DOE OSTI2021

Degradation-resistant TiO 2 @Sn anodes for high-capacity lithium-ion batteries

As the demand for higher-performance batteries has increased, so has the body of research on theoretical high-capacity anode materials. However, the research has been hindered because the high-capacity anode material properties and interactions are not well understood, largely due to the difficulty of observing cycling in situ. Using electrochemical scanning transmission electron microscopy (ec-STEM), we report the real-time observation and electrochemical analysis of pristine tin (Sn) and titanium dioxide-coated Sn (TiO 2 @Sn) electrodes during lithiation/delithiation. As expected, we observed a volume expansion of the pristine Sn electrodes during lithiation, but we further observed that the expansion was followed by Sn detachment from the current collector. Remarkably, although the TiO 2 @Sn electrodes also exhibited similar volume expansion during lithiation, they showed no evidence of Sn detachment. We found that the TiO 2 surface layer acted as an electrochemically activated artificial solid-electrolyte interphase that serves to conduct Li ions. As a physical coating, it mechanically prevented Sn detachment following volume changes during cycling, providing significant degradation resistance and 80% Coulombic efficiency for a complete lithiation/delithiation cycle. Interestingly, upon delithiation, TiO 2 @Sn electrode displayed a self-healing mechanism of small pore formation in the Sn particle followed by agglomeration into several larger pores as delithiation continued.

25 ENERGY STORAGE↗
DOE OSTI2021

Uncovering the Relationship between Aging and Cycling on Lithium Metal Battery Self-Discharge

Lithium metal is considered the “holy grail” material to replace typical Li-ion anodes due to the absence of a host structure coupled with a high theoretical capacity. The absence of a host structure results in large volumetric changes when lithium is electrodeposited/dissolved, making the lithium prone to stranding and parasitic reactions with the electrolyte. Lithium research is focused on enabling highly reversible lithium electrodeposition/dissolution, which is important to achieving long cycle life. Understanding the various mechanisms of self-discharge is also critical for realizing practical lithium metal batteries but is often overlooked. In contrast to previous work, it is shown here that self-discharge via galvanic corrosion is negligible, particularly when lithium is cycled to relevant capacities. Rather, the continued electrochemical cycling of lithium metal results in self-discharge when periodic rest is applied during cycling. The extent of self-discharge can be controlled by increasing the capacity of plated lithium, tuning electrolyte chemistry, incorporating regular rest, or introducing lithiophilic materials. Finally, the Coulombic losses that occur during periodic rest are largely reversible, suggesting that the dominant self-discharge mechanism in this work is not an irreversible chemical process but rather a morphological process.

25 ENERGY STORAGE↗
DOE OSTI2021

Mechanical studies of the solid electrolyte interphase on anodes in lithium and lithium ion batteries

A stable solid electrolyte interphase (SEI) layer is key to high performing lithium ion batteries for metrics such as calendar and cycle life. The SEI must be mechanically robust to withstand large volumetric changes in anode materials such as lithium and silicon, so understanding the mechanical properties and behavior of the SEI is essential for the rational design of artificial SEI and anode form factors. The mechanical properties and mechanical failure of the SEI are challenging to study, because the SEI is thin at only ~ 10 – 200 nm thick and is air sensitive. Furthermore, the SEI changes as a function of electrode material, electrolyte and additives, temperature, potential, and formation protocols. A variety of in situ and ex situ techniques have been used to study the mechanics of the SEI on a variety of lithium ion battery anode candidates; however, there hasn't been a succinct review of the findings thus far. Because of the difficultly of isolating the true SEI and its mechanical properties, there have been a limited number of studies that can fully de-convolute the SEI from the anode it forms on. A review of past research will be helpful for culminating current knowledge and helping to inspire new innovations to better quantify and understand the mechanical behavior of the SEI. This review will summarize the different experimental and theoretical techniques used to study the mechanics of SEI on common lithium ion battery anodes and their strengths and weaknesses.

25 ENERGY STORAGE↗
DOE OSTI2021

Effects of Applied Interfacial Pressure on Li-Metal Cycling Performance and Morphology in 4 M LiFSI in DME

Lithium-metal anodes can theoretically enable 10x higher gravimetric capacity than conventional graphite anodes. However, Li-metal anode cycling has proven difficult due to porous and dendritic morphologies, extensive parasitic solid electrolyte interphase reactions, and formation of dead Li. We systematically investigate the effects of applied interfacial pressure on Li-metal anode cycling performance and morphology in the recently developed and highly efficient 4 M lithium bis(fluorosulfonyl)imide in 1,2-dimethoxyethane electrolyte. We present cycling, morphology, and impedance data at a current density of 0.5 mA/cm 2 and a capacity of 2 mAh/cm 2 at applied interfacial pressures of 0, 0.01, 0.1, 1, and 10 MPa. Cryo-focused ion beam milling and cryo-scanning electron microscopy imaging in cross section reveal that increasing the applied pressure during Li deposition from 0 to 10 MPa leads to greater than a fivefold reduction in thickness (and therefore volume) of the deposited Li. This suggests that pressure during cycling can have a profound impact on the practical volumetric energy density for Li-metal anodes. A “goldilocks zone” of cell performance is observed at intermediate pressures of 0.1–1 MPa. Increasing pressure from 0 to 1 MPa generally improves cell-to-cell reproducibility, cycling stability, and Coulombic efficiency. However, the highest pressure (10 MPa) results in high cell overpotential and evidence of soft short circuits, which likely result from transport limitations associated with increased pressure causing local pore closure in the separator. All cells exhibit at least some signs of cycling instability after 50 cycles when cycled to 2 mAh/cm 2 with thin 50 μm Li counter electrodes, though instability decreases with increasing pressure. In contrast, cells cycled to only 1 mAh/cm 2 perform well for 50 cycles, indicating that capacity plays an important role in cycling stability.

25 ENERGY STORAGE↗
DOE OSTI2021

MnSn 2 and MnSn 2 –TiO 2 nanostructured anode materials for lithium-ion batteries

The high theoretical lithium storage capacity of Sn makes it an enticing anode material for Li-ion batteries (LIBs); however, its large volumetric expansion during Li–Sn alloying must be addressed. Combining Sn with metals that are electrochemically inactive to lithium leads to intermetallics that can alleviate volumetric expansion issues and still enable high capacity. Here, we present the cycling behavior of a nanostructured MnSn 2 intermetallic used in LIBs. Nanostructured MnSn 2 is synthesized by reducing Sn and Mn salts using a hot injection method. The resulting MnSn 2 is characterized by x-ray diffraction and transmission electron microscopy and then is investigated as an anode for LIBs. The MnSn 2 electrode delivers a stable capacity of 514 mAh g -1 after 100 cycles at a C/10 current rate with a Coulombic efficiency >99%. Unlike other Sn-intermetallic anodes, an activation overpotential peak near 0.9 V versus Li is present from the second lithiation and in subsequent cycles. We hypothesize that this effect is likely due to electrolyte reactions with segregated Mn from MnSn 2 . To prevent these undesirable Mn reactions with the electrolyte, a 5 nm TiO 2 protection layer is applied onto the MnSn 2 electrode surface via atomic layer deposition. The TiO 2 -coated MnSn 2 electrodes do not exhibit the activation overpotential peak. The protection layer also increases the capacity to 612 mAh g -1 after 100 cycles at a C/10 current rate with a Coulombic efficiency >99%. This higher capacity is achieved by suppressing the parasitic reaction of Mn with the electrolyte, as is supported by x-ray photoelectron spectroscopy analysis.

77 NANOSCIENCE AND NANOTECHNOLOGY↗
DOE OSTI2021

Edge-Propagation Discharge Mechanism in CFx Batteries—A First-Principles and Experimental Study

Graphite fluoride (CF x ) cathodes coupled with lithium anodes yield one of the highest theoretical specific capacities (>860 mAh/g) among primary batteries. In practice, the observed discharge voltage (~2.5 V) is significantly lower than thermodynamic limits (>4.5 V), the discharge rate is low, and so far Li/CF x has only been used in primary batteries. Understanding the discharge mechanism at atomic length scales will improve practical CFx energy density, rate capability, and rechargeability. So far, purely experimental techniques have not identified the correct discharge mechanism or explained the discharge voltage. In this work, we apply density functional theory calculations to demonstrate that a CF x -edge propagation discharge mechanism based on lithium insertion at the CF/C boundary in partially discharged CF x exhibits a voltage range of 2.5 to 2.9 V—depending on whether solvent molecules are involved. The voltages and solvent dependence agree with our discharge and galvanostatic intermittent titration technique measurements. The predicted discharge kinetics are consistent with CF x operations. Finally, we predict some Li/CF x rechargeability under the application of high potentials, along a charging pathway different from that of discharge. Our work represents a general, quasi-kinetic framework to understand the discharge of conversion cathodes, circumventing the widely used phase diagram approach which most likely does not apply to Li/CF x because equilibrium conditions are not attained in this system.

25 ENERGY STORAGE↗
DOE OSTI2020

Use of a Be-dome holder for texture and strain characterization of Li metal thin films via sin 2 (ψ) methodology

Residual strain in electrodeposited Li films may affect safety and performance in Li metal battery anodes, so it is important to understand how to detect residual strain in electrodeposited Li and the conditions under which it arises. To explore this Li films, electrodeposited onto Cu metal substrates, were prepared under an applied pressure of either 10 or 1000 kPa and subsequently tested for the presence or absence of residual strain via sin 2 (ψ) analysis. X-ray diffraction (XRD) analysis of Li films required preparation and examination within an inert environment; hence, a Be-dome sample holder was employed during XRD characterization. Results show that the Li film grown under 1000 kPa displayed a detectable presence of in-plane compressive strain (–0.066%), whereas the Li film grown under 10 kPa displayed no detectable in-plane strain. Here, the underlying Cu substrate revealed an in-plane residual strain near zero. Texture analysis via pole figure determination was also performed for both Li and Cu and revealed a mild fiber texture for Li metal and a strong bi-axial texture of the Cu substrate. Experimental details concerning sample preparation, alignment, and analysis of the particularly air-sensitive Li films have also been detailed. This work shows that Li metal exhibits residual strain when electrodeposited under compressive stress and that XRD can be used to quantify that strain.

36 MATERIALS SCIENCE↗