Oxygen Distribution and Segregation at Grain Boundaries in Nb and Ta-Encapsulated Nb Thin Films for Superconducting Qubits

We report on atomic-scale analyses of oxygen distribution and segregation at grain boundaries (GBs) of Nb and Ta-encapsulated Nb (Ta/Nb) thin films for superconducting qubits using atom probe tomography (APT) and transmission electron microscopy (TEM). We observe oxygen segregation at grain boundaries (GBs) relative to the oxygen concentration within the grains for both Nb and Ta-capped Nb thin films and find that a higher oxygen concentration in the interior of Nb grains leads to greater oxygen segregation levels at GBs. This finding reveals that the formation of a local equilibrium of oxygen concentration between GBs and grain interiors of Nb is the primary driving force of the oxygen segregation behaviors in Nb and Ta-capped Nb. The enrichment factors (CGB/Cgrain) for oxygen segregation at GBs in Nb and Ta-capped Nb range from 2.4 ± 0.3 to 2.7 ± 0.4. The current results also highlight that controlling oxygen impurities in Nb during film deposition and fabrication processing is important to concomitantly reducing the level of oxygen segregation at GBs in Nb. Finally, we find that increases in the oxygen concentration in both Nb grains and GBs correlate with a suppression in the critical temperature for superconductivity (Tc). Together, our comparative chemical and charge transport property analyses provide atomic-scale insights into a potential mechanism, contributing to the decoherence in superconducting qubits.

Lee, Jaeyel [Fermilab] (ORCID:0000000185429612)↗
DOE OSTI2026

Impact of Annealing on Superconducting Properties of Tantalum Thin Films

The pursuit for higher-coherence superconducting qubits has led to the adoption of new materials and innovative fabrication techniques. Among the commonly used superconducting materials, tantalum-based or tantalum-capped superconducting qubits have demonstrated the longest lifetimes, outperforming niobium devices even in the presence of their native oxides. Given the losses introduced by the surface oxide, one method to further improve performance is to reduce or eliminate the native oxide on tantalum through UHV annealing. In this work, we examine the effect of dissolved oxygen as a function of annealing temperature on the superconducting properties of tantalum thin films. Dissolved oxygen is quantified using atom probe tomography (APT) and secondary ion mass spectrometry (TOF-SIMS) and correlated with electromagnetic transport measurements performed using a Physical Property Measurement System (PPMS). This study observes that annealing decomposes the native oxide and drives oxygen diffusion into the film matrix. Increasing oxygen content decreases the superconducting transition temperature (Tc) and the residual resistivity ratio (RRR). The critical field decreases with the incorporation of oxygen, while the film’s coherence length decreases relatively by 5%. These results, as well as findings from ongoing studies linking fabrication processes to the structural and chemical properties of the superconducting film and Josephson junction, provide insight into effective strategies for improving the performance of superconducting devices.

Shinde, Maithilee [IIT, Chicago; Fermilab]↗
DOE OSTI2026

TLS characterization using multilevel decay of a fixed-frequency transmon

Transmon qubits are a cornerstone of superconducting quantum computing platforms, yet their coherence times often exhibit temporal fluctuations that degrade processor performance. These variations are commonly attributed to shifts in the resonance frequencies of individual two-level systems (TLSs) near the qubit transition. In this study, we monitor the lifetimes of multiple energy levels of a fixed-frequency transmon and examine their temporal correlations. Our measurements reveal that one or more TLSs—detuned by more than 100 MHz from the qubit transition—can still significantly influence coherence. The proposed method provides a powerful tool for TLS spectroscopy without the need to tune the transmon frequency, either via a flux-tunable inductor or AC-Stark shifts.

Roy, Tanay [Fermilab] (ORCID:000000019442862X)↗
DOE OSTI2026

TLS characterization using multilevel decay of a fixed-frequency transmon

Transmon qubits are a cornerstone of superconducting quantum computing platforms, yet their coherence times often exhibit temporal fluctuations that degrade processor performance. These variations are commonly attributed to shifts in the resonance frequencies of individual two-level systems (TLSs) near the qubit transition. In this study, we monitor the lifetimes of multiple energy levels of a fixed-frequency transmon and examine their temporal correlations. Our measurements reveal that one or more TLSs—detuned by more than 100 MHz from the qubit transition—can still significantly influence coherence. The proposed method provides a powerful tool for TLS spectroscopy without the need to tune the transmon frequency, either via a flux-tunable inductor or AC-Stark shifts.

Roy, Tanay [Fermilab] (ORCID:000000019442862X)↗
DOE OSTI2026

Two-Level System Spectroscopy from Correlated Multilevel Relaxation in Superconducting Qubits

Transmon qubits are a cornerstone of modern superconducting quantum computing platforms. Temporal fluctuations of energy relaxation in these qubits are widely attributed to microscopic two-level systems (TLSs) in device dielectrics and interfaces, yet isolating individual defects typically relies on tuning the qubit or the TLS into resonance. We demonstrate a novel spectroscopy method for fixed-frequency transmons based on multilevel relaxation: repeated preparation of the second excited state and simultaneous $T_1$ extraction of the first and second excited states reveals characteristic correlations in the decay rates of adjacent transitions. From these correlations we identify one or more dominant TLSs and reconstruct their frequency drift over time. Remarkably, we find that TLSs detuned by $\gtrsim 100\,\mathrm{MHz}$ from the qubit transition can still significantly influence relaxation. The proposed method provides a powerful tool for TLS spectroscopy without the need to tune the transmon frequency, either via a flux-tunable inductor or AC-Stark shifts.

Roy, Tanay [Fermilab] (ORCID:000000019442862X)↗
DOE OSTI2026

Effect of metal encapsulation on bulk superconducting properties of niobium thin films used in qubits

Niobium metal occupies nearly 100% of the volume of a typical 2D transmon device. While the aluminum Josephson junction is of utmost importance, maintaining quantum coherence across the entire device means that pair-breaking in Nb leads, capacitive pads, and readout resonators can be a major source of decoherence. The established contributors are surface oxides and hydroxides, as well as absorbed hydrogen and oxygen. Metal encapsulation of freshly grown surfaces with non-oxidizing metals, preferably without breaking the vacuum, is a successful strategy to mitigate these issues. While the positive effects of encapsulation are undeniable, it is important to understand its impact on the macroscopic behavior of niobium films. We present a comprehensive study of the bulk superconducting properties of Nb thin films encapsulated with gold and palladium/gold, and compare them to those of bare Nb films. Magneto-optical imaging, magnetization, resistivity, and London and Campbell penetration depth measurements reveal significant differences in encapsulated samples. Both sputtered, and epitaxial Au-capped films exhibit the highest residual resistivity ratio and superconducting transition temperature, as well as the lowest upper critical field, London penetration depth, and critical current. These results are in good agreement with the microscopic theory of anisotropic normal and superconducting states of Nb. We conclude that pair-breaking in the bulk of niobium films, driven by disorder throughout the film rather than just at the surface, is a significant source of quantum decoherence in transmons. We also conclude that gold capping not only passivates the surface but also affects the properties of the entire film, significantly reducing the scattering rate due to defects likely induced by surface diffusion if the film is not protected immediately after fabrication.

Datta, Amlan [Ames Lab; Iowa State U.]↗
DOE OSTI2025

Impact of Annealing on the Chemical and Superconducting Properties of Ta Thin Films

Tantalum thin films are annealed to dissolve the surface oxide. The effect of annealing is studied using material characterization tools, XPS and TOF-SIMS, and electrical transport measurements of the annealed films are taken using standard PPMS methods to correlate with the surface chemistry. Annealing dissociates the surface oxide, and the oxygen produced diffuses into the thin film. The introduction of oxygen reduces the quality of the thin film, as shown by the suppression of Tc and a reduction in RRR.

Shinde, Maithilee [IIT, Chicago]↗
DOE OSTI2025

Correlating Superconducting Qubit Performance Losses to Sidewall Near-Field Scattering via Terahertz Nanophotonics

Elucidating dielectric losses, structural heterogeneity, and interface imperfections is critical for improving coherence in superconducting qubits. However, most diagnostics rely on destructive electron microscopy or low-throughput millikelvin quantum measurements. Here, we demonstrate noninvasive terahertz (THz) nano-imaging/-spectroscopy of encapsulated niobium transmon qubits, revealing sidewall near-field scattering that correlates with qubit coherence. We further employ a THz hyperspectral line scan to probe dielectric responses and field participation at Al junction interfaces. These findings highlight the promise of THz near-field methods as a high-throughput proxy characterization tool for guiding material selection and optimizing processing protocols to improve qubit and quantum circuit performance.

Kim, Richard H.J. [Ames Lab]↗
DOE OSTI2025

Ultracoherent superconducting cavity-based multiqudit platform with error-resilient control

Superconducting radio-frequency (SRF) cavities offer a promising platform for quantum computing due to their long coherence times, yet integrating nonlinear elements like transmons for control often introduces additional loss. We report a multimode quantum system based on a 2-cell elliptical shaped SRF cavity, comprising two cavity modes weakly coupled to an ancillary transmon circuit, designed to preserve coherence while enabling efficient control of the cavity modes. We mitigate the detrimental effects of the transmon decoherence through careful design optimization that reduces transmon-cavity couplings and participation in the dielectric substrate and lossy interfaces, to achieve single-photon lifetimes of 20.6 ms and 15.6 ms for the two modes, and a pure dephasing time exceeding 40 ms. This marks an order-of-magnitude improvement over prior 3D multimode memories. Leveraging sideband interactions and novel error-resilient protocols, including measurement-based correction and post-selection, we achieve high-fidelity control over quantum states. This enables the preparation of Fock states up to $N = 20$ with fidelities exceeding 95%, the highest reported to date to the authors' knowledge, as well as two-mode entanglement with an estimated coherence-limited fidelities of 99.9% after post-selection. These results establish our platform as a robust foundation for quantum information processing, allowing for future extensions to high-dimensional qudit encodings.

Kim, Taeyoon [Fermilab; Northwestern U.]↗
DOE OSTI2025

Building a Long-Lived 3D Multimode Quantum Processing Unit with TESLA Cavities

Superconducting radio-frequency (SRF) cavities, such as TESLA-shaped cavities, are excellent candidates for long-lived quantum memories. Integrating these cavities with nonlinear elements, such as transmons, enables universal quantum control; however, this integration can often introduce unwanted losses. In this talk, we present the successful integration of a long-lived 2-cell TESLA cavity with an ancillary qubit, forming a quantum processing unit (QPU) that allows for robust control while maintaining coherence. We demonstrate universal control of the QPU through various schemes, including ancilla-cavity sideband and echoed conditional displacement (ECD) methods, enabling fault-tolerant high-fidelity preparation of large Fock states and fast entanglement generation. These results illustrate the versatility and efficiency of our 3D quantum processing unit, paving the way for advanced quantum computing applications.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2025

Chemical Analysis of Tantalum Thin Films compared to Niobium Thin Films using SIMS and XPS

Superconducting qubits are a leading platform for quantum computation. These circuits are typically made from superconducting materials like aluminum or niobium. However, the amorphous niobium oxide and aluminum oxide on the surface of these circuits introduce considerable RF loss due to the presence of two-level systems (TLS), which limits the maximum coherence times T1 to ~100 μs. Capping the niobium qubits with a tantalum layer leads to a 3- 5x improvement [Bal et al., 2024]. But even in this case, tantalum forms an amorphous surface oxide that introduces loss. In an effort to devise strategies to eliminate the presence of this oxide, we present a comprehensive study on the nature of Ta oxide using x-ray photoemission spectroscopy (XPS) and secondary ion mass spectrometry (ToF-SIMS) as a function of heat treatment. The thin films were annealed in ultra-high vacuum conditions and analyzed in situ to characterize the composition and evolution of the native tantalum oxide layer and oxide-metal interface. Our analysis reveals two critical differences between tantalum and niobium oxides: Nb2O5 completely dissolves at 400°C, while Ta2O5 persists even at 800°C. Additionally, tantalum oxide contains only a single suboxide (TaO), in contrast to niobium's two suboxides (NbO and NbO2). The suboxide of tantalum contributes minimally to the total oxide content and shows a relative increase with temperature. Understanding the oxide’s behavior will open new pathways for optimizing coherence times in tantalum qubits.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2025

Impact of surface growth method and surface treatment in niobium-based superconducting devices

We explore the comparison between two growth methods for niobium film - sputtering and electron-cyclotron resonance growth - for niobium-based superconducting resonators. We discuss some of the key properties of the films, including surface characterization and residual resistance measurements metrics. We present our design of various devices used in this study including superconducting resonators and qubits, both in planar configurations and integrated in 3D cavities, as well as experimental characterization of coherence metrics.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2025

Controlled Growth of Ta Oxide With Reactive Sputtering for Overlap Josephson Junction Application

Josephson junctions $\($JJs$\)$ are indispensable elements for superconducting quantum electronics. There is a growing need to develop processes for high quality JJs. Here we explore the growth of Ta oxide as a dielectric barrier for Metal-Oxide-Metal overlap JJ implementations. We study films of Ta oxides prepared with reactive magnetron sputtering. TaOx is grown on silicon and Ta films with varying RF power and oxygen concentrations. Tuning these parameters allows us to control the rate of deposition as well as composition of polycrystalline Ta oxides needed to meet our dielectric requirements for Josephson Junctions.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2025

Comparative Study of Quasi-Particle Burst Events in Transmon Qubits made with Different Materials and Geometries

Superconducting qubits are susceptible to various noise sources, including cosmic rays. ambient gamma and infrared radiation, which can significantly impact their performance. High-energy radiations deposit energy into the qubit substrate, generating high-energy phonons that disrupt Cooper pairs and create quasi-particles (QPs). Infrared photons, on the other hand can directly create QPs. The tunneling of these quasi-particles across Josephson junctions leads to qubit de-excitation and causes relaxation errors. In this study, we utilize a fast feedback mechanism for qubit reset to detect QP burst events with high time resolution [1]. We investigate transmon qubits fabricated with different encapsulations [2], geometries, and substrates at the above-ground laboratory of the Superconducting Quantum Materials and Systems (SQMS) center at Fermilab. Our preliminary results are presented, with discussions on their implications for the performance of modern quantum hardware. [1] Dominicis and Roy et al.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗