Mechanical properties and oxidation and corrosion resistance of reduced-chromium 304 stainless steel alloys

An experimental program was undertaken to identify effective substitutes for part of the Cr in 304 stainless steel as a method of conserving the strategic element Cr. Although special emphasis was placed on tensile properties, oxidation and corrosion resistance were also examined. Results indicate that over the temperature range of -196 C to 540 C the yield stress of experimental austenitic alloys with only 12 percent Cr compare favorably with the 18 percent Cr in 304 stainless steel. Oxidation resistance and in most cases corrosion resistance for the experimental alloys were comparable to the commercial alloy. Effective substitutes for Cr included Al, Mo, Si, Ti, and V, while Ni and Mn contents were increased to maintain an austenitic structure.

Stephens, J. R.↗
NASA NTRS1978

Low-chromium stainless steels

Two modified stainless-steel formulations, with only two-thirds chromium content found in conventional type 304, have mechanical and chemical properties comparable to type 304. Low-chromium stainless steels have potential uses in heat exchangers, transfer lines for chemicals, automobile trim, and other applications.

Barrett, C. A.↗
NASA NTRS1975

Several braze filler metals for joining an oxide-dispersion-strengthened nickel-chromium-aluminum alloy

An evaluation was made of five braze filler metals for joining an aluminum-containing oxide dispersion-strengthened (ODS) alloy, TD-NiCrAl. All five braze filler metals evaluated are considered suitable for joining TD-NiCrAl in terms of wettability and flow. Also, the braze alloys appear to be tolerant of slight variations in brazing procedures since joints prepared by three sources using three of the braze filler metals exhibited similar brazing characteristics and essentially equivalent 1100 C stress-rupture properties in a brazed butt-joint configuration. Recommendations are provided for brazing the aluminum-containing ODS alloys.

Gyorgak, C. A.↗
NASA NTRS1972

State-of-technology for joining TD-NiCr sheet.

At the current state-of-technology there are many joining processes that can be used to make sound welds in TD-NiCr sheet. Some of these that are described in this report are electron beam welding (EBW), gas-tungsten arc welding (GTAW), diffusion welding (DFW), resistance spot welding (RSW), resistance seam welding (RSEW), and brazing. Roll welding (RW) and explosion welding (EXW) have not been developed to the point where they can be used to make sound welds in TD-NiCr. Joining work that has previously been done on TD-NiCr by various organizations, both privately supported and under Air Force and NASA contracts, is described in this summary. Current work is also described that is being done at General Dynamics/Convair (under NASA contract) and at NASA/Lewis to develop and evaluate DFW, RSW, RSEW, and brazing. Preliminary comparisons of joining processes are made for typical applications. A brief description of the manufacture of TD-NiCr sheet by a recently standardized process (under NASA contract) also is given.

Holko, K. H.↗
NASA NTRS1972

State-of-technology for joining TD-NiCr sheet

At the current state-of-technology there are many joining processes that can be used to make sound welds in TD-NiCr sheet. Some of these that are described in this report are electron beam welding, gas-tungsten arc welding, diffusion welding, resistance spot welding, resistance seam welding, and brazing. The strengths of the welds made by the various processes show considerable variation, especially at elevated temperatures. Most of the fusion welding processes tend to give weak welds at elevated temperatures (with the exception of fusion-type resistance spotwelds). However, solid-state welds have been made with parent metal properties. The process used for a specific application will be dictated by the specific joint requirements. In highly stressed joints at elevated temperatures, one of the solid-state processes, such as DFW, RSW (solid-state or fusion), and RSEW, offer the most promise.

Holko, K. H.↗
NASA NTRS1971

Protective coating for salt-bath brazing

Ceramic coating, consisting of graphite, enameler's clay, and algin binder, applied to materials prior to salt bath brazing facilitates brazing process and results in superior joints. Alternate coating materials and their various proportions are given.

Francisco, A. C.↗
NASA NTRS1967

Extrusion of small-diameter, thin-wall tungsten tubing

Small-diameter, thin-wall seamless tubing of tungsten has been fabricated in lengths of up to 10 feet by hot extrusion over a floating mandrel. Extrusion of 0.50-inch-diameter tubing over 0.4-inch-diameter mandrels was accomplished at temperatures ranging from 3000 degrees to 4000 degrees F.

Blankenship, C. P.↗
NASA NTRS1965

Apparatus facilitates pressure-testing of metal tubing

Burst-testing of refractory metal tubing is conducted in an apparatus in which tubular specimans are firmly gripped and test pressures and temperatures are applied. Porosity, flaw, and fatigue-stress rupture are also tested.

Gyorgak, C. A.↗
NASA NTRS1964

Guide for extrusion dies eliminates straightening operation

To prevent distortion of extruded metal, a guidance assembly is aligned with the die. As the metal emerges from the extrusion dies, it passes directly into the receiver and straightening tube system, and the completed extrusion is withdrawn.