A new diffusion-inhibited oxidation-resistant coating for superalloys
(Previously announced in STAR as N81-33273)
Gedwill, M. A.↗
Engineering topics
Glasgow, T. K.
Publications and source records attributed to Glasgow, T. K..
A new diffusion-inhibited oxidation-resistant coating for superalloys
A concept for enhanced protection of superalloys consists of adding an oxidation- and diffusion-resistant cermet layer between the superalloy and the outer oxidation-resistant metallic alloy coating. Such a duplex coating was compared with a physical-vapor-deposited (PVD) NiCrAlY coating in cyclic oxidation at 1150 C. The substrate alloy was MA 754 - an oxide-dispersion-strengthened superalloy that is difficult to coat. The duplex coating, applied by plasma spraying, outperformed the PVD coating on the basis of weight change and both macroscopic and metallographic observations.
Gedwill, M. A.↗
Oxidation and hot corrosion of coated and bare oxide dispersion strengthened superalloy MA-755E
Cyclic hot corrosion and oxidation of an experimental oxide dispersion strengthened (ODS) superalloy MA-755E were conducted in a hot gas stream at Mach 0.3. The response of the ODS alloy, bare or with protective coatings, was similar to that of a conventional cast alloy, IN-792, in hot corrosion at 900 C. However, during oxidation at 1100 and 1150 C the ODS alloy differed from the cast alloy by developing a greater amount of subsurface porosity. Compared with a diffused aluminide coating, an electron beam vapor deposited NiCrAlY coating offered superior oxidation protection and decreased porosity formation. In additional testing, the tendency to form porosity was associated with the large grains of recrystallized powder metallurgy alloys but was independent of the presence of an oxide dispersion.
Glasgow, T. K.↗
Oxide dispersion strengthened superalloy
MA6000E alloy is strengthened at high temperatures by dispersion of yttrium oxide. Strength properties are about twice those of conventional nickel base alloys. Good thermal fatigue, intermediate temperature strength, and good oxidation resistance give alloy unique combination of benefits. Application in aircraft gas turbine is improved.
Glasgow, T. K.↗
Creep shear behavior of the oxide dispersion strengthened superalloy MA 6000E
The shear rupture life of the oxide dispersion strengthened (ODS) superalloy MA 6000E was determined at 650 and 760 C was 250 MPa. Comparisons were made at 760 C with the conventional cast superalloy B-1900+Hf, the ODS alloy MA 754, and the directionally solidified eutectic alloy gamma/gamma prime-delta was 170 MPa, and for B-1900+Hf was 360 MPa. The ODS alloy MA 6000E and gamma/gamma prime-delta failed with very little indication of ductile accommodation. Both MA 754 and B-1900+Hf showed some ductile tearing. Fracture surfaces of the ODS alloy MA 754 showed discontinuities similar size, shape, and roughness to its grain structure, but the fracture surfaces of MA 6000E were much smoother than its grain boundaries.
Glasgow, T. K.↗
Progress in materials and structures at Lewis Research Center
The development of power and propulsion system technology is discussed. Specific emphasis is placed on the following: high temperature materials; composite materials; advanced design and life prediction; and nondestructive evaluation. Future areas of research are also discussed.
Glasgow, T. K.↗
Effect of milling and leaching on the structure of sintered silicon
The effects of attrition milling and acid leaching on the sintering behavior and the resultant structures of two commercial silicon powders were investigated. Sintering was performed in He for 16 hours at 1200, 1250, and 1300 C. Compacts of as-received Si did not densify during sintering. Milling reduced the average particle size to below 0.5 microns and enhanced densification (1.75 g/cc). Leaching milled Si further enhanced densification (1.90 g/cc max.) and decreased structural coarsening. After sintering, the structure of the milled and leached powder compacts appears favorable for the production of reaction bonded silicon nitride.
Yeh, H. C.↗
Reaction bonded silicon nitride prepared from wet attrition-milled silicon
Silicon powder wet milled in heptane was dried, compacted into test bar shape, helium-sintered, and then reaction bonded in nitrogen-4 volume percent hydrogen. As-nitrided bend strengths averaged approximately 290 MPa at both room temperature and 1400 C. Fracture initiation appeared to be associated with subsurface flaws in high strength specimens and both subsurface and surface flaws in low strength specimens.
Herball, T. P.↗
Reaction bonded silicon nitride prepared from wet attrition-milled silicon
Silicon powder wet milled in heptane was dried, compacted into test bar shape, helium-sintered, and then reaction bonded in nitrogen-4 vol% hydrogen. As-nitrided bend strengths averaged approximately 290 MPa at both room temperature and 1400 C. Fracture initiation appeared to be associated with subsurface flaws in high-strength specimens and both subsurface and surface flaws in low-strength specimens.
Herbell, T. P.↗
Recrystallization characteristics of oxide dispersion strengthened nickel-base alloys
Electron microscopy was employed to study the process of recrystallization in two oxide dispersion strengthened (ODS) mechanically alloyed nickel-base alloys, MA 754 and MA 6000E. MA 754 contained both fine, uniformly dispersed particles and coarser oxides aligned along the working direction. Hot rolled MA 754 had a grain size of 0.5 microns and high dislocation densities. After partial primary recrystallization, the fine grains transformed to large elongated grains via secondary (or abnormal) grain growth. Extruded and rolled MA 6000E contained equiaxed grains of 0.2 micron diameter. Primary recrystallization occurring during working eliminated virtually all dislocations. Conversion from fine to coarse grains was triggered by gamma prime dissolution; this was also a process of secondary or abnormal grain growth. Comparisons were made to conventional and oxide dispersion strengthened nickel-base alloys.
Hotzler, R. K.↗
Formation of porous surface layers in reaction bonded silicon nitride during processing
Microstructural examination of reaction bonded silicon nitride (RBSN) has shown that there is often a region adjacent to the as-nitrided surfaces that is even more porous than the interior of this already quite porous material. Because this layer of large porosity is considered detrimental to both the strength and oxidation resistance of RBSN, a study was undertaken to determine if its formation could be prevented during processing. All test bars studied were made from a single batch of Si powder which was milled for 4 hours in heptane in a vibratory mill using high density alumina cylinders as the grinding media. After air drying the powder, bars were compacted in a single acting die and hydropressed.
Shaw, N. J.↗
Materials and structures technology
Materials and structures performance limitations, particularly for the hot section of the engine in which these limitations limit the life of components, are considered. Failure modes for components such as blades, vanes, and combustors and how they are affected by the environment for such components are discussed. Methods used to improve the materials used for such components are: (1) application of directional structures to turbine components for high strength at high temperatures; (2) improved coatings to increase oxidation and corrosion resistance; (3) increase strength and stiffness with reduced weight by applying higher specific properties of composite materials; and (4) cost effective processing such as near net shape powder methods applied to disks. Life prediction techniques developed to predict component life accurately in advance of service and progress in improving the intermediate and cold section components of turbine engines are covered.
Signorelli, R. A.↗
An oxide dispersion strengthened alloy for gas turbine blades
The strength of the newly developed alloy MA-6000E is derived from a nickel alloy base, an elongated grain structure, naturally occurring precipitates of gamma prime, and an artificial distribution of extremely fine, stable oxide particles. Its composition is Ni-15Cr-2Mo-2Ta-4W-4.5Al-2.5Ti-0.15Zr 0.05C-0.01B-1.1Y2O3. It exhibits the strength of a conventional nickel-base alloy at 1400 F but is quite superior at 2000 F. Its shear strength is relatively low, necessitating consideration of special joining procedures. Its high cycle, low cycle, and thermal fatigue properties are excellent. The relationship between alloy microstructure and properties is discussed.
Glasgow, T. K.↗
Bend strengths of reaction bonded silicon nitride prepared from dry attrition milled silicon powder
Dry attrition milled silicon powder was compacted, sintered in helium, and reaction bonded in nitrogen-4 volume percent hydrogen. Bend strengths of bars with as-nitrided surfaces averaged as high as 210 MPa at room temperature and 220 MPa at 1400 C. Bars prepared from the milled powder were stronger than those prepared from as-received powder at both room temperature and at 1400 C. Room temperature strength decreased with increased milling time and 1400 C strength increased with increased milling time.
Herbell, T. P.↗
An oxide dispersion strengthened alloy for gas turbine blades
The strength of the newly developed alloy MA-6000E is derived from a nickel alloy base, an enlongated grain structure, naturally occurring precipitates of gamma prime, and an artificial distribution of extremely fine, stable oxide particles. Its composition is Ni-15% Cr-2% Mo-2% Ta-4% W-4.5% Al-2.5% Ti-0.15% Zr-0.05% C-0.01% B-1.1% Y2O3. It exhibits strength of a conventional nickel-base alloy at 1400 F, but is quite superior at 2000 F. Its shear strength is relatively low, necessitating consideration of special joining procedures. Its high-cycle, low-cycle, and thermal fatigue properties are excellent. The relationship between alloy micro-structure and properties is discussed.
Glasgow, T. K.↗
Formation of porous surface layers in reaction bonded silicon nitride during processing
An effort was undertaken to determine if the formation of the generally observed layer of large porosity adjacent to the as-nitride surfaces of reaction bonded silicon nitrides could be prevented during processing. Isostatically pressed test bars were prepared from wet vibratory milled Si powder. Sintering and nitriding were each done under three different conditions:(1) bars directly exposed to the furnance atmosphere; (2) bars packed in Si powder; (3) bars packed in Si3N4 powder. Packing the bars in either Si of Si3N4 powder during sintering retarded formation of the layer of large porosity. Only packing the bars in Si prevented formation of the layer during nitridation. The strongest bars (316 MPa) were those sintered in Si and nitrided in Si3N4 despite their having a layer of large surface porosity; failure initiated at very large pores and inclusions. The alpha/beta ratio was found to be directly proportional to the oxygen content; a possible explanation for this relationship is discussed.
Shaw, N. J.↗
Longitudinal shear behavior of several oxide dispersion strengthened alloys
Two commercial oxide dispersion strengthened (ODS) alloys, MA-753 and MA-754, and three experimental ODS alloys, MA-757E, MA-755E, and MA-6000E, were tested in shear at 760 C. Comparisons were made with other turbine blade and vane alloys. All of the ODS alloys exhibited less shear strength than directionally solidified Mar-M 200 = Hf or then conventionally cast B-1900. The strongest ODS alloy tested, MA-755E, was comparable in both shear and tensile strength to the lamellar directionally solidified eutectic alloy gamma/gamma prime - delta. Substantial improvements in shear resistance were found for all alloys tested when the geometry of the specimen was changed from one generating a transverse tensile stress in the shear area to one generating a transverse compressive stress. Finally, 760 C shear strength as a fraction of tensile strength was found to increase linearly with the log of the transverse tensile ductility.
Glasgow, T. K.↗
Surface examination of small particles
Electron-microscopy specimen-preparation technique is used to study micron size particles. Process involves coating particles with vacuum-evaporated carbon, dissolving particles in solvent, then examining residue. Process is applicable to study of catalysts, nucleation and growth of metal oxides, and to determine chemical nature of lubricated surfaces after wear has occurred.
Buzek, B. C.↗