Gober, Megan [Univ. of Alabama, Huntsville, AL (United States)] (ORCID:0000000248451850)

DOE OSTI2025

High spatial resolution neutron imaging of lithium-ion batteries: Correlating microstructure and lithium transport

Thick electrodes for lithium-ion batteries can increase the overall energy density, but increasing the electrode thickness introduces charge transport limitations. These limitations may be mitigated through proper electrode structuring. Here, high spatial resolution neutron imaging was used to understand the correlation between microstructure and lithium transport in lithium-ion anodes. Batteries with distinct graphite anode microstructures were produced and studied with high spatial resolution in operando neutron radiography to observe the effects of structure on transport. High spatial resolution neutron computed tomography was performed following in operando neutron radiography. X-ray computed tomography and scanning electron microscopy were used to observe the finer scale anode structure to complement neutron imaging. Solvent-free anodes containing a tightly-packed layered structure confined lithium movement close to the separator. This structure limited capacity, but supported better rate capability. Conversely, a more open pore structure in the wet cast anodes yielded higher capacity with reduced rate capability. Together, these results show that lithium distributions can be controlled by the macroscopic structure of the electrodes, the microstructural pore network, and the microscale active areas that support electrochemical reactions. Furthermore, multimodal imaging applying the complementary strengths of neutron and X-ray methods is shown as a tool for advancing battery design.

25 ENERGY STORAGE↗

DOE OSTI2024

Voltage and temperature effects on low cobalt lithium-ion battery cathode degradation

Degradation of low cobalt lithium-ion cathodes was tested using a full factorial combination of upper cut-off voltage (4.0 V and 4.3 V vs. Li/Li + ) and operating temperature (25 °C and 60 °C). Half-cell batteries were analyzed with electrochemical and microstructural characterization methods. Electrochemical performance was assessed with galvanostatic cycling, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS) supported by distribution of relaxation times (DRT) analysis. Electrode microstructure was characterized with scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray absorption near edge structure (XANES) imaging. Higher cut-off voltage cycling shows presence of NiO x formation, a low diffusivity rock-salt phase, in both CV and XRD data. XRD patterns confirmed that the rock-salt phase was beginning to form at the low cut-off voltage at high temperature, but in much lower intensity than at the high cut-off voltage. Higher temperature accelerates degradation processes at both voltages. Degradation factors at high temperature include NiO x formation, cathode material dissolution, and electrolyte decomposition. SEM analysis suggests that supporting phases may isolate and disconnect active material particles reducing capacity retention and battery life cycle. DRT analysis and XANES imaging show that both high temperature samples revealed a NiO x phase based on an increased diffusive impedance and a visible shift in the XANES spectra. The low cut-off voltage, high temperature sample showed a split peak and shift to lower energies indicating early formation of the NiO x phase. The diffusive impedance, which hinders intercalation and deintercalation, is driven by the formation of the NiO x phase. While primarily driven by cut-off voltage, elevated temperature also contributes to this degradation mechanism.

electrochemical impedance spectroscopy↗