Engineering topics

Gardner, Douglas J.

Publications and source records attributed to Gardner, Douglas J..

8 records

DOE OSTI2024

High-strength 3D printed poly(lactic acid) composites reinforced by shear-aligned polymer-grafted cellulose nanofibrils

This work demonstrates the application of pilot-scale surface functionalization of cellulose nanofibrils (CNFs) by aqueous grafting-through polymerization and subsequent spray drying in 3D printed poly(lactic acid) (PLA) composites. Grafted-CNF composites attain an ultimate tensile strength of 88 ± 3 MPa and a tensile modulus of elasticity of 7.8 ± 1.3 GPa in the printing direction at 20 wt% reinforcement loading. These increases, 42% and 139% over neat PLA, respectively, represent the strongest reported 3D printed CNF/PLA composite to date in the literature. The mechanisms behind these improvements are investigated by comparisons to neat PLA and unmodified spray-dried CNF/PLA controls using melt rheology, dynamic mechanical analysis, and assessment of the reinforcement dispersion. These experiments reveal that improved network formation and shear-induced alignment of the grafted CNFs facilitate the remarkable tensile properties of the printed composites.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2024

Material property characterization of 3D printed polypropylene wood plastic composites

Abstract Wood flour (WF) at 10 wt.% and 20 wt.% loadings was used as a reinforcing filler to enhance the applicability of polypropylene (PP) for 3D printing. After performing printability tests of PP wood plastic composites (WPCs), the mechanical properties of both injection‐molded and 3D‐printed PP WPC specimens were explored. Test specimens were prepared from 3D printed hexagons for analyzing the mechanical properties. Adding WF to neat PP increased the storage modulus and the glass transition temperature while decreasing the degree of crystallinity and the coefficient of thermal expansion, while enhancing the printability of neat PP. The tensile strength, tensile modulus of elasticity, flexural strength, and flexural modulus of elasticity of injection‐molded neat PP improved by up to 21%, 59%, 30%, and 56%, respectively, with 20 wt.% WF. However, the impact strength of injection‐molded neat PP decreased by 85%, with 20 wt.% WF. After 3D printing, the tensile strength and tensile modulus of elasticity of printed neat PP increased by up to 84% and 60%, respectively, with 20 wt.% WF. The flexural strength and flexural modulus of elasticity of neat printed PP remained unchanged compared to those of PP filled with 20 wt.% WF, while the impact strength decreased by 87%. Highlights WF was used as a reinforcement in polypropylene designed for 3D printing A pilot‐scale, pellet‐fed 3D printer was used to print hollow hexagons, and then test specimens were fabricated from these hexagons for mechanical properties The tensile and flexural properties of 3D printed neat polypropylene improved, while the impact strength decreased after adding 20 wt.% WF to the neat PP.

Hwang, Sungjun↗

DOE OSTI2024

Improving the Recyclability of Polymer Composites With Cellulose Nanofibrils

Cellulose nanofibers (CNFs) have been widely studied for their reinforcing potential in high-performance composites. While there are numerous publications on CNF-reinforced composites in a variety of polymer matrices, few have considered the recyclability of such thermoplastic composites and whether the incorporation of CNFs deteriorates or improves their performance upon reprocessing. In this study, two thermoplastic resins, poly(lactic acid) (PLA), and glycol-modified polyethylene terephthalate (PETg), were prepared with CNF reinforcement and thermomechanically recycled to investigate the effect of CNF inclusion on the composite properties after reprocessing as well as their effect on the composites’ number of useful life cycles. Additionally, changes in mechanical, thermal, rheological, molecular, and microstructural properties of the composites and/or base resins were monitored as a function of cycle numbers. As is typical, the polymers’ molecular weight and mechanical performance deteriorated with continued processing. However, the addition of spray dried CNF was found to better maintain the mechanical performance of both polymers throughout multiple recycling steps as compared to neat samples. For example, the tensile strength of PETg with 20 wt% CNF after 6 processing cycles was found to exceed that of virgin neat PETg, and higher loadings of CNF were found to preserve a higher yield strength during multiple rounds of reprocessing compared to PETg composites with lower CNF loadings. Ultimately this study indicates that the addition of CNF to some thermoplastic materials can increase both their sustainability by offsetting the use of high-embodied energy resins and their circularity by enabling performance retention over more use cycles.

42 ENGINEERING↗

DOE OSTI2023

Characterization of CNC Nanoparticles Prepared via Ultrasonic-Assisted Spray Drying and Their Application in Composite Films

The ultrasonic-assisted spray dryer, also known as a nano spray dryer and predominantly used on a lab scale in the pharmaceutical and food industries, enables the production of nanometer-sized particles. In this study, the nano spray dryer was applied to cellulosic materials, such as cellulose nanofibrils (CNFs) and cellulose nanocrystals (CNCs). CNC suspensions were successfully dried, while the CNF suspensions could not be dried, attributable to their longer fibril lengths. The nano spray drying process was performed under different drying conditions, including nebulizer hole sizes, solid concentrations, and gas flow rates. It was confirmed that the individual particle size of nano spray-dried CNCs (nano SDCNCs) decreased as the nebulizer hole sizes and solid contents of the suspensions decreased. The production rate of the nano spray dryer increased with higher solid contents and lower gas flow rates. The resulting nano SDCNCs were added to a polyvinyl alcohol (PVA) matrix as a reinforcing material to evaluate their reinforcement behavior in a plastic matrix using solvent casting. After incorporating the 20 wt.% nano SDCNCs into the PVA matrix, the tensile strength and tensile modulus elasticity of the neat PVA nanocomposite film increased by 22% and 32%, respectively, while preserving the transparency of the films.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Spray Drying Enzyme-Treated Cellulose Nanofibrils

Enzyme-treated cellulose nanofibrils (CNFs) were produced via a lab-scale mass colloider using bleached kraft pulp (BKP) to evaluate their processability and power requirements during refining and spray-drying operations. To evaluate the energy efficiency in the CNF refining process, the net energy consumption, degree of polymerization (DP), and viscosity were determined. Less energy was consumed to attain a given fines level by using the endoglucanase enzymes. The DP and viscosity were also decreased using the enzymes. The morphological properties of the enzyme-pretreated spray-dried CNF powders (SDCNFs) were measured. Subsequently, the enzyme-pretreated SDCNFs were added to a PP matrix with MAPP as a coupling agent. The mixture was then compounded through a co-rotating twin-screw extruder to determine whether the enzyme treatment of the CNFs affects the mechanical properties of the composites. Compared to earlier studies on enhancing PMCs with SDCNF powders, this research investigates the use of enzyme-pretreated SDCNF powders. It was confirmed that the strength properties of PP increased by adding SDCNFs, and the strength properties were maintained after adding enzyme-pretreated SDCNFs.

59 BASIC BIOLOGICAL SCIENCES↗

DOE OSTI2023

Bioinspired design toward nanocellulose-based materials

Nature provides lots of inspiration for material and structural design for various applications. Deriving design principles from the investigation of nature can provide a rich source of inspiration for the development of multifunctional materials. The bioinspired design templates mainly include mussels, nacre, and various plant species. As a sustainable and renewable feedstock, nanocellulose can be used to fabricate advanced materials with multifunctional properties through bioinspired designs. However, challenges and opportunities remain for realizing the full potential in the design of novel materials. Here, this article reviewed recent development in the bioinspired nanocellulose based materials and their application. This article summarizes the functions (e.g., surface wetting) and applications (e.g., composite) of bioinspired nanocellulose-based materials. The bioinspired design templates are discussed along with strategies, advantages, and challenges to the development of synthetic mimics. Additionally, mechanisms and processes (e.g., chemical modification, self-assembly) leading to biomimetic design are discussed. Finally, future research directions and opportunities of bioinspired nanocellulose-based materials are highlighted.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Polymer-Grafted Cellulose Nanofibrils with Enhanced Interfacial Compatibility for Stronger Poly(lactic acid) Composites

Cellulose nanofibrils (CNFs) are a promising reinforcement for biodegradable composite matrices such as poly(lactic acid) (PLA), but they require commercially scalable drying methods that preserve their fibrillar morphology along with improved interfacial interactions with polymer matrices. In this work, a water-based grafting-through polymerization scheme to modify CNFs improved spray drying behavior and reinforcement capacity in PLA composites. All polymer modifications yielded CNFs with a more fibrillar morphology after spray drying, increasing specific surface area by up to 490% compared to unmodified CNFs, values similar to conventional freeze drying. Polymer-grafted CNFs in PLA composites improved the tensile strength by 16% at 20 wt % loading and stiffness by 22% at a 10 wt % loading with two different graft-polymer chemistries compared to unmodified CNF composites. Surface energy heterogeneity measurements of the reinforcements and PLA matrix were employed to understand the improvements in composite properties. Polymer modifications lowered the total surface energy of the CNFs, and calculated ratios of work of adhesion to work of cohesion suggested improved interfacial compatibility for four of the modified CNFs with PLA. Rheological oscillatory shear studies of the composites correlated solid-like melt behavior, as demonstrated by storage moduli dominance, with higher tensile strength. Thermal analysis of the composites revealed that excessive plasticization by the poly(oligoethylene glycol methyl ether methacrylate)-grafted sample potentially offset mechanical property improvements imparted by the more fibrillar morphology. This work provides an opportunity for large-scale manufacturing of CNF/PLA composites via an entirely aqueous modification scheme and industrially relevant spray drying process.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Review on Hybrid Reinforced Polymer Matrix Composites with Nanocellulose, Nanomaterials, and Other Fibers

The use of composite materials has seen many new innovations for a large variety of applications. The area of reinforcement in composites is also rapidly evolving with many new discoveries, including the use of hybrid fibers, sustainable materials, and nanocellulose. In this review, studies on hybrid fiber reinforcement, the use of nanocellulose, the use of nanocellulose in hybrid forms, the use of nanocellulose with other nanomaterials, the applications of these materials, and finally, the challenges and opportunities (including safety issues) of their use are thoroughly discussed. This review will point out new prospects for the composite materials world, enabling the use of nano- and micron-sized materials together and creating value-added products at the industrial scale. Furthermore, the use of hybrid structures consisting of two different nano-materials creates many novel solutions for applications in electronics and sensors.

36 MATERIALS SCIENCE↗