Extending carbon chemistry at high-pressure by synthesis of CaC 2 and Ca 3 C 7 with deprotonated polyacene- and para-poly(indenoindene)-like nanoribbons

Metal carbides are known to contain small carbon units similar to those found in the molecules of methane, acetylene, and allene. However, for numerous binary systems ab initio calculations predict the formation of unusual metal carbides with exotic polycarbon units, [C 6 ] rings, and graphitic carbon sheets at high pressure (HP). Here we report the synthesis and structural characterization of a HP-CaC 2 polymorph and a Ca 3 C7 compound featuring deprotonated polyacene-like and para-poly(indenoindene)-like nanoribbons, respectively. We also demonstrate that carbides with infinite chains of fused [C6] rings can exist even at conditions of deep planetary interiors (~140 GPa and ~3300 K). Hydrolysis of high-pressure carbides may provide a possible abiotic route to polycyclic aromatic hydrocarbons in Universe.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2024

Stabilization of N6 and N8 anionic units and 2D polynitrogen layers in high-pressure scandium polynitrides

Abstract Nitrogen catenation under high pressure leads to the formation of polynitrogen compounds with potentially unique properties. The exploration of the entire spectrum of poly- and oligo-nitrogen moieties is still in its earliest stages. Here, we report on four novel scandium nitrides, Sc 2 N 6 , Sc 2 N 8 , ScN 5, and Sc 4 N 3 , synthesized by direct reaction between yttrium and nitrogen at 78-125 GPa and 2500 K in laser-heated diamond anvil cells. High-pressure synchrotron single-crystal X-ray diffraction reveals that in the crystal structures of the nitrogen-rich Sc 2 N 6 , Sc 2 N 8, and ScN 5 phases nitrogen is catenated forming previously unknown N 6 6 − and N 8 6 − units and$${\!\,}_{\infty }{\!\,}^{2}({{{{{\rm{N}}}}}}_{5}^{3-})$$ ∞ 2 ( N 5 3 − ) anionic corrugated 2D-polynitrogen layers consisting of fused N 12 rings. Density functional theory calculations, confirming the dynamical stability of the synthesized compounds, show that Sc 2 N 6 and Sc 2 N 8 possess an anion-driven metallicity, while ScN 5 is an indirect semiconductor. Sc 2 N 6 , Sc 2 N 8 , and ScN 5 solids are promising high-energy-density materials with calculated volumetric energy density, detonation velocity, and detonation pressure higher than those of TNT.

Science & Technology - Other Topics↗

DOE OSTI2022

Materials synthesis at terapascal static pressures

Theoretical modelling predicts very unusual structures and properties of materials at extreme pressure and temperature conditions. Hitherto, their synthesis and investigation above 200 gigapascals have been hindered both by the technical complexity of ultrahigh-pressure experiments and by the absence of relevant in situ methods of materials analysis. Here we report on a methodology developed to enable experiments at static compression in the terapascal regime with laser heating. We apply this method to realize pressures of about 600 and 900 gigapascals in a laser-heated double-stage diamond anvil cell, producing a rhenium–nitrogen alloy and achieving the synthesis of rhenium nitride Re 7 N 3 —which, as our theoretical analysis shows, is only stable under extreme compression. Full chemical and structural characterization of the materials, realized using synchrotron single-crystal X-ray diffraction on microcrystals in situ, demonstrates the capabilities of the methodology to extend high-pressure crystallography to the terapascal regime.

36 MATERIALS SCIENCE↗

DOE OSTI2021

The crystal structure of a new calcium aluminate phase containing formate

A new calcium aluminate phase containing formate ions was synthesized and its crystal structure determined. This new phase is indicated as M-phase and was firstly observed in Portland cement pastes hydrated in presence of Ca-formate and in excess of water. The crystal structure of the M-phase was successfully solved in the R-3 space group of the trigonal system on the basis of synchrotron X-ray single crystal diffraction data. The structural model was confirmed by Rietveld refinement of the powder diffraction data acquired on the synthesized pure sample. The crystal structure of the M-phase is similar to that of ettringite, being characterized by columns of AlO{sub 6} octahedra alternating with groups of three edge-sharing CaO{sub 7} polyhedra. The formate ions (HCOO){sup −} share two oxygens with Ca polyhedra and are located in the interspace between the columns. The crystal structure of the M-phase testifies the strong interaction occurring between small organic molecules as formate and the calcium aluminate components of Portland cement.

36 MATERIALS SCIENCE↗