Testing for hydrogen environment embrittlement - Experimental variables

Hydrogen embrittlement is classified into three types: internal reversible hydrogen embrittlement, hydrogen reaction embrittlement, and hydrogen environment embrittlement. Characteristics of and materials embrittled by these types of hydrogen embrittlement are discussed. Hydrogen environment embrittlement is reviewed in detail. Factors involved in standardizing test methods for detecting the occurrence of and evaluating the severity of hydrogen environment embrittlement are considered. The effects of test technique, hydrogen pressure, gas purity, strain rate, stress concentration factor, and test temperature are discussed.

Gray, H. R.↗
NASA NTRS1972

Effects of hot-salt stress corrosion on titanium alloys.

Susceptibility of titanium alloys to hot-salt stress-corrosion cracking increased as follows: Ti-2Al-11Sn-5Zr-1Mo-0.2Si (679), Ti-6Al-2Sn-4Zr-2Mo (6242), Ti-6Al-4V (64), Ti-6Al-4V-3Co (643), Ti-8Al-1Mo-1V (811), and Ti-13V-11Cr-3Al (13-11-3). The Ti-5Al-6Sn-2Zr-1Mo-0.25Si (5621S) alloy was both the least and most susceptible, depending on heat treatment. Such rankings can be drastically altered by heat-to-heat variations and processing conditions. Residual compressive stresses reduce susceptibility to stress-corrosion. Detection of substantial concentrations of hydrogen in all corroded alloys confirmed the generality of a previously proposed hydrogen embrittlement mechanism.

Gray, H. R.↗
NASA NTRS1972

Hydrogen environment embrittlement.

Hydrogen embrittlement is classified into three types: internal reversible hydrogen embrittlement, hydrogen reaction embrittlement, and hydrogen environment embrittlement. Characteristics of and materials embrittled by these types of hydrogen embrittlement are discussed. Hydrogen environment embrittlement is reviewed in detail. Factors involved in standardizing test methods for detecting the occurrence of and evaluating the severity of hydrogen environment embrittlement are considered. The effects of test technique, hydrogen pressure, purity, strain rate, stress concentration factor, and test temperature are discussed.

Gray, H. R.↗
NASA NTRS1972

Effect of initial hydrogen content of a titanium alloy on susceptibility to hot salt stress corrosion.

The influence of the initial hydrogen content of a titanium alloy on subsequent resistance to hot salt stress corrosion embrittlement and cracking was investigated. A Ti-8Al-1Mo-1V alloy was tested in four conditions: mill annealed (70 ppm H), duplex annealed (70 ppm H), vacuum annealed to an intermediate (36 ppm H) and a low (9 ppm H) hydrogen level. Material annealed at 650 C (duplex condition) exhibited resistance to hot salt stress corrosion superior to that exhibited by material in the mill annealed condition. Reduction of the alloy hydrogen content from 70 to as low as 9 ppm did not influence resistance to hot salt stress corrosion embrittlement or cracking.

Gray, H. R.↗
NASA NTRS1972

Hot-salt stress-corrosion of titanium alloys as related to turbine engine operation.

Demonstration that the major variables influencing hot-salt stress-corrosion of titanium alloys are alloy processing conditions, heat-to-heat variations and composition, surface condition, and cyclic exposures. Under simulated compressor environmental conditions the commonly used 64 alloy is creep limited and not stress-corrosion limited. Cyclic exposures to stress-corrosion conditions are not as detrimental as continuous exposures for equivalent total times.

Gray, H. R.↗
NASA NTRS1972

Ion and laser microprobes applied to the measurement of corrosion produced hydrogen on a microscopic scale.

Use of an ion microprobe and a laser microprobe to measure concentrations of corrosion-produced hydrogen on a microscopic scale. Hydrogen concentrations of several thousand ppm were measured by both analytical techniques below corroded and fracture surfaces of hot salt stress corroded titanium alloy specimens. This extremely high concentration compares with only about 100 ppm hydrogen determined by standard vacuum fusion chemical analyses of bulk samples. Both the ion and laser microprobes were used to measure hydrogen concentration profiles in stepped intervals to substantial depths below the original corroded and fracture surfaces. For the ion microprobe, the area of local analysis was 22 microns in diameter and for the laser microprobe, the area of local analysis was about 300 microns in diameter. The segregation of hydrogen below fracture surfaces supports a previously proposed theory that corrosion-produced hydrogen is responsible for hot salt stress corrosion embrittlement and cracking of titanium alloys. These advanced analytical techniques suggest great potential for many areas of stress corrosion and hydrogen embrittlement research, quality control, and field inspection of corrosion problems. For example, it appears possible that a contour map of hydrogen distribution at notch roots and crack tips could be quantitatively determined. Such information would be useful in substantiating current theories of stress corrosion and hydrogen embrittlement.

Gray, H. R.↗
NASA NTRS1972

Hot-salt stress-corrosion of titanium alloys as related to turbine operation

In an effort to simulate typical compressor operating conditions of current turbine engines, special test facilities were designed. Air velocity, air pressure, air dewpoint, salt deposition temperature, salt concentration, and specimen surface condition were systematically controlled and their influence on hot-salt stress-corrosion evaluated. The influence of both continuous and cyclic stress-temperature exposures was determined. The relative susceptibility of a variety of titanium alloys in commonly used heat-treated conditions was determined. The effects of both environmental and material variables were used to interpret the behavior of titanium alloys under hot-salt stress-corrosion conditions found in jet engines and to appraise their future potential under such conditions.

Gray, H. R.↗
NASA NTRS1972

Hydrogen environment embrittlement

Hydrogen embrittlement is classified into three types: internal reversible hydrogen embrittlement, hydrogen reaction embrittlement, and hydrogen environment embrittlement. Characteristics of and materials embrittled by these types of hydrogen embrittlement are discussed. Hydrogen environment embrittlement is reviewed in detail. Factors involved in standardizing test methods for detecting the occurrence of and evaluating the severity of hydrogen environment embrittlement are considered. The effect of test technique, hydrogen pressure, purity, strain rate, stress concentration factor, and test temperature are discussed. Additional research is required to determine whether hydrogen environment embrittlement and internal reversible hydrogen embrittlement are similar or distinct types of embrittlement.

Gray, H. R.↗
NASA NTRS1971

Ion and laser microprobes applied to the measurement of corrosion-produced hydrogen on a microscopic scale

An ion microprobe and a laser microprobe were used to measure concentrations of corrosion-produced hydrogen on a microscopic scale. Hydrogen concentrations of several thousand ppm were measured by both analytical techniques below the fracture surfaces of hot-salt stress-corroded titanium alloy specimens. This segregation of hydrogen below fracture surfaces supports a previously proposed theory that corrosion-produced hydrogen is responsible for hot-salt stress-corrosion embrittlement and cracking of titanium alloys. These advanced analytical techniques suggest great potential for many areas of stress-corrosion and hydrogen embrittlement research, quality control, and field inspection applications.

Gray, H. R.↗
NASA NTRS1971

Effect of initial hydrogen content of a titanium alloy on susceptibility to hot-salt stress-corrosion

The Ti-8Al-1Mo-1V alloy was tested in four conditions: mill annealed (70 ppM H), duplex annealed (70 ppM H), vacuum annealed to an intermediate (36 ppM) and a low (9 ppM H) hydrogen level. Material annealed at 650 C (duplex condition) exhibited resistance to hot-salt stress corrosion superior to that exhibited by material in the mill-annealed condition. Reduction of the alloy hydrogen content from 70 to as low as 9 ppM did not influence resistance to hot-salt stress corrosion embrittlement or cracking.

Gray, H. R.↗
NASA NTRS1971

Relative susceptibility of titanium alloys to hot-salt stress-corrosion

Susceptibility of titanium alloys to hot-salt stress-corrosion cracking increased as follows: Ti-2Al-11Sn-5Zr-0.2Si(679), Ti-6Al-2Sn-4Zr-2Mo(6242), Ti-6Al-4V(64), Ti-6Al-4V-3Co(643), Ti-8Al-1Mo-1V(811), and Ti-13V-11Cr-3A1(13-11-3). The Ti-5Al-6Sn-2Zr-1Mo-0.25Si(5621S) alloy was both the least and most susceptible depending on heat treatment. Such rankings can be drastically altered by heat-to-heat and processing variations. Residual compressive stresses and cyclic exposures also reduce susceptibility to stress-corrosion. Simulated turbine-engine compressor environmental variables such as air velocity, pressure, dewpoint, salt concentration, and salt deposition temperature have only minor effects. Detection of substantial concentrations of hydrogen in all corroded alloys confirmed the existence of a hydrogen embrittlement mechanism.

Gray, H. R.↗