DOE OSTI2025

Blending Compostable Plastics for Packaging Applications

Non-sustainable packaging materials (polymers) are a large portion of the increasing amount of plastic waste that become environmental pollutants. While many biodegradable or compostable polymers have been developed in recent years, most fail to compete with the non-sustainable polymers dominating the market, due to lack of certain desired properties, such as thermal (high melt temperature) and mechanical (high ductility) performance. For example, the popular compostable polymer polylactic acid (PLLA) has a high melt temperature but is very brittle. Another polymer, poly(d-valerolactone) (PVL) demonstrates great ductility but has a very low melt temperature. By blending PLLA and PVL, there is an opportunity to create a new biodegradable material with synergistic desired properties for packaging applications. In this study, we produce several (9) physical blends of PVL and PLLA with varying compositions of the two polymers while applying three different materials to make them more compatible (compatibilizers). We test the success of compatibilization by scanning electron microscopy (SEM), mechanic testing (strain at break) and differential scanning calorimetry (melting temperature). Overall, we highlight several promising materials with high compatibility and desired thermomechanical properties for sustainable packaging. Ideally, these materials could help mitigate future plastic pollution in Colorado and beyond.

blending↗
DOE OSTI2024

Chain-End Controlled Depolymerization Selectivity in α,α-Disubstituted Propionate PHAs with Dual Closed-Loop Recycling and Record-High Melting Temperature

In this article, within the large poly(3-hydroxyalkanoate) (PHA) family, C3 propionates are much less studied than C4 butyrates, with the exception of α,α-disubstituted propionate PHAs, particularly poly(3-hydroxy-2,2-dimethylpropionate), P3H(Me) 2 P, due to its high melting temperature (T m ~ 230 °C) and crystallinity (~76%). However, inefficient synthetic routes to its monomer 2,2-dimethylpropiolactone [(Me) 2 PL] and extreme brittleness of P3H(Me) 2 P largely hinder its broad applications. Here, we introduce simple, efficient step-growth polycondensation (SGP) of a hydroxyacid or methyl ester to afford P3H(Me) 2 P with low to medium molar mass, which is then utilized to produce lactones through base-catalyzed depolymerization. The ring-opening polymerization (ROP) of the 4-membered lactone leads to high-molar-mass P3H(Me) 2 P, which can be depolymerized by hydrolysis to the hydroxyacid in 99% yield or methanolysis to the hydroxyester in 91% yield, achieving closed-loop recycling via both SGP and ROP routes. Intriguingly, the chain end of the SGP-P3H(Me) 2 P determines the depolymerization selectivity toward 4- or 12-membered lactone formation, while both can be repolymerized back to P3H(Me) 2 P. Through the formation of copolymers P3H(Me/R) 2 P (R = Et, n Pr), PHAs with high tensile strength and ductility, coupled with high barriers to water vapor and oxygen, have been created. Notably, the PHA structure–property study led to P3H( n Pr) 2 P with a record-high T m of 266 °C within the PHA family.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Dual Recycling of Depolymerization Catalyst and Biodegradable Polyester that Markedly Outperforms Polyolefins

Abstract Chemically recyclable, circular polymers continue to attract increasing attention, but rendering both catalysts for depolymerization and high‐performance polymers recyclable is a more sustainable yet challenging goal. Here we introduce a dual catalyst/polymer recycling system in that recyclable inorganic phosphomolybdic acid catalyzes selective depolymerization of high‐ceiling‐temperature biodegradable poly(δ‐valerolactone) in bulk phase, which, upon reaching suitable molecular weight, exhibits outstanding mechanical performance with a high tensile strength of ≈66.6 MPa, fracture strain of ≈904 %, and toughness of ≈308 MJ m −3 , and thus markedly outperforms commodity polyolefins, recovering its monomer in pure state and quantitative yield at only 100 °C. In sharp contrast, the uncatalyzed depolymerization not only requires a high temperature of >310 °C but is also low yielding and non‐selective. Importantly, the recovered monomer can be repolymerized as is to reproduce the same polymer, thereby closing the circular loop, and the recycled catalyst can be reused repeatedly for depolymerization runs without loss of its catalytic activity and efficiency.

Li, Xin‐Lei↗
DOE OSTI2023

Dual Recycling of Depolymerization Catalyst and Biodegradable Polyester that Markedly Outperforms Polyolefins

Chemically recyclable, circular polymers continue to attract increasing attention, but rendering both catalysts for depolymerization and high-performance polymers recyclable is a more sustainable yet challenging goal. Here we introduce a dual catalyst/polymer recycling system in that recyclable inorganic phosphomolybdic acid catalyzes selective depolymerization of high-ceiling-temperature biodegradable poly(δ-valerolactone) in bulk phase, which, upon reaching suitable molecular weight, exhibits outstanding mechanical performance with a high tensile strength of ≈66.6 MPa, fracture strain of ≈904 %, and toughness of ≈308 MJ m –3 , and thus markedly outperforms commodity polyolefins, recovering its monomer in pure state and quantitative yield at only 100 °C. In sharp contrast, the uncatalyzed depolymerization not only requires a high temperature of >310 °C but is also low yielding and non-selective. Importantly, the recovered monomer can be repolymerized as is to reproduce the same polymer, thereby closing the circular loop, and the recycled catalyst can be reused repeatedly for depolymerization runs without loss of its catalytic activity and efficiency.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Chemically circular, mechanically tough, and melt-processable polyhydroxyalkanoates

Polyhydroxyalkanoates (PHAs) have attracted increasing interest as sustainable plastics because of their biorenewability and biodegradability in the ambient environment. However, current semicrystalline PHAs face three long-standing challenges to broad commercial implementation and application: lack of melt processability, mechanical brittleness, and unrealized recyclability, the last of which is essential for achieving a circular plastics economy. Here we report a synthetic PHA platform that addresses the origin of thermal instability by eliminating α-hydrogens in the PHA repeat units and thus precluding facile cis-elimination during thermal degradation. This simple α,α-disubstitution in PHAs enhances the thermal stability so substantially that the PHAs become melt-processable. Synergistically, this structural modification also endows the PHAs with the mechanical toughness, intrinsic crystallinity, and closed-loop chemical recyclability.

Science & Technology - Other Topics↗