DOE OSTI2023

Elucidating Structural Transition Dynamics in the Magnesium Cathode MgCr 2 O 4

Multivalent batteries, e.g., those based on magnesium (Mg), are promising candidates for next-generation energy storage due to their high volumetric energy densities and low cost. However, the corresponding ion migration and structural transition mechanisms are often linked and difficult to observe directly. Here, in this paper, we report the direct investigation of atomic transport pathways of cations in spinel magnesium chromate (MgCr 2 O 4 ) by using aberration-corrected scanning transmission electron microscopy (STEM). Cr atoms are directly observed to reversibly occupy the otherwise vacant octahedrally coordinated interstitial sites, passing through tetrahedral sites normally occupied by Mg. Furthermore, imaging and electron energy loss spectroscopy show that electron irradiation induces the formation of Mg and O vacancies, facilitating the migration of Cr and leading to an irreversible phase transition. These results demonstrate the ability of STEM to capture the pathway of deleterious point defects that can result in undesirable phase transitions.

25 ENERGY STORAGE↗

DOE OSTI2022

Controlling dendrite propagation in solid-state batteries with engineered stress

Metal-dendrite penetration is a mode of electrolyte failure that threatens the viability of metal-anode-based solid-state batteries. Whether dendrites are driven by mechanical failure or electrochemical degradation of solid electrolytes remains an open question. If internal mechanical forces drive failure, superimposing a compressive load that counters internal stress may mitigate dendrite penetration. Here, we investigate this hypothesis by dynamically applying mechanical loads to growing dendrites in Li 6.6 La 3 Zr 1.6 Ta 0.4 O 12 solid electrolytes. Operando microscopy reveals marked deflection in the dendrite growth trajectory at the onset of compressive loading. For sufficient loading, this deflection averts cell failure. Using fracture mechanics, we quantify the impact of stack pressure and in-plane stresses on dendrite trajectory, chart the residual stresses required to prevent short-circuit failure, and propose design approaches to achieve such stresses. For the materials studied here, we show that dendrite propagation is dictated by electrolyte fracture, with electronic leakage playing a negligible role.

25 ENERGY STORAGE↗