NASA NTRS1985

Toughening reinforced epoxy composites with brominated polymeric additives

Cured polyfunctional epoxy resins including tris (hydroxyphenyl) methane triglycidyl ether are toughened by addition of polybrominated polymeric additives having an EE below 1500 to the pre-cure composition. Carboxy terminated butadiene acrylonitrile rubber is optionally present in the precure mixture as such or as a pre-formed copolymer with other reactants. Reinforced composites, particularly carbon reinforced composites, of these resins are disclosed and shown to have improved toughness.

Nir, Z.↗

NASA NTRS1985

Toughening reinforced epoxy composites with brominated polymeric additives

Cured polyfunctional epoxy resins including tris(hydroxyphenyl)methane triglycidyl ether are toughened by addition of polybrominated polymeric additives having an EE below 1500 to the pre-cure composition. Carboxy-terminated butadiene-acrylonitrile rubber is optionally present in the pre-cure mixture as such or as a pre-formed copolymer with other reactants. Reinforced composites, particularly carbon-reinforced composites, of these resins are disclosed and shown to have improved toughness.

Nir, Z.↗

NASA NTRS1980

A small-scale test for fiber release from carbon composites

A test method was developed to determine relative fiber loss from pyrolyzed composites with different resins and fiber construction. Eleven composites consisting of woven and unwoven carbon fiber reinforcement and different resins were subjected to the burn and impact test device. The composites made with undirectional tape had higher fiber loss than those with woven fabric. Also, the fiber loss was inversely proportional to the char yield of the resin.

Gilwee, W. J., Jr.↗

NASA NTRS1980

Oxygen index tests of thermosetting resins

The flammability characteristics of nine thermosetting resins under evaluation for use in aircraft interiors are described. These resins were evaluated using the Oxygen Index (ASTM 2863) testing procedure. The test specimens consisted of both neat resin and glass reinforced resin. When testing glass-reinforced samples it was observed that Oxygen Index values varied inversely with resin content. Oxygen values were also obtained on specimens exposed to temperatures up to 300 C. All specimens experienced a decline in Oxygen Index when tested at an elevated temperature.

Gilwee, W. J., Jr.↗

NASA NTRS1979

Thermal response of composite panels

The thermochemical and flammability characteristics of laminating resins and composites currently in use and others being considered for use as aircraft interior panels are described. The properties studied included: (1) limiting oxygen index of the composite constituents; (2) fire containment capability of the composite; (3) smoke evolution from the composite; (4) thermogravimetric analysis; (5) composition of the volatile products of thermal degradation; and (6) relative toxicity of the volatile products of pyrolysis. The performance of high-temperature laminating resins such as modified phenolics, polyimides and bismaleimides is compared with the performance of epoxies. The relationship of increased fire safety with the use of polymers with high anaerobic char yield is shown. Processing parameters of the state-of-the-art epoxy resin and the advanced resin composites are detailed.

Kourtides, D. A.↗

NASA NTRS1979

Thermochemical characterization of some thermally stable thermoplastic and thermoset polymers

The thermochemical and flammability properties of some thermally stable polymers considered for use in aircraft interiors are described. The properties studied include: (1) thermomechanical properties such as glass transition and melt temperature; (2) dynamic thermogravimetric analysis in anaerobic environment; (3) flammability properties such as oxygen index, flame spread, and smoke evolution; and (4) selected physical properties. The thermoplastic polymers evaluated include polyphenylene sulfide, polyaryl sulfone, 9,9-bis(4-hydroxyphenyl)-fluorene polycarbonate-poly(dimethylsiloxane) and polyether sulfone. The thermoset polymers evaluated include epoxy, bismaleimide, a modified phenolic, and polyaromatic melamine resin. These resins were primarily used in the fabrication of glass-reinforced prepregs for the construction of experimental panels. Test results and relative rankings of some of the flammability parameters are presented, and the relationship of the molecular structure, char yield, and flammability properties of these polymers are discussed.

Kourtides, D. A.↗

NASA NTRS1979

A small-scale test for fiber release from carbon composites

A burn/impact test apparatus is used to determine the amount of fiber release from carbon fiber composites after burn and impact. The calculation of the theoretical char binder content of the composite is made based on the temperature of the test specimen and the char yield of the resin as determined by thermogravimetric analysis. The test results indicate that carbon fiber release depends on the type of reinforcement used. There was more fiber release with the quasi-isotropic composite made with unidirectional tape than with the woven fabric reinforcement. The amount of fiber release in the impact chamber after burning is coincident with the calculated char binder.

Gilwee, W. J., Jr.↗

NASA NTRS1978

Relative toxicity of the pyrolysis products from some thermoplastic and thermoset polymers

Relative toxicity data on the pyrolysis products of a variety of thermoplastic and thermoset polymers are presented. The data are presented in terms of time to incapacitation and time to death with a fixed sample weight of 1.0 g, and in terms of the apparent lethal concentration required to produce 50 percent mortality within a fixed exposure period of 30 min.

Kourtides, D. A.↗

NASA NTRS1977

Honeycomb-laminate composite structure

A honeycomb-laminate composite structure was comprised of: (1) a cellular core of a polyquinoxaline foam in a honeycomb structure, and (2) a layer of a noncombustible fibrous material impregnated with a polyimide resin laminated on the cellular core. A process for producing the honeycomb-laminate composite structure and articles containing the honeycomb-laminate composite structure is described.

Gilwee, W. J., Jr.↗

NASA NTRS1976

A composite system approach to aircraft cabin fire safety

The thermochemical and flammability characteristics of two polymeric composites currently in use and seven others being considered for use as aircraft interior panels are described. The properties studied included: (1) limiting oxygen index of the composite constituents; (2) fire containment capability of the composite; (3) smoke evolution from the composite; (4) thermogravimetric analysis; (5) composition of the volatile products of thermal degradation; and (6) relative toxicity of the volatile products of pyrolysis. The performance of high-temperature laminating resins such as bismaleimides is compared with the performance of phenolics and epoxies. The relationship of increased fire safety with the use of polymers with high anaerobic char yield is shown. Processing parameters of one of the bismaleimide composites is detailed.

Kourtides, D. A.↗

NASA NTRS1976

Flammability characteristics of aircraft interior composites

The thermochemical and flammability characteristics of two polymeric composites currently in use and seven others being considered for use as aircraft interior panels are described. The properties studied included: (1) oxygen index of the composite constituents; (2) fire containment capability of the composite; (3) smoke evolution from the composite; (4) thermogravimetric analysis; (5) composition of the volatile products of pyrolysis. The performance of foam filled honeycomb laminated panels consisting of high-temperature laminating bismaleimide resins is compared with the performance of empty honeycomb laminated panels consisting of laminating epoxy or phenolic resins at similar densities. Processing parameters of one of the bismaleimide composites is detailed.

Kourtides, D. A.↗

NASA NTRS1976

A composite system approach to aircraft cabin fire safety

The thermochemical and flammability characteristics of two polymeric composites currently in use and seven others being considered for use as aircraft interior panels are described. The properties studied included: (1) limiting oxygen index of the composite constituents; (2) fire containment capability of the composite; (3) smoke evolution from the composite; (4) thermogravimetric analysis; (5) composition of the volatile products of thermal degradation; and (6) relative toxicity of the volatile products of pyrolysis. The performance of high temperature laminating resins such as bismaleimides is compared with the performance of phenolics and epoxies. The relationship of increased fire safety with the use of polymers with high anaerobic char yield is shown. Processing parameters of one of the baremaleimide composites are detailed.

Kourtides, D. A.↗

NASA NTRS1975

Fire dynamics of modern aircraft from a materials point of view

A general approach for selecting polymers to increase fire safety in aircraft is described. It is shown that polymer flammability and thermal protection capability are related to the molecular structure of the polymer and its thermochemical properties. These criteria are used to develop advanced fire-resistant materials which can achieve increased survivability in both post-crash and in-flight fires. The degree of fire hardening of materials depends greatly on the available heat load and fire threat present. It is shown that improvements in fire safety can be achieved by the use of polymers possessing certain basic thermochemical parameters such as high char yield.

Parker, J. A.↗

NASA NTRS1975

Fire dynamics of modern aircraft from a materials point of view

A general approach for selecting polymers to increase fire safety in aircraft is described. It is shown that polymer flammability and thermal protection capability are related to the molecular structure of the polymer and its thermochemical properties. These criteria are used to develop advanced fire-resistant materials that can achieve increased survivability in both post-crash and in-flight fires. The degree of fire hardening of materials depends greatly on the available heat load and fire threat present. It is shown that improvements in fire safety can be achieved by the use of polymers possessing certain basic thermochemical parameters such as high char yield.

Parker, J. A.↗