but magnitudes were not well correlated to resolved model values. These results support the use of homogenized laminate models for module shape derivation, though resolved models remain necessary for stress analyses. The accuracy of plate theory was found to be inadequate for most applications.

14 SOLAR ENERGY↗

DOE OSTI2022

Instrumented Photovoltaic Modules for Environmental Characterization and Simulation Model Validation

Photovoltaic modules are subjected to various mechanical stressors in their deployment environments, ranging from installation handling to wind and snow loads. Damage incurred during these mechanical events has the potential to initiate subsequent degradation mechanisms, reducing useful module lifespan. Thus, characterizing the mechanical state of photovoltaic modules is pertinent to the development of reliable packaging designs. In this work, photovoltaic modules with strain gauges directly incorporated into the module laminate were fabricated and subjected to mechanical loading to characterize internal strains within the module when under load. These experimental measurements were then compared against results obtained by high-fidelity finite-element simulations. The simulation results showed reasonable agreement in the strain values over time; however, there were large discrepancies in the magnitudes of these strains. Both the instrumentation technique and the finite-element simulations have areas where they can improve. These areas of improvement have been documented. Despite the observed discrepancies between the experimental and simulated results, the module instrumentation proved to be a useful gauge in monitoring and characterizing the mechanical state. With some process improvements, this method could potentially be applied to other environments that a photovoltaic module will encounter in its lifetime that are known to cause damage and degrade performance.

14 SOLAR ENERGY↗

DOE OSTI2021

Towards validation of combined-accelerated stress testing through failure analysis of polyamide-based photovoltaic backsheets

Abstract Novel methods for advancing reliability testing of photovoltaic (PV) modules and materials have recently been developed. Combined-accelerated stress testing (C-AST) is one such method which has demonstrated reliable reproduction of some field-failures which were not reproducible by standard certification tests. To increase confidence and assist in the development of C-AST, and other new testing protocols, it is important to validate that the failure modes observed and mechanisms induced are representative of those observed in the field, and not the product of unrealistic stress conditions. Here we outline a method using appropriate materials characterization and modelling to validate the failure mechanisms induced in C-AST such that we can increase confidence in the test protocol. The method is demonstrated by applying it to a known cracking failure of a specific polyamide (PA)-based backsheet material. We found that the failure of the PA-based backsheet was a result of a combination of stress factors. Photo-oxidation from ultra-violet (UV) radiation exposure caused a reduction in fracture toughness, which ultimately lead to the cracking failure. We show that the chemical and structural changes observed in the backsheet following C-AST aging were also observed in field-aged samples. These results increase confidence that the conditions applied in C-AST are representative of the field and demonstrates our approach to validating the failure mechanisms induced.

14 SOLAR ENERGY↗

DOE OSTI2021

Computational Modeling of Photovoltaic Mini-Modules Undergoing Accelerated Stress Testing

A finite element model of a four-cell photovoltaic mini-module was developed and compared to experimental results from an accelerated stress test protocol in order to validate that computational models can accurately represent their physical counterparts when subjected to mechanical loading and to assess mini-module representativeness against full scale photovoltaic modules. Deflected shapes across the simulated mini-modules were compared to measured mini-module shapes when subjected to various pressure loads. Displaced mini-module shape results constrained to the experimental protocols of 0.4 mm and 1.1 mm of displacement at the mini-module center were compared to experimental results of full-size modules subjected to module qualification test load levels of 1.0 kPa and 2.4 kPa, to assess if the bending of mini-modules was representative of full-sized modules under the load. Temperature cycling was incorporated into the model to simulate the impacts of stress due to thermal expansion of the backsheet and cells. A preliminary uncertainty analysis was performed to show how variations in material properties and geometric parameters change the simulation results.

computational modeling↗

DOE OSTI2021

Towards Validation of Advanced Accelerated Stress Testing Protocols through Failure Analysis and Materials Characterization

As the lifetime of photovoltaic modules increases toward the goal of 50 years, accelerated stress testing is critical to assessing the viability of newer, improved, and often cheaper materials in the field. However, the validation of accelerated testing to reproduce field failure has remained elusive. The recent developments of more advanced stress testing protocols utilizing sequential and combined stressors have provided another opportunity for validation. Using a suite of mechanical, chemical, and structural characterization methods we report the development of our approach using a known bad backsheet “AAA.” We then apply this approach to PVDF-based backsheets to further confirm the generalizability of this approach. The outcome of this work is two-fold: (1) validation of advanced accelerated testing protocols which will enable the prediction of field failures in new materials, and (2) deeper insights into the degradation mechanisms observed through the extensive characterization allowing for improved materials engineering and development.

accelerated aging↗

DOE OSTI2020

Effects of Photovoltaic Module Materials and Design on Module Deformation Under Load

Quasi-static structural finite-element models of an aluminum-framed crystalline silicon photovoltaic module and a glass-glass thin-film module were constructed and validated against experimental measurements of deflection under uniform pressure loading. Specific practices in the computational representation of module assembly were identified as influential to matching experimental deflection observations. Additionally, parametric analyses using Latin hypercube sampling were performed to propagate input uncertainties related to module materials, dimensions, and tolerances into uncertainties in simulated deflection. Sensitivity analyses were performed on the uncertainty quantification datasets using linear correlation coefficients and variance-based sensitivity indices to elucidate key parameters influencing module deformation. Results identified edge tape and adhesive material properties as being strongly correlated to module deflection, suggesting that optimization of these materials could yield module stiffness gains at par with the conventionally structural parameters, such as glass thickness. This exercise verifies the applicability of finite-element models for accurately predicting mechanical behavior of solar modules and demonstrates a workflow for model-based parametric uncertainty quantification and sensitivity analysis. Finally, applications of this capability include the assessment of field environment loads, derivation of representative loading conditions for reduced-scale testing, and module design optimization, among others.

42 ENGINEERING↗

DOE OSTI2020

Correlation of Advanced Accelerated Stress Testing with Polyamide-Based Photovoltaic Backsheet Field-Failures

Cracking of polyamide (PA)-based photovoltaic (PV) backsheet materials has been widely reported for field-aged modules. Failure was not detected by conventional accelerated stress tests (ASTs), which lacked the necessary combination of stress factors and/or factor sequences. PA-based AAA backsheet cracking has since been reproduced through combined and sequential stress testing. Planar- and cross-sectional-optical microscopy as well as Fourier-transform Infrared Spectroscopy (FTIR), have been used to elucidate the mechanical and chemical changes which lead to failure of the backsheet. Field-aged backsheet samples demonstrating failure in various climates (including locations in China and Italy) are also analyzed. Through the analysis, a comparison is made between the different stress testing protocols and the field-aged samples to validate relevance of the advanced stress tests. It is shown that the changes induced through combined-accelerated stress testing (C-AST) were most representative of changes induced by the field, supporting the relevance of C-AST and providing validity for the test protocol.

14 SOLAR ENERGY↗

DOE OSTI2020

Effects of Photovoltaic Module Materials and Design on Module Deformation Under Load

Static structural finite element models of an aluminum-framed crystalline silicon (c-Si) photovoltaic (PV) module and a glass-glass thin film PV module were constructed and validated against experimental measurements of deflection under uniform pressure loading. Parametric analyses using Latin Hypercube Sampling (LHS) were performed to propagate simulation input uncertainties related to module material properties, dimensions, and manufacturing tolerances into expected uncertainties in simulated deflection predictions. This exercise verifies the applicability and validity of finite element modeling for predicting mechanical behavior of solar modules across architectures and enables computational models to be used with greater confidence in assessment of module mechanical stressors and design for reliability. Sensitivity analyses were also performed on the uncertainty quantification data sets using linear correlation coefficients to elucidate the key parameters influencing module deformation. This information has implications on which materials or parameters may be optimized to best increase module stiffness and reliability, whether the key optimization parameters change with module architecture or loading magnitudes, and whether parameters such as frame design and racking must be replicated in reduced-scale reliability studies to adequately capture full module mechanical behavior.

14 SOLAR ENERGY↗

DOE OSTI2020

Understanding PV Polymer Backsheet Degradation through X-Ray Scattering

Understanding how photovoltaic (PV) module backsheet polymers age and degrade in response to environmental stresses is important for designing polymers that can maintain their structural integrity after decades of outdoor use. X-ray scattering is a powerful technique for exploring backsheet polymer structure at the angstrom- (wide-angle, WAXS) and nanometer- (small-angle, SAXS) length-scales. We present the use of SAXS and WAXS to study pristine and aged polymer backsheets. The structural insight from these techniques can be used to compare the degradation induced by accelerated testing with the degradation seen in field-aged PV materials.

14 SOLAR ENERGY↗