DOE OSTI2023

Enhanced Tritium Retention in LiAlO2 Pellets via Engineered Glazes: Tritium Science Project

This project investigated the impact of adding a thin (10 – 50 µm) layer of amorphous glaze to the surface of a TPBAR pellet on its retention of helium, hydrogen (as a surrogate for tritium), and water (as a surrogate for tritiated water). The hypothesis was that the glaze would significantly reduce permeation of hydrogen species with a lesser impact on hindering helium permeation. A non-crystallizing soda-lime-silicate glass, known as SCN-1, was selected for this proof-of-concept study. It was found that continuous glaze layers of the desired thickness could be applied to the pellets with two or more dip coats, depending on the targeted thickness. At 330°C, the glaze was found to have a permeability that was lower than that of the pellet by a factor of ~10 6 , implying that a thin 10 – 50 µm layer can significantly increase pellet retention of hydrogen. Meanwhile, the permeation rate of helium through the glaze was found to be ~20 times higher than that of hydrogen or water. An unanticipated outcome of the study was that unglazed pellets were measured to have hydrogen diffusivities that are a factor of ~105 greater than the diffusivity value used in the TPBAR COMSOL model to achieve observed tritium retention rates. When the higher measured diffusivity was substituted into the model and the model was run with all tritium species in the pellet in the form of T 2 O at a partial pressure of 20 Pa in equilibrium with LiOT, the resulting retention was 50% after 500 days.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Experimental review of the performances of protective coatings for interconnects in solid oxide fuel cells

Ferritic stainless-steel interconnects are used in solid oxide fuel cells; however, coatings are required to improve their performance. Although several types of coatings have been proposed, they have been scarcely investigated under similar conditions. This study compares the characteristics of uncoated Crofer 22 APU and eight different coatings on Crofer 22 APU for up to 3,000 hours at 800°C. The coatings were deposited at various research laboratories around the world, and the experiments were performed at Chalmers University of Technology, Sweden. Cross-sections of the samples were analysed using scanning electron microscopy and energy-dispersive x-ray spectroscopy. The (Co,Mn)-based coated steels showed more than 50-fold lower chromium evaporation and at least 3 times thinner Cr 2 O 3 scale thickness compared to uncoated steel. The coated steel samples showed lower area-specific resistance (ASR) values than the uncoated steel after 3,000 hours of exposure, irrespective of the coating thickness, composition and deposition method.

25 ENERGY STORAGE↗

DOE OSTI2022

Aluminization Coatings and Glass Seals for High Temperature Systems - CRADA 536 (Final Report)

The objective of this project was to demonstrate the suitability of PNNL’s Reactive Air Aluminization (RAA) coatings (US Patent Numbers 10,577,694, 10,378,094, and 9,481,923) for use in high-temperature systems. In particular, PNNL and Utility Global undertook a collaborative effort to explore the applicability of these coatings in Utility Global’s high-temperature hydrogen reactors where they would be used to prepare the sealing surfaces of the reactor technology. Utility Global instructed PNNL regarding their needs relating to further development of glass seal technologies suitable for use in their systems. This effort entailed alkaline earth-based silicate glass development and characterization; evaluation and characterization of reliability and compatibility of the coatings with glass seals, working environments, and substrates; performance demonstrations of representative cells and intermediate cells sealed using the glass seals and/or coatings of interest; and incorporation of the aluminization coatings and glass seals into Utility Global reactors for testing.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Synthesis and Photonic Sintering of Proton Conducting Lanthanide Nickelates

Lanthanide nickelate perovskites are known proton conductors at intermediate temperatures (350-600°C). They are attractive targets for proton conducting fuel cells and electrolyzers due to their operational temperature range and their stability in the presence of CO 2 . These materials have the formula LNiO 3 , with the lanthanide L = La, Ce, Pr, Nd, or Sm. Sintering is challenging due to phase transformations that occur at lower temperatures than those required for sintering. In this project, a series of lanthanide nickelate perovskites was synthesized via both a precursor solid solution method and the glycine nitrate process. Powders derived from the precursor solid solution method for LaNiO 3 and NdNiO 3 were sintered at Utility Global Inc. at various temperatures utilizing fast photonic sintering. LaNiO 3 was successfully sintered while maintaining the perovskite phase. NdNiO 3 underwent a phase transformation at all the conditions tested. The stability of the perovskite phase decreases moving right across the lanthanides in the periodic table, while the expected proton conductivity increases. These results will inform further investigations into lanthanide nickelate perovskites toward the goal of producing a free-standing, sintered, proton-conducting membrane.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Conductivity and Transference Number Determination Protocols for Solid Oxide Cell Materials

To standardize materials and component characterization for next generation hydrogen production and energy generation solid oxide cell (SOC) technologies, test protocols are being established to facilitate comparison across the numerous laboratories and research institutions where SOC development for application in solid oxide fuel cells (SOFCs) and solid oxide electrolyzes cells (SOEC) is conducted. This paper proposes guiding protocols for fundamental electrical properties characterization of SOC materials, including temperature- and oxygen partial pressure (pO 2 )-dependent conductivity measurements, and use of the electromotive force for determining the transference numbers, or contributions of each charge carrier (i.e., ions and electrons), to the total conductivity. The protocol for Archimedes density measurements is also provided as an integral technique to both of these methods.

25 ENERGY STORAGE↗

DOE OSTI2022

Improved Understanding of Zircaloy Hydrogen Pickup Mechanisms in BWRs. NSUF Report (Final Report)

Using an instrumented autoclave operating at 288°C and 1100 psi, electrical impedance spectroscopy (EIS) measurements were taken from three neutron irradiated fuel channel samples (Zircaloy-2 and Zircaloy-4). The three high priority fuel channel samples were tested at 288°C using a simulated PWR water with the AC frequency range extending down through 10 -4 Hz, with corresponding DC measurements to validate the resistance measurements. EIS measurements were also taken at room temperature using a simulated PWR water from four neutron irradiated fuel channel samples (Zircaloy-2 and Zircaloy-4). and four water rod samples (Zircaloy-2). EIS measurements were also performed on unirradiated Zircaloy-2 tubes that were previously oxidized in autoclaves at various temperatures for different time durations to obtain oxide layers of different thicknesses. These experiments proved to be more challenging than anticipated because of the small size of the samples, which required development of fixtures to allow valid testing of the materials, some of which are radioactive, under pressure and temperature. Equivalent circuits were used to model the data. Some samples resulted in Nyquist plots where the arcs were too close to each other resulting in the inability to separate the different oxide morphological thicknesses. Microstructural characterization in the form of optical microscopy, scanning electron microscopy and (scanning) transmission electron microscopy was performed to document the microstructural features of the oxidized Zr-2 and Zr-4 samples (oxide and metal/oxide interface) and to interpret the EIS results. At the start of this work, it was assumed that despite the laminar cracks and porosity visible in both optical and SEM, the oxide scale is dense near the metal, effectively preventing the water from contacting the metal directly. While it is generally accepted that the large laminar cracks pores allow the water to percolate into the oxide film, it is unknown just how deep it can go, and how interconnected is the porosity, which will dictate how much the porosity is connected electrically to the water within the oxide scale. The EIS results demonstrated that there is in fact a distribution of oxide thicknesses over the various samples, and within each material condition, that are communicating to the liquid. This is derived from the fact that Nyquist plots have an arc radius whose center point is often below the Z’ axis, implying that instead of a single oxide thickness, these oxides have a distribution of thicknesses. This distribution of thicknesses produces arcs that are not clearly separable in most of the samples.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗