Time-Evolved Hetero-Alkali Interphases Enable Long-Life Sulfide-Based Anode-Free Solid-State Batteries
Sulfide-based anode-free solid-state batteries (AFSSBs) offer compelling advantages in terms of energy density and safety, yet their practical implementation is severely hindered by undesirable interfacial reactions between sulfide solid electrolytes (SEs) and freshly plated lithium (Li), as well as non-uniform Li plating/stripping behavior. Herein, an effective interfacial stabilization strategy by incorporating sodium bis(fluorosulfonyl)imide (NaFSI) additive into the Li5.4PS4.4Cl1.6 (LPSC) is investigated. Unlike conventional Li-based additives that form static passivation layers, NaFSI introduces a transient hetero-alkali chemistry that kinetically governs interphase evolution during fresh Li plating. NaFSI induces a timesequenced interphase evolution: an initial NaF/LiF-rich layer that suppresses early sulfide reduction, followed by a LiF/Li3N-rich layer that optimizes Li⁺ transport during repeated anode-free cycling. This evolved robust and fast ion conducting layer mitigates interfacial impedance growth, enhances Li + transport kinetics, and suppresses localized Li growth and filamentary shorting. As a result, the anode-free full cell with NaFSI modified LPSC as the interlayer exhibits an excellent cycling stability over 500 cycles at 0.2 C with a capacity retention of 77.6%, whereas the cell with bare LPSC suffers from rapid capacity decay after 100 cycles, retaining only 32.1% of its initial capacity. This work establishes dynamic heteroalkali additive chemistry as a general strategy to kinetically program solid-solid interphases, guiding the interface design in anode-free solid-state batteries.