High Sulfur Loading and Capacity Retention in Bilayer Garnet Sulfurized‐Polyacrylonitrile/Lithium‐Metal Batteries with Gel Polymer Electrolytes
The cubic‐garnet (Li 7 La 3 Zr 2 O 12 , LLZO) lithium–sulfur battery shows great promise in the pursuit of achieving high energy densities. The sulfur used in the cathodes is abundant, inexpensive, and possesses high specific capacity. In addition, LLZO displays excellent chemical stability with Li metal; however, the instabilities in the sulfur cathode/LLZO interface can lead to performance degradation that limits the development of these batteries. Therefore, it is critical to resolve these interfacial challenges to achieve stable cycling. Here, an innovative gel polymer buffer layer to stabilize the sulfur cathode/LLZO interface is created. Employing a thin bilayer LLZO (dense/porous) architecture as a solid electrolyte and significantly high sulfur loading of 5.2 mg cm −2 , stable cycling is achieved with a high initial discharge capacity of 1542 mAh g −1 (discharge current density of 0.87 mA cm −2 ) and an average discharge capacity of 1218 mAh g −1 (discharge current density of 1.74 mA cm −2 ) with 80% capacity retention over 265 cycles, at room temperature (22 °C) and without applied pressure. Achieving such stability with high sulfur loading is a major step in the development of potentially commercial garnet lithium–sulfur batteries.
Oxide‐Based Solid‐State Batteries: A Perspective on Composite Cathode Architecture
Abstract The garnet‐type phase Li 7 La 3 Zr 2 O 12 (LLZO) attracts significant attention as an oxide solid electrolyte to enable safe and robust solid‐state batteries (SSBs) with potentially high energy density. However, while significant progress has been made in demonstrating compatibility with Li metal, integrating LLZO into composite cathodes remains a challenge. The current perspective focuses on the critical issues that need to be addressed to achieve the ultimate goal of an all‐solid‐state LLZO‐based battery that delivers safety, durability, and pack‐level performance characteristics that are unobtainable with state‐of‐the‐art Li‐ion batteries. This perspective complements existing reviews of solid/solid interfaces with more emphasis on understanding numerous homo‐ and heteroionic interfaces in a pure oxide‐based SSB and the various phenomena that accompany the evolution of the chemical, electrochemical, structural, morphological, and mechanical properties of those interfaces during processing and operation. Finally, the insights gained from a comprehensive literature survey of LLZO–cathode interfaces are used to guide efforts for the development of LLZO‐based SSBs.